Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Uniform and well-dispersed Y2O3:Eu/YVO4:Eu composite microspheres with high photoluminescence prepared by chemical corrosion approach

Facile Synthesis and Luminescence Properties of Highly Uniform MF/YVO4:Ln3+ (ln = Eu, Dy, and Sm) Composite Microspheres

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

Influence of Concentration Effect and Au Coating on Photoluminescence Properties of YVO<sub>4</sub>:Eu<sup>3+</sup>Nanoparticle Colloids

General and Facile Method To Prepare Uniform Y<sub>2</sub>O<sub>3</sub>:Eu Hollow Microspheres

Two-steps Prepared Monodisperse Li-doped Y2O3:Eu3+ Microspheres and Their Luminescence Properties

Controllable Synthesis and Size-Dependent Luminescent Properties of YVO<sub>4</sub>:Eu<sup>3+</sup>Nanospheres and Microspheres

Facile Synthesis and Luminescence Properties of Octahedral Yvo4:Eu3+ Microcrystals

Synthesis and luminescence properties of Y 2O 3:Eu with flower-like microstructure

Microsphere Morphology Tuning and Photo-Luminescence Properties of Monoclinic Y2wo6

Preparation and photoluminescence of yttrium hydroxide and yttrium oxide doped with europium nanowires

Synthesis and Spectra Properties of YVO<SUB>4</SUB>:Eu Nanoparticles: Synthesis and Spectra Properties of YVO<SUB>4</SUB>:Eu Nanoparticles

SYNTHESIS OF Y_2O_3∶Eu NANOCRYSTALLINE BY COMPLEX PRECURSORS

Facile Synthesis and Luminescence of Uniform Y2O3 Hollow Spheres by a Sacrificial Template Route

MgO-Y2O3:Eu composite ceramics with high quantum yield and excellent thermal performance

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Synthesis and Enhanced Luminescence of Uniform and Well-Dispersed Quasispherical Yvo4:Ln(3+) (ln = Eu, Dy) Nanoparticles by A Solvothermal Method

Polymer-assisted chemical solution approach to YVO4:Eu nanoparticle networks

Optimization of photoluminescence of Eu3+ doped YVO4 nanoparticles by green microwave synthesis

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Synthesis and characterization of highly uniform Lu2O 3:Ln3+ (Ln = Eu, Er, Yb) luminescent hollow microspheres