Abstract:Titania-based nanocomposites have recently attracted much attention due to their unique structure and properties. Titania has been known to have three crystal phases: brookite, anatase and rutile. The anatase titania has the highest photoactivity than the other two phases. Meanwhile Ohtani et al. [1] reported that amorphous titania has a negligible photoactivity compared to the crystalline titania. Much work has been conducted on the optimization of catalytic properties of titania used in the photodegradation of organic pollutants in water by either using modified titania or thin titania films. Many researches indicated that dopants, such as many oxides, can effectively suppress the transformation of anatase into rutile by improving the onset transformation temperature [2]. Silica-titania mixed oxide is considered a potential candidate because it is used as not only a good photocatalyst itself but also a support material for other chemical reaction catalysts [3, 4]. 30SiO2/TiO2 powders (30 denotes the weight percent of silica) were prepared by sol-gel process. Ti(OBu n )4 and TEOS were used as precursors of titania and silica respectively. After TEOS was stirred in a mixture solution of pure ethanol, distilled water and hydrochloric acid for 1 h, Ti(OBu n )4 was added slowly into the mixture. The sol of SiO2/TiO2 was obtained after another two hours’ vigorous stirring and cooled to room temperature. The gel was calcined at different temperatures and then ground into fine powders. The distilled water solution of methyl orange (with a concentration of 25 mg/L) was chosen for photodegradation. 0.2 g powders were added into 40 ml of the above solution with vigorous agitation under the mercury light. A 756MC UV-VIS spectrometer was used to record the change of concentration of the methyl orange. FT-IR spectra was obtained by a Bruker EQUINOX55 spectrometer. TEM and HREM observations were carried out using a Jeol-2010 electron microscope. The XRD patterns were made in a D/max3A diffractometer with Cu Kα radiation. The crystallite size of powders was determined by Scherrer equation. Electron spin resonance measurements were made with a Bruker paramagnetic spectrometer. X-ray photoelectron spectroscopy (XPS) spectra of the sample were obtained with an NP-1 using the Mg Kα excitation source and the binding energies referenced to the C1s hydrocarbon line at 284.6 eV. The atomic ratios were obtained by intergrating the areas under the peak. Photodegradation for methyl orange with 30SiO2/ TiO2 samples calcinated at different temperature under UV irradiation is illustrated in Fig. 1. The results of other samples heated at temperatures higher than 850 ◦ C were not shown in this figure because further increase of the calcination temperature decreased the decomposition rate. It can be seen that decomposition rate of the samples fired at 400 ◦ C and 500 ◦ Ci s low. When the calcination temperature was further increased to 600 ◦ C, the higher photoactivity than Degussa P25’s was obtained. The sample heated at 800 ◦ C has the best photoactivity about 2 times higher than the Degussa P25.

High Efficient Photocatalyst of Spherical TiO2 Particles Synthesized by a Sol–gel Method Modified with Glycol

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Large-surface Mesoporous TiO2 Nanoparticles: Synthesis, Growth and Photocatalytic Performance.

Preparation and Characterization of Nanosized Anatase TiO2 Cuboids for Photocatalysis

Synthesis, Characterization and Photocatalytic Activity of Hierarchical Spherical TiO2 Nanostructures

Synthesis and Photocatalytic Property of TiO<sub>2</sub> Particles Preparated in the Solvothermal Method

Porous TiO2 Hollow Nanospheres: Synthesis, Characterization and Enhanced Photocatalytic Properties

Synthesis of Titanium Dioxide and the Study of Photocatalytic Activity

Enhanced photoactivity of silica-titania binary oxides prepared by sol-gel method

Mesoporous SiO2-Modified Nanocrystalline TiO2 with High Anatase Thermal Stability and Large Surface Area As Efficient Photocatalyst

Preparation of Photocatalytic Activity Nanosized TiO2 by Hydrolysis-Sol Method

Study on relationship of particle structure and photocatalytic properties of nano-TiO2 powder

The synthesis of hydrophobic nano-TiO2 powder and its photocatalytic property

Highly efficient visible light TiO2 photocatalyst prepared by sol-gel method at temperatures lower than 300°C.

Spray-hydrolytic Synthesis of Highly Photoactive Mesoporous Anatase Nanospheres for the Photocatalytic Degradation of Toluene in Air

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles

Photocatalyst of TiO2 Ultrafine Powders Prepared by Thermohydrolysis of TiOSO4 Solution

Fast Synthesis of Monodisperse TiO2 Submicrospheres Via a Modified Sol-Gel Approach

Preparation of Tm2Ti2O7 by Sol-Gel Method and Its Photocatalytic Activity

Sol-Gel Preparation and Characterization of High Activity Titanium Dioxide Nanocrystalline Photocatalyst

Preparation of Controllable Crystalline Titania and Study on the Photocatalytic Properties.