Abstract:A new Mg-5Bi-1Mn-0.5Zn-0.2Ag (BMZQ5100, wt%) alloy is developed and analyzed comparatively its extrudability, microstructure, mechanical property and thermal stability with a commercial AZ91 alloy. The results show that the BMZQ5100 alloy can be successfully extruded at a high extrusion speed (ES) of 30 m/min without surface cracks, but there are a large number of hot cracks occurred on the low-speed-extruded AZ91 alloy surface (ES: 5 m/min). For the 30 m/min extruded BMZQ5100 alloy (BMZQ5100-E30), it exhibits a completely dynamic recrystallized (DRX) grain structure with a slightly larger grain size and stronger basal fiber texture than the 2 m/min extruded AZ91 alloy (AZ91-E2) without surface cracks. In terms of second phase, the former alloy contains submicron Mg3Bi2 phases at grain boundaries (GBs), nano-scale Mg3Bi2 and α-Mn particles within grain interiors, along with the co-segregation of Zn and Ag at GBs. The latter alloy has a continuous network of submicron Mg17Al12 phases along GBs, but no any solute segregation is observed at GBs. The BMZQ5100-E30 alloy exhibits more excellent mechanical properties with a tensile yield strength of ∼ 271 MPa, an ultimate tensile strength of ∼ 319 MPa and an acceptable elongation-to-failure of ∼ 8%, compared with the AZ91-E2 alloy. The GB strengthening, precipitation strengthening and solute segregation strengthening on the TYS occupy ∼ 46.2, ∼ 45.5 and ∼ 8.3%, respectively. In addition, the BMZQ5100-E30 alloy has higher microstructural thermal stability than the AZ91-E2 alloy, because of second phase pinning and solute segregation at GBs to effectively inhibit the grain growth during annealing.

BULK Al90Mn8Ce2 ALLOY WITH ULTRA HIGH STRENGTH

Bulk Al90mn9ce1 Alloy with Ultra-High Strength Prepared by Spark Plasma Sintering

Achieving Enhanced Strength Retention at Elevated Temperatures in Ultrafine-Fibrous Interconnected Al-Ce-Ni Eutectic Alloy Solidified under Super-Gravity Field

Refining Mechanism and Elevated-Temperature Mechanical Properties of Al-Ce Alloys Solidified under Super Gravity Field

Bulk nanostructured Al-Si alloy with remarkable improvement in strength and ductility

Ultra-high strength Al-Zn-Mg-Cu alloys with high zinc content prepared via powder hot extrusion

Achieving exceptional ultrahigh-strength in low-alloy Mg-1Al-1Ca-0.4Mn (wt%) alloy by regulating bimodal microstructure

Investigation of Microstructures and Mechanical Properties of Ultra-High Strength Al-Zn-Mg-Cu Alloy Prepared by Rapid Solidification and Hot Extrusion

Approaching 1 GPa ultra‐high tensile strength in a nanostructured Al‐Zn‐Mg‐Cu‐Zr‐Sc alloy prepared by severe plastic deformation

Fabrications and mechanical properties of bulk amorphous, nanocrystalline, nanoquasicrystalline alloys in aluminum-based system

The cobalt-free Fe35Mn15Cr15Ni25Al10 high-entropy alloy with multiscale particles for excellent strength-ductility synergy

High strength and ductility in a dual-phase hetero-structured AlCoCrFeNi2.1 eutectic high-entropy alloy by powder metallurgy

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

An Mg‐Al‐Zn Alloy with Verry High Specific Strength and Superior High‐strain‐rate Superplasticity Processed by Reciprocating Extrusion

Developing a high-speed-extruded BMZQ5100 alloy with higher strength and microstructural thermal stability than AZ91 alloy

A Bulk Metal/ceramic Composite Material with a Cellular Structure

Achieving ultrahigh specific strength of an ultrafine grained Mg-9Li-1Al alloy via the combined processing of ECAP with repeated annealing and rolling

High Strength Extruded Mg–5Zn–2Nd–1.5Y–0.6Zr–0.4Ca Alloy Produced by Electromagnetic Casting

A Zr-45Ti-54Al-3V alloy with excellent elevated temperature mechanical properties: Millimeter-scale coarse grains with initial subgrains

Enhanced load transfer and ductility in Al–9Ce alloy through heterogeneous lamellar microstructure design by cold rolling and annealing

Achieving ultrahigh strength in binary Al-10Mg alloy through heavy cryogenic rolling