Abstract:Directional solidification of A1-4.5Cu alloy refined by adding Al-5Ti-1B has been carried out to investigate the texture formation and grain boundary characteristic of the paramagnetic crystal under a high magnetic field. OM and EBSD were applied to analyze the microstructures solidified at different temperature gradients (G) and magnetic field intensities (B). The results show that at the temperature gradient of 27 K/cm; the orientations of fcc alpha-Al grains without magnetic field are random. However, as a high magnetic field is imposed, the easy magnetization axes < 310 > of the alpha-Al grains are aligned parallel to the direction of the magnetic field leading to < 310 > texture. Meanwhile, the ratio of coincidence site lattice (CSL) grain boundaries increases with the increment of magnetic field intensity and reaches its maximum value at 4 T, but decreases as the magnetic field enhances further. On the other hand, when the temperature gradient is elevated, columnar dendrite morphology is exhibited without magnetic field; while a 6 T high magnetic field is introduced, the columnar dendrites are broken and equiaxed grains of random orientations are obtained. The alignment behavior of the free crystals in melt could be attributed to the magnetic crystalline anisotropy of alpha-Al. Moreover, the influence of fluid flow on the texture formation and CSL grain boundary development under magnetic field is discussed. The absence of convection is benefit for grain reorientation and CSL boundary formation. The application of high static magnetic field will inhibit the macro-scale convection. However, the interaction between thermoelectric current and magnetic field will cause micro-scale fluid flow, i.e., thermoelectric magnetic convection (TEMC). The TEMC will give rise to perturbation near the solid-liquid interface leading to the appearance of freckles as well as the decreasing of the ratio of CSL boundary. Moreover, it is proposed that the formation of CSL boundary is associated with the rotation of the free grains in melt along specific crystallographic axes by magnetic torque.

Solidification Structure of 6063 Alloy under Pulsed Magnetic Field

Numerical Study on Solidification Characteristics under Pulsed Magnetic Field

Numerical and experimental studies on solidification of AZ80 magnesium alloy under out-of-phase pulsed magnetic field

Revealing the Mechanisms for the Nucleation and Formation of Equiaxed Grains in Commercial Purity Aluminum by Fluid-Solid Coupling Induced by a Pulsed Magnetic Field

Influence of a high pulsed magnetic field on the tensile properties and phase transition of 7055 aluminum alloy

Evolutions of Electromagnetic Fields and Forced Flow Driven by the Pulse Length of a Pulsed Magnetic Field and Their Relevance to the Grain Refinement of a Solidified Al–Si Hypoeutectic Alloy

Numerical Simulation of Electromagnetic Phenomena and Solidification under a Pulsed Magnetic Field

Pulse Magnetic Field Refinement of Solidification Structure of Metals

Direct chill casting of magnesium alloy under pulsed magnetic field

Effect of Pulsed Magnetic Field on Microstructure and Mechanical Properties of 7050 Al Alloy After Two-Stage Aging

Effect of Electromagnetic Stirring on Fine Grain Formation and Tensile Property Improvement for Fe-Ni Superalloy

Magnetic induced re-dissolution and microstructure modifications on mechanical properties of Cr4Mo4V steel subjected to pulsed magnetic treatment

Numerical study of flow and heat transfer behaviors during direct-chill casting of large-size magnesium alloy billet under pulsed magnetic field

Faceted Growth Of Primary Al2cu Crystals During Directional Solidification In High Magnetic Field

Microstructure evolution, diffusion behavior, and mechanical properties of a Cu/AlCoCrFeNi 2.1 composite under pulsed magnetic field

Comparative Study on the Grain Refinement of Al-Si Alloy Solidified under the Impact of Pulsed Electric Current and Travelling Magnetic Field

Experimental study on solidification structure of Al ingot by pulse magneto oscillation

Texture Formation and Grain Boundary Characteristic of A1-4.5cu Alloys Directionally Solidified under High Magnetic Field

Microstructure development in eutectic Al–Fe alloy during directional solidification under high magnetic fields at different growth velocities

Effects of an oscillation electromagnetic field on grain refinement and Al8Mn5 phase formation during direct-chill casting of AZ31B magnesium alloy

Magnetic field treatment effects on microstructure and properties of A356 aluminium alloy