Abstract:GeTe and Ge0.99-xIn0.01SnxTe0.94Se0.06 (x = 0, 0.01, 0.03, and 0.06) samples were prepared by vacuum synthesis combined with spark plasma sintering (SPS). The thermoelectric properties of GeTe were coordinated by multiple doping of Sn, In, and Se. In this work, a maximum zT(zT = S2σT/κ) of 0.9 and a power factor (PF = S2σ) of 3.87 μWmm-1 K-2 were obtained in a sample of Ge0.99In0.01Te0.94Se0.06 at 723K. The XRD results at room temperature show that all samples are rhombohedral phase structures. There is a peak (~27°) of the Ge element in GeTe and the sample (x = 0), but it disappears after Sn doping, indicating that Sn doping can promote the dissolution of Ge. The scattering mechanism of the doped samples was calculated by the conductivity ratio method. The results show that phonon scattering Is dominant in all samples, and alloy scattering is enhanced with the increase in the Sn doping amount. In doping can introduce resonance energy levels and increase the Seebeck coefficient, and Se doping can introduce point defects to suppress phonon transmission and reduce lattice thermal conductivity. Therefore, the thermoelectric properties of samples with x = 0 improved. Although Sn doping will promote the dissolution of Ge precipitation, the phase transition of the samples near 580 K deteriorates the thermoelectric properties. The thermoelectric properties of Sn-doped samples improved only at room temperature to ~580 K compared with pure GeTe. The synergistic effect of multi-element doping is a comprehensive reflection of the interaction between elements rather than the sum of all the effects of single-element doping.

Selenium doping in potential topological superconductor Sn 0.8 In 0.2 Te

Selenium Doping NaCl-type Superconductor: SnAs1−xSex (X=0–0.13)

Effect of Te Doping on Superconductivity and Charge-Density Wave in Dichalcogenides 2H-Nbse2-xtex (X=0, 0.1, 0.2)

Nematic Transition and Nanoscale Suppression of Superconductivity in Fe(Te,Se)

Influence of Sn Doping on the Phase Formation and Superconductivity of Fese0.93

Study on the Effect of Sn, In, and Se Co-Doping on the Thermoelectric Properties of GeTe

Effect Of Selenium Doping On The Superconductivity Of Nb2pd(S1-Xsex)(5)

Superconductivity in A Misfit Phase That Combines the Topological Crystalline Insulator Pb1-Xsnxse with the Cdw-Bearing Transition Metal Dichalcogenide Tise2

Structural and Superconducting Properties in the Te-doped Spinel CuRh2Se4

Effect of Te Doping on the Structure and Superconductivity of K X Fe 2− Y Se 2− Z Te Z Single Crystals

Enhanced Superconductivity in FeTe0.8S0.2 Via Sn Doping

Significant enhancement in Jc and suppression of Jc anisotropy for Sn-doped FeSe0.4Te0.6 single crystals

Different Response Of Superconductivity To The Transition-Metal Impurities In K(0.8)2yxm(X)Se(2) (M = Cr, Mn, Co, Zn)

Fully Gapped Superconductivity In In-Doped Topological Crystalline Insulator Pb0.5sn0.5te

Magnetism and Superconductivity in MxFe1+yTe1–zSez (M = Cr, Mn, Co, Ni, Cu, and Zn) Single Crystals

Superconductivity induced by In substitution into the topological crystalline insulator Pb(0.5)Sn(0.5)Te

High Thermoelectric Performance of SnTe Via in Doping and Cu1.75Se Nanostructuring Approach

Enhancement of the superconducting transition temperature due to multiband effect in the topological nodal-line semimetal Pb$_{1-x}$Sn$_{x}$TaSe$_{2}$

Superconductivity and non-metallicity induced by doping the topological insulators Bi2Se3 and Bi2Te3

Effect of Sn Doping in (bi0.25sb0.75)2−x Sn X Te3 (0 ≤ X ≤ 0.1) on Thermoelectric Performance

Effects On Superconductivity Of Transition-Metal Doping In Fese0.5te0.5