Li2OLiFZnF2B2O3P2O5: MnO glasses – Thermal, structural, optical and luminescence characteristics

c parthasaradhi reddy,v naresh,k t ramakrishna reddy
IF: 3.754
2016-01-01
Optical Materials
Abstract:Abstract Here, we present results pertaining to thermal, structural, optical and photoluminescence properties of Li 2 O LiF ZnF 2 B 2 O 3 P 2 O 5 : (0.1–1.5 mol.%) MnO glasses. DTA profiles revealed a change in glass transition temperature with the addition of MnO suggesting an increase in glass stability. The modifications in structural units are interpreted from FTIR and Raman spectral profiles, which confirm the formation of stable P O B bonds. The host Li 2 O LiF ZnF 2 B 2 O 3 P 2 O 5 (labelled as LZBP) glass exhibits emission in the blue region on excitation with 361 nm. The red shift in optical absorption edge and decrease in energy of band gap as a function of MnO concentration is analysed from Tauc’s plot. The nature of local symmetry around manganese ions in LZBP matrix has been understood by evaluating the crystal field strength (Dq) and Racah inter-electronic repulsion parameters ( B u0026 C ) from absorption spectrum and electron-lattice interaction energy ( Sħω ) factor from emission spectrum. The emission spectra of (0.1–1.5 mol.%) Mn 2+ : LZPB glasses have shown broad band at 613 nm assigned to electronic transition 4 T 1g (G) →  6 A 1g (S) displaying orange-red emission upon excitation at 413 nm. Octahedral coordination of Mn 2+ ions has been estimated from the position of emission in luminescence spectra. The effect of Mn 2+ concentration on emission properties has been discussed from lifetime curves and energy level scheme.
What problem does this paper attempt to address?