Pt and Mo Co-Decorated MnO 2 Nanorods with Superior Resistance to H 2 O, Sintering, and HCl for Catalytic Oxidation of Chlorobenzene
Gong Chen,Yuanpu Cai,Hao Zhang,Dongsen Hong,Shijie Shao,Chensheng Tu,Yuexiang Chen,Feng Wang,Biao Chen,Yuting Bai,Xingyi Wang,Qiguang Dai
DOI: https://doi.org/10.1021/acs.est.1c05086
2021-10-08
Abstract:MnO2 nanorods with exposed (110), (100), or (310) facets were prepared and investigated for catalytic oxidation of chlorobenzene, then the (110)-exposed MnO2 nanorod was screened as the candidate parent and further modified by Pt and/or Mo with different contents. The loading of Pt enhanced activity and versatility of the pristine MnO2, but the polychlorinated byproducts and Cl2 were promoted, conversely, as the decoration of Mo inhibited the polychlorinated byproducts and improved durability. Determination of structure and properties suggested that Pt facilitated the formation of more oxygen vacancies/Mn3+ and surface adsorbed oxygen weakened the bonds of surface lattice oxygen, while Mo stabilized surface lattice oxygen and increased acid sites, especially Brønsted acid sites. Expectedly, Pt and Mo bifunctionally modified MnO2 presented a preferable activity, selectivity, and durability along with the super resistance to H2O, high-temperature, and HCl, and no prominent deactivation was observed within 30 h at 300 °C under dry and humid conditions, even at high-temperature aging at 600 °C and HCl-pretreatment (7 h). In this work, the optimized Mo and Pt codecorated MnO2 was considered a promising catalyst toward practical applications for catalytic oxidation of actual Cl-VOCs emissions.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.est.1c05086.The catalyst characterization information is provided together with the catalytic activity data, HRTEM, XRD, Raman, XPS, TG/DTG, UV–vis DRS, and DRIFTS spectra (PDF)This article has not yet been cited by other publications.
environmental sciences,engineering, environmental