Abstract:On the road of lead-free piezoelectric ceramics into practical applications, the study of Ni-internal-electrode (K, Na)NbO3-based (KNN-based) multilayer actuators (MLAs) is an important part, possessing the advantages of environmentally friendly and low cost. The Ni-internal-electrode KNN-based MLAs with different layer numbers and layer thicknesses were fabricated via the tape casting method and sintered in the reducing atmosphere. The piezoelectric layers consist of the main KNN-based phase and a trace amount of second phase Mn4Nb2O9. The element diffusion between the Ni electrodes and KNN-based grains is tiny, indicating that Ni is suitable for co-firing with KNN-based ceramics. After sintering, the compressive stress perpendicular to the thickness direction and the "relative tensile stress" parallel to the thickness direction are retained in the MLAs, bringing influences on the piezoelectric and dielectric properties of KNN-based materials. Compared with the bulk ceramics, the prepared MLAs significantly reduce the driving voltages and increase the displacement outputs, which are more applicable to the scenarios of miniaturization and portability. Particularly, the 46-layer actuator shows high displacements of 1580 and 2737 nm under the voltages of 100 and 200 V, respectively. However, the inverse piezoelectric coefficient d(33)* for each layer of MLAs is still lower than that of the bulk ceramics, indicating that the piezoelectric properties of the KNN-based materials are suppressed. To give full play to the piezoelectric properties of KNN-based materials, more attentions should be paid to the design of reasonable electrode structure and the development of internal electrode paste for MLAs.

Investigation on Co‐fired Multilayer KNN‐based Lead‐free Piezoceramics

Preparation of KNN Based Lead-Free Piezoelectric Ceramics Via Composition Designing and Two-Step Sintering

New K0.48Na0.52NbO3–Bi(Zn0.5Zr0.5)O3 Lead-Free Ceramics: Microstructure and Piezoelectricity

Fabrication and Electrical Properties of Fine-Scale 1–3 Piezoceramic/Epoxy Composites Using (K,na)nbo3-Based Lead-Free Ceramics

High Piezoelectric Properties and High TC in KNN-Based Lead-Free Ceramics Sintered in Reducing Atmosphere

Adaptive ferroelectric states in KNN-based piezoceramics: Unveiling the mechanism of enhancing piezoelectric properties through multiple phase boundary engineering

Recent Developments in (K, Na)NbO3-Based Lead-Free Piezoceramics

Simultaneous Enhancement of Piezoelectricity and Temperature Stability in KNN‐Based Lead‐Free Ceramics Via Layered Distribution of Dopants

Nanodomains in KNN‐Based Lead‐Free Piezoelectric Ceramics: Origin of Strong Piezoelectric Properties

(K, Na)NbO 3 -based lead-free piezoceramics: Phase transition, sintering and property enhancement

Effects of the Addition of Li0.8Ni0.2Nb0.96O3 on the Structure and Electrical Properties of K0.48Na0.52NbO3 Lead-Free Piezoceramics

Excellent piezoelectric performance of KNNS-based lead-free piezoelectric ceramics through powder pretreatment by hydrothermal method

(K,na)nbo3‐based Lead‐Free Piezoceramics: Fundamental Aspects, Processing Technologies, and Remaining Challenges

Enhancement of piezoelectric properties and temperature stability by forming an MPB in KNN-based lead-free ceramics

BNH doping enhances the piezoelectric properties and temperature stability of KNN-based lead-free piezoelectric ceramics

Piezoelectricity of lead-free (K, Na)NbO3 nanoscale single crystals

Textured Potassium Sodium Niobate Lead-Free Ceramics with High d33 and Qm for Meeting High-Power Applications

Technology Transfer of Lead-Free (K, Na)NbO3-based Piezoelectric Ceramics

Sintering properties of K_(0.5)Na_(0.5)NbO_3 lead-free piezoelectric ceramics

KNN‐based Piezoelectric Ceramic Multilayer Actuators with Ni Internal Electrodes

High mechanical quality factor and piezoelectricity in potassium sodium niobate ceramics