Abstract:The (1 − x)(Li 0.03 Na 0.5 K 0.47 )(Nb 0.92 Sb 0.05 Ta 0.03 )O 3 –xBa 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 (LNKNST–BCZT, x = 0, 0.5, 1.5, 2.5, and 3.5%) lead-free piezoceramics were synthesized by the conventional solid-state reaction method with adding nano-sized Ba 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 (BCZT) powder to investigate their influences on crystal structure and electrical properties. The X-ray diffraction (XRD) analysis reveals that all the sintered LNKNST–BCZT ceramics exhibit pure perovskite structure with the mainly rhombohedral (R) phase or the coexistence of rhombohedral (R) phase and tetragonal (T) phase. The composition of the LNKNST–1.5%BCZT ceramics locates around the critical point, i.e., the ceramics changing from the coexistence of rhombohedral (R) phase and tetragonal (T) phase to purely rhombohedral (R) phase, and presents the most densified microstructure morphology, which can be confirmed further by the field emission scanning electron microscope (FESEM) observation. There are two dielectric anomalies in the temperature dependent dielectric properties curves of the LNKNST–BCZT ceramics, which correlate with the ferroelectric rhombohedral (R) phase changing to the ferroelectric tetragonal (T) phase, and then to the paraelectric cubic (C) phase. Both the Curie–Weiss law and the power law fittings confirm the diffuse phase transition ferroelectrics characteristic of the LNKNST–1.5%BCZT ceramics, which is considered as correlating with the polar nanoregions (PNRs). Due to the densification effect caused by the chosen amount of nano-sized BCZT doping and the construction of R–T polymorphic phase boundary, the LNKNST–1.5%BCZT ceramics exhibit the best ferroelectric and piezoelectric properties. The complex impedance spectroscopy analysis confirms that the extrinsic electrical conduction mechanism at high temperatures is dominated by the oxygen vacancies induced by the evaporation of the alkali metals during sintering.

Recent Developments in (K, Na)NbO3-Based Lead-Free Piezoceramics

Effects of Na Excess on the Preparation and Characterization of (K0.5na0.5)nbo3ceramics

New K0.48Na0.52NbO3–Bi(Zn0.5Zr0.5)O3 Lead-Free Ceramics: Microstructure and Piezoelectricity

(K, Na)NbO 3 -based lead-free piezoceramics: Phase transition, sintering and property enhancement

(K,na)nbo3‐based Lead‐Free Piezoceramics: Fundamental Aspects, Processing Technologies, and Remaining Challenges

(K, Na)NbO3-based Lead-free Piezoceramics: Status, Prospects and Challenges

Effects of nano-sized BCZT on structure and electrical properties of KNN-based lead-free piezoceramics

Preparation of KNN Based Lead-Free Piezoelectric Ceramics Via Composition Designing and Two-Step Sintering

The structural origin of enhanced piezoelectric performance and stability in lead free ceramics

High Piezoelectric Properties and High TC in KNN-Based Lead-Free Ceramics Sintered in Reducing Atmosphere

Crystallographic Texture and Phase Structure Induced Excellent Piezoelectric Performance in KNN‐based Ceramics

(K0.44,Na0.52,Li0.04)(Nb0.84,Ta0.10,Sb0.06)O3 ferroelectric ceramics

BNH doping enhances the piezoelectric properties and temperature stability of KNN-based lead-free piezoelectric ceramics

Potassium sodium niobate (KNN) lead-free piezoceramics: A review of phase boundary engineering based on KNN materials

Enhanced Piezoelectric Properties and Temperature Stability in KNN-based Textured Ceramics

Piezoelectricity of lead-free (K, Na)NbO3 nanoscale single crystals

Role of ZnO dopant in enhancing piezoelectric characteristics in KNN‐based piezoelectric ceramics

Influence of calcination and sintering temperature on the microstructure, dielectric, ferroelectric and piezoelectric properties of the lead-free KNN ceramics

Phase Structure and Polar Characteristics of Alkali Niobate Ceramics Modified by Ba0.6ca0.4zro3

Adaptive ferroelectric states in KNN-based piezoceramics: Unveiling the mechanism of enhancing piezoelectric properties through multiple phase boundary engineering

Sodium–potassium–niobate based piezoelectric ceramics: processing—microstructure—properties