Abstract:Corrosion behavior of ferritic (Fe–14Cr–2W+Y2O3) and ferritic–martensitic (Fe–9Cr–2W+Y2O3) oxide dispersion strengthened (ODS) steels in the static isothermal liquid Pb was investigated at 550 and 650°C depending on the oxygen concentration CO in the melt for duration up to 1000h. It was determined that the interaction mode of steels changes from the dissolution in the pure Pb (CO⩽10−14wt%O) to the formation of protective oxide layers on the surface of steels in the oxygen-added Pb (CO∼10−6wt%O) and to formation of multiphase non-protective scales in the Pb saturated by oxygen (CO∼10−3wt%O). In general, the observed corrosion behavior of ODS steels coincides with that of traditional chromium steels. However, specific structure of ODS steels causes some variations in corrosion process. In the pure Pb (CO⩽10−14wt%O) the fine-grained structure promotes inter-granular corrosion attack and penetration of lead into steel matrix along grain boundaries. Increase in Cr content in the steel promotes corrosion attack. In the oxygen-added Pb (CO∼10−6wt%O) the fine-grained structure, vice versa, ensures formation of oxide layers with higher Cr content due to fast diffusion of Cr into growing oxide along grain boundaries. The protective properties of oxide layers are improved with temperature rise (550→650°C) and chromium content in steel. In the oxygen-saturated Pb (CO∼10−3wt%O) the ODS steels undergo severe oxidation accompanied by the formation of non-protective multiphase scale which consist of mixture of different oxide phases: plumboferrite, magnetite, Fe–Cr spinel and free Pb. The oxidation kinetics intensifies drastically with temperature and decelerates with increasing chromium content in the steel. Based on the experimental data the scheme of interaction of components in the "steel - liquid Pb” system depending on temperature and oxygen content is proposed.

The Corrosion Behavior Of Pure Iron Under Solid Na2so4 Deposit In Wet Oxygen Flow At 500 Degrees C

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Corrosion Mechanism of Pure Cr under Solid NaCl Deposit in Oxygen Flow with Water Vapor at 600℃

Corrosion Behavior of 20G Steel in Saline (na2so4) Circumstances at High Temperature/Pressure

Corrosion Behavior of Pure Ti under a Solid NaCl Deposit in a Wet Oxygen Flow at 600 °C

Electrochemical Impedance Spectroscopy (EIS) Studies of the Corrosion of Pure Fe and Cr at 600°C under Solid NaCl Deposit in Water Vapor

The Mechanism of Electrochemical Testing Method under Synergistic Effect of NaCl and Water Vapor at 600℃

Corrosion behavior of metals or alloys with a solid NaCl deposit in wet oxygen at medium temperature

Impact of SO2 Concentration on the Corrosion Rate of X70 Steel and Iron in Water-Saturated Supercritical CO2 Mixed with SO2

Corrosion Behavior of Fe–14Cr–2W and Fe–9Cr–2W ODS Steels in Stagnant Liquid Pb with Different Oxygen Concentration at 550 and 650°C

Effect of SO2 on the Corrosion Behaviors of CoCrFeNiTi0.5 Alloy Anti-Alkali Metal Sulfate

Atmospheric Corrosion of Steel A3 Deposited with Ammonium Sulfate and in the Presence of Sulfur Dioxide

Effects of Exposure Temperature and Time on Corrosion Behavior of a Ferritic–martensitic Steel P92 in Aerated Supercritical Water

Assessment of Corrosion Protection Performance of FeOOH/Fe3O4/C Composite Coatings Formed in Situ on the Surface of Fe Metal in Air-Saturated 3.5 Wt.% NaCl Solution.

Effect of SO 4 2− in aerobic/anaerobic environment and its interaction with HCO 3 − on corrosion behavior of carbon steel

Synergistic Effect of Different NaCl Concentrations on the Initial Corrosion of Q235 Steel under a Simulated SO2 Environment

Evidence for the occurrence of electrochemical reactions and their interaction with chemical reactions during the corrosion of pure Fe with solid NaCl deposit in water vapor at 600°C

The Electrochemical Corrosion Mechanisms of Pure Cr with NaCl Deposit in Water Vapor at 600 degrees C

Effect of SO42− in aerobic/anaerobic environment and its interaction with HCO3− on corrosion behavior of carbon steel

Iron oxide fluxing and precipitation in sulphate deposits during heat-resistant alloy corrosion in simulated combustion gas

Corrosion Behavior of Oxide Dispersion Strengthened Ferritic Steels in Supercritical Water