Corrosion Behavior of Pure Ti under a Solid NaCl Deposit in a Wet Oxygen Flow at 600 °C

Lei Fan,Li Liu,Min Cao,Zhongfen Yu,Ying Li,Minghui Chen,Fuhui Wang

DOI: https://doi.org/10.3390/met6040072

IF: 2.695

2016-01-01

Metals

Abstract:The corrosion behavior of pure Ti under a solid NaCl deposit in a wet O2 flow at 600 °C has been studied. The results showed that the corrosion rate was greatly accelerated by solid NaCl, which destroyed the compact and protective TiO2 scale to yield non-protective N4Ti5O12 and other products. Detailed scanning electron microscopy (SEM) equipped with an energy dispersive spectrometer (EDX), and X-ray diffraction (XRD) analysis showed that, during the corrosion process, the metal (Ti) diffused outward rapidly and reacted with the wet O2 to form a thick and porous corrosion products scale. The electrochemical reaction was also observed during the whole corrosion process at 600 °C, which further accelerated the corrosion rate. A possible mechanism has been proposed for pure Ti covered with a solid NaCl deposit in wet O2 at 600 °C, based on the experimental results.