MnO2–TiO2/C Nanocomposite Arrays for High-Performance Supercapacitor Electrodes

Biao Gao,Xingxing Li,Yiwei Ma,Yue Cao,Ziying Hu,Xuming Zhang,Jijiang Fu,Kaifu Huo,Paul K. Chu

DOI: https://doi.org/10.1016/j.tsf.2014.09.071

IF: 2.1

2015-01-01

Thin Solid Films

Abstract:Coaxial TiO2 and carbon nanotube arrays (TiO2/C NTAs) are prepared by hydrothermal treatment of anatase TiO2 nanotube arrays (TiO2 NTAs) in a glucose solution and carbonized under N2 at 700°C. The TiO2/C NTAs provide an extremely large, solvated, ion accessible surface area as well as a direct pathway for charge transport, thus yielding substantially improved areal capacitance of 26.1mF/cm2 at a current density of 0.1mA/cm2 that is 60 times larger than the capacitance of anatase TiO2 NTAs under the same conditions. The TiO2/C NTAs provide a good support for depositing highly pseudocapacitive materials such as MnO2 to form coaxial MnO2, C and TiO2 nanotube arrays (MnO2–TiO2/C NTAs), producing better capacitive properties. The MnO2–TiO2/C electrode shows a high specific capacitance (580F/g at a current density of 2.6A/g), an excellent rate capability and a good cycling stability.