Abstract:In this work, Cu-1.4 wt%Ta-Zr alloys with different Zr content (0, 0.1, 0.2 and 0.5 wt%) were fabricated by mechanical alloying combined with spark plasm sintering. The effect of Zr addition on the microstructures, mechanical properties and thermal stability of Cu-Ta alloy were characterized. Cu-Ta alloys composes of ultrafine equiaxed grains along with the uniformly dispersion of semi-coherent Ta nanoclusters and incoherent Ta coarse particles. As Zr is introduced into Cu-Ta alloy, the Ta precipitates were effectively refined, especially for the reduction of Ta coarse particles. The significant refinement effect of the grains is realized when Zr content reaches 0.2 wt%, and high-proportioned nano-sized grains are facilitated to form, along with the activation of a lot of twins and the formation of intermetallic composed of Cu and Zr. The dislocation density and strength increase remarkably with the increase of Zr content, and the highest strength (499 MPa for yield strength and 600 MPa for ultimate tensile strength) is achieved as the Zr content is up to 0.2 wt%. Compared with Cu-Ta alloy (382 MPa for yield strength and 560 MPa for ultimate tensile strength), the significant increment of 31% for the yield strength is successfully realized by Cu-Ta-0.2 wt%Zr alloy. Cu-Ta-0.2 wt%Zr alloys exhibit the excellent thermal stability, and the hardness keeps stable even the sample was annealed at 700 °C for 300 h, showing superior microstructural stability in comparison with Cu-Ta alloy (~4.5% reduction of the hardness after 300 h at 700 °C). The softening temperature of Cu-Ta-0.2 wt%Zr alloy is up to 1028 °C (1022 °C for Cu-Ta alloy) along with higher hardness than that of Cu-Ta alloy at the same annealing temperature. This study provides a new way to fabricate dispersion strengthened Cu alloys with high strength, exceptional thermal stability and softening resistance, which have great potential application value in the field of future fusion reactor.

Influence of Minor Zr and Ti on Microstructures and Properties of Al–8·6Zn–2·5Mg–2·2Cu Alloys

Effects of Zr Addition on the Deformation Behavior, Microstructure and Mechanical Properties of Dental Ti Alloys

Effect of Ti Addition on the Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn Alloys

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Effect of Ti content on microstructure and properties of Al-9.9Zn-2.6Mg-0.91Cu-0.2Zr-xTi aluminum alloy

Effect of combined addition of Zr, Ti and Y on microstructure and tensile properties of an Al-Zn-Mg-Cu alloy

Effects of nano-sized TiB2 particles and Al3Zr dispersoids on microstructure and mechanical properties of Al–Zn–Mg–Cu based materials

Effect of Zr addition on the microstructure evolution and mechanical properties of extruded Al-Cu-Li-Mn alloys

Effect Of La, Zr Micro-Alloying On The Microstructure And Mechanical Properties Of Al-5mg-0.2ti Alloy

Influence of Zr Microalloying on the Microstructure and Room-/High-Temperature Mechanical Properties of an Al–Cu–Mn–Fe Alloy

Effects of Cr and Zr additions on the microstructure and properties of Cu-6wt.% Ag alloys

Effect of Minor Addition of Zirconium on Microstructure and Mechanical Property of Al-12Mg Alloy

Effect of Zr addition on the microstructure, phase transformation and mechanical property of Ni 50 Mn 25 Ga 17 Cu 8 alloy

Effects of Zr addition on the microstructures, mechanical properties and thermal stability of Cu-Ta alloys

Effect of Ti addition on properties of Zr54Al10.2Ni9.4Cu26.4 glass forming alloy

Effects of Different Zn/Mg Ratio and Ti Content on Hot Extruded 7xxx series Aluminum Alloy

Effect of Ti content on microstructures and mechanical properties of cast Al-2Li-2Cu-0.5Mg alloy

Effect of zirconium content on the microstructure, physical properties and corrosion behavior of Ti alloys

Influence of Zr content on microstructure and mechanical properties of As-cast Al-Zn-Mg-Cu alloy

Effects of Ti Addition on Microstructure, Mechanical Properties and Corrosion Resistance of the Cu-Zn-Ni Alloy

Effects of Al-Ti-C Refiner and Forming Processes on the Microstructure and Properties of Al-Zn-Mg-Cu Alloys