Unusual He-ion Irradiation Strengthening and Inverse Layer Thickness-Dependent Strain Rate Sensitivity in Transformable High-Entropy Alloy/metal Nanolaminates: A Comparison of Fe50Mn30Co10Cr10/Cu Vs Fe50Mn30Co10Ni10/Cu
Y. F. Zhao,H. H. Chen,D. D. Zhang,J. Y. Zhang,Y. Q. Wang,K. Wu,G. Liu,J. Sun
DOI: https://doi.org/10.1016/j.jmst.2021.10.036
2022-01-01
Journal of Material Science and Technology
Abstract:In this work, we prepare transformable HEA/Cu nanolaminates（NLs） with equal individual layer thickness（h） by the magnetron sputtering technique, i.e., Fe 50 Mn 30 Co 10 Cr 10 /Cu and Fe 50 Mn 30 Co 10 Ni 10 /Cu, and comparatively study He-ion irradiation effects on their microstructure and mechanical properties. It appears that the as-deposited HEA/Cu NLs manifest two size h-dependent hardness regimes（i.e., increased hardness at small h and hardness plateau at large h）, while the He-implanted ones exhibit monotonically increased hardness. Contrary to the fashion that smaller h renders less irradiation hardening in bimetal NLs, the Fe 50 Mn 30 Co 10 Cr 10 /Cu NLs manifest the trend that smaller h leads to greater irradiation hardening. By contrast, the Fe 50 Mn 30 Co 10 Ni 10 /Cu NLs exhibit the maximum irradiation hardening at a critical h = 50 nm. Below this critical size, smaller h results in lower radiation hardening（similar to bimetal NLs）,while above this size, smaller h results in greater radiation hardening(similar to Fe 50 Mn 30 Co 10 Cr 10 /Cu NLs). Moreover, these transformable HEA/Cu NLs display inverse h-dependent strain rate sensitivity（SRS m） before and after He-ion irradiation. Nevertheless, compared with as-deposited samples, the irradiated Fe 50 Mn 30 Co 10 Cr 10 /Cu NLs display reduced SRS, while the irradiated Fe 50 Mn 30 Co 10 Ni 10 /Cu NLs display enhanced SRS. Such unusual size-dependent irradiation strengthening and inverse h effect on SRS in irradiated samples were rationalized by considering the blocking effects of He bubbles on dislocation nucleation and motion, i.e., dislocations shearing or bypassing He bubbles.