Abstract:Bulk metallic glass(BMG) Cu58Zr20Ti20Mo2 rods with a diameter of 3 mm were prepared by using copper mould suction cast.The structure,thermal stability,compression strength and fracture morphology of this bulk metallic glass were investigated by X-ray diffractometry,differential scanning calorimetry,compression tester and scanning electronic microscopy.The results indicate that a small addition of molybdenum is beneficial for improving glass-forming ability in Cu60Zr20Ti20 system.This amorphous alloy shows a two-stage crystallization,the glass-transition temperature is about 422.6 ℃ and the onset of crystallization temperature is 453.4 ℃.Moreover,this amorphous alloy exhibits a linear relation between the stress and strain and shows a brittle fracture mode.The compression strength is about 1 720 MPa and the elongation about 3.4%.The surface morphology of fracture shows a clear vein pattern.The characteristics of both compression behaviour and fracture of Cu57Zr20Ti20Mo3 alloy with a small amount of amorphous phase are similar to those of the above fully amorphous alloy,but the strength decreases to 1 546 MPa,the elongation is 3.4% and the vein pattern becomes a little disordered and some liquid drops can be observed in the fracture surface.

Formation of bulk metallic glass in situ nanocomposite in (Cu50Zr43Al7)99Si1 alloy

Zr-based Bulk Metallic Glass Composite with in Situ Precipitated Nanocrystals

Formation and mechanical properties of Cu_(58)Zr_(20)Ti_(20)Mo_2 bulk metallic glass

Synthesis,structure and Mechanical Properties of Zr-Cu-based Bulk Metallic Glass Composites

Formation and mechanical properties of bulk Cu-Ti-Zr-Ni metallic glasses with high glass forming ability

Formation of Cu–Zr–Al Bulk Metallic Glass Composites with Improved Tensile Properties

Failure behavior of Cu–Ti–Zr-based bulk metallic glass alloys

Glass-forming ability and corrosion resistance of Zr-based Zr-Ni-Al bulk metallic glasses

Microstructural heterogeneities governing the deformation of Cu47.5Zr47.5Al5 bulk metallic glass composites

Bulk Glass Formation of 12 Mm Rod in La–Cu–Ni–Al Alloys

Plasticity-improved Zr–Cu–Al Bulk Metallic Glass Matrix Composites Containing Martensite Phase

Unusual Solidification Behavior of a Zr–Cu–Ni–Al Bulk Glassy Alloy Made from Low-Purity Zr

Microstructure evolution and mechanical properties of Cu46Zr47Al7 bulk metallic glass composite containing CuZr crystallizing phases

Is Cu60Ti10Zr30 a Bulk Glass-Forming Alloy?

Bulk metallic glass formation in the (Ti,Zr)-(Ni,Cu)-S system

73 Mm-Diameter Bulk Metallic Glass Rod By Copper Mould Casting

Formation, Thermal Stability and Mechanical Properties of Ti42.5Zr7.5Cu40Ni5Sn5 Bulk Metallic Glass

Ni- and Be-free Zr-based bulk metallic glasses with high glass-forming ability and unusual plasticity.

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

Formation of Bulk Metallic Glasses in Cu45Zr48−Al7RE (RE = La, Ce, Nd, Gd and 0 ≤x≤ 5 At.%)

Synthesis of Centimeter-Size Ag-doped Zr–Cu–Al Metallic Glasses with Large Plasticity