Modification of Poly(ethylene 2,5-Furandicarboxylate) with Aliphatic Polycarbonate Diols: 1. Randomnized Copolymers with Significantly Improved Ductility and High CO2 Barrier Performance
Hongzhou Xie,Linbo Wu,Bo-Geng Li,Philippe Dubois
DOI: https://doi.org/10.1016/j.eurpolymj.2020.109856
IF: 6
2020-01-01
European Polymer Journal
Abstract:Poly(ethylene 2,5-furandicarboxylate) (PEF) is a very promising biobased polymer possessing very high mechanical strength, rigidity and gas barrier performance. But its poor ductility and toughness may limit its applications. In this study, PEF-based copolymers with high intrinsic viscosity were successfully synthesized via melt polycondensation of dimethyl 2,5-furandicarboxylate (DMFD) and ethylene glycol in the presence of a copolycarbonate diol (PPeHC diol) as produced from 1,5-pentylene diol (PeDO), 1,6-hexylene diol (HDO) and dimethyl carbonate, and characterized with H-1 NMR, C-13 NMR, DSC, TGA, tensile, impact and gas barrier testing. The products were "randomnized" as a result of ester-carbonate exchange reaction occurring along melt polycondensation, and therefore became amorphous copolymers possessing composition-dependent physico-mechanical properties which can be tunable from rigid-to-ductile thermoplastics to thermoplastic elastomers. Particularily, the copolymers with phi(PPeHC) of 25 wt% and 30 wt% are thermoplastics possessing greatly improved ductility (elongation at break up to 194%) and CO2 barrier performance higher than poly(ethylene terephthalate) (PET; BIFCO2 3.6-2.8), and retaining high tensile modulus (2.2-1.9 GPa) and yielding strength (69-58 MPa) comparable to the bottle-grade PET. In comparison, the copolymer with phi(PPeHC) of 40 wt% behaves as a high performance thermoplastic elastomer with excellent gas barrier performance as well as high tensile strength (23 MPa).