Abstract:Mechanism of enhancement by plasma‐treated nano‐alumina in epoxy resin during polarization. In this study, to ramp up the thermal stability and insulation characteristics of epoxy resin (EP), the plasma‐treated EP/alumina composites with a mass fraction of 1 wt% were fabricated. The variations of functional groups in the EP composites with/without plasma treatment were characterized by Fourier transform infrared spectroscopy (FTIR), and the glass transition temperature of the specimens was analyzed by differential scanning calorimetry (DSC) analysis. The space charge distributions, the electrical conductivity and DC breakdown strength of the specimens were measured at 90°C. Moreover, the results were further analyzed in depth. The results indicated that the nanocomposites prepared with plasma‐treated nano‐alumina exhibited a higher concentration of OH and CO groups. At 90°C, the plasma‐treated alumina nanoparticles significantly increased the charge injection threshold of EP from about 26 nC (untreated) to 19 nC (treated); reduced the internal electric field distortion, decreased the charge accumulation and dissipation, and increased the breakdown strength from about 104 kV/mm (untreated) to 115 kV/mm (treated), and the conductivity from about 5.1 × 10−14 S/m (untreated) to 3.1 × 10−14 S/m (treated). In summary, it was elucidated that plasma‐treated nano‐alumina particles could effectively reduce deep trap density, trapped charges, charge injection and transportation and reinforce composites' insulation performance at high temperatures. Highlights The DBD plasma treatment is environmentally friendly with high efficiency. The testing adopted advanced characterization and analysis techniques. Plasma treatment of alumina nanoparticles enhanced the thermal stability. The treated nano‐alumina reinforced insulation performance of EP nanocomposites. The plasma treatment raised the space charge injection threshold and barrier.

Influence of Alumina Content and Thermal Treatment on the Thermal Conductivity of UPE/Al2O3 Composite

Preparation of AlN microspheres/UHMWPE composites for insulating thermal conductors

Effect of Modification of Al2O3on Thermal Conductivity of HDPE/PA6 Composites

Development of High Impact and Thermal Conducting Insulating Polycarbonate/Polyethylene/Alumina Composites

Effective Thermal Conductivity and Thermal Properties of Phthalonitrile‐terminated Poly(arylene Ether Nitriles) Composites with Hybrid Functionalized Alumina

Effect of the alumina micro-particle sizes on the thermal conductivity and dynamic mechanical property of epoxy resin

PROPERTIES AND APPLICATION OF PPS/ALUMINA THERMAL CONDUCTIVE COMPOSITES

Thermal and electrical properties of epoxy composites at high alumina loadings and various temperatures

Study on Preparation and Properties of Ultrahigh Molecular Weight Polyethylene Composites Filled with Different Carbon Materials

Construction of alumina framework with a sponge template toward highly thermally conductive epoxy composites

Ultra-High Molecular Weight Polyethylene Fibers/Epoxy Composites: Effect of Fiber Treatment on Properties

Excellent thermal conductive epoxy composites via adding UHMWPE fiber obtained by hot drawing method

Preparation and Thermal Conductivity of Alumina/Graphene/Waterborne Polyurethane Composite

Functionalized Al2O3 fillers/glass fibers cloth/PTFE composites with excellent thermal properties

Effect of Branched Alumina on Thermal Conductivity of Epoxy Resin

Polymer Composite with Enhanced Thermal Conductivity and Insulation Properties through Aligned Al2O3 Fiber

Thermally conductive, mechanically robust alumina-incorporated polyurethane films prepared by ultraviolet light curing

Mechanical and Thermal Properties of Al2O3-Filled Epoxy Composites

Effect of Alumina Coating and Extrusion Deformation on Microstructures and Thermal Properties of Short Carbon Fibre–al Composites

Impact of plasma‐treated nano‐alumina on the thermal and electrical properties of epoxy resin at elevated temperatures

Effect of Different Surface Treatment Agents on the Physical Chemistry and Electrical Properties of Polyethylene Nano‐alumina Nanocomposites