Gelation/crystallization Mechanisms of UHMWPE Solutions and Structures of Ultradrawn Gel Films
Xiaomei Shi,Yuezhen Bin,Daishui Hou,Yongfeng Men,Masaru Matsuo
DOI: https://doi.org/10.1038/pj.2013.66
IF: 3.135
2013-01-01
Polymer Journal
Abstract:The gelation mechanisms of ultra-high-molecular-weight polyethylene (UHMWPE) chains differed significantly in decalin and paraffin, although these are typical solvents used to gel spin UHMWPE fibers with high strengths and moduli. In both solvents, gelation was attributed to liquid–liquid phase separation driven by concentration fluctuations during the initial stage. The gelation speeds and temperatures differed significantly in the two solvents. In decalin, solvent flowed from the gels, syneresis occurred during crystallization and dry gel films were prepared. In contrast, in paraffin, many nucleating points appeared immediately, and no syneresis occurred even after quenching to room temperature. To prepare dry gel films, paraffin was blotted with filter paper, and paraffin residues were removed in hexane. However, the small-angle X-ray scattering spectra from both films were similar, indicating crystalline lamellae and ultradrawing. The gelation speeds and temperatures for decalin and paraffin differed significantly. In decalin, gel syneresis occurred by solvent flow from the gels accelerates crystallization, and dry gel films were prepared. In contrast, in paraffin, many nucleating points appeared immediately, and few syneresis occurred even after quenching to room temperature. To prepare dry gel films, paraffin was blotted with filter paper, and residual paraffin was removed in hexane. However, the small-angle X-ray scattering (SAXS) patterns from both films provided similar profiles indicating large crystalline lamellar stacking ensuring ultradrawing.