Abstract:The Ti-6Al-4V (TC4) alloy wheel hub has exhibited some defects that affect the properties during the vertical centrifugal casting process. Therefore, the analysis of the solidification process would contribute to solving the above-mentioned problems. In this study, an orthogonal experimental design was employed to optimize the process parameters (rotational speed, mold preheating temperature, and pouring temperature) of the vertical centrifugal casting method. The effects of process parameters on the velocity field, temperature field, and total shrinkage porosity during the solidification process were explored, and the microstructure and mechanical properties of the wheel hub prepared by the vertical centrifugal casting method were also investigated. The results showed that the rotational speed mainly induced the change of the velocity field. The pouring temperature and mold preheating temperature affected the temperature field and solidification time. Based on the analysis of the orthogonal experiment, the optimal parameters were confirmed as a rotational speed of 225 rpm, mold preheating temperature of 400 °C, and pouring temperature of 1750 °C, respectively. The simulation results of total shrinkage porosity were in agreement with the experiment results. The wheel hub was composed of nonuniform α and β phases. The lath α phase precipitated from larger β grains with different orientations. Compared with the other samples at different locations, the α phase in the PM sample (middle of the TC4 wheel hub) displayed high peak intensity and uniformly distributed β phase along the radial direction of the wheel hub. Moreover, the PM sample revealed a higher tensile strength of 820 MPa and similar Vickers hardness of 318 HV compared with the other samples at different locations, which were higher than those of rolling and extrusion molding. This experiment design would provide a good reference for the vertical centrifugal casting of the TC4 alloy.

Characteristics of Defect Bands and Their Formation Mechanisms in A356 Wheel Fabricated by Horizontal Squeeze Casting

Prediction of Fatigue Life for Automotive A-Alloy Wheel with Integrated Cast Defects

Defect band formation in high pressure die casting AE44 magnesium alloy

On the Tensile Failure Induced by Defect Band in High Pressure Die Casting of AM60B Magnesium Alloy

Influence of Melt Flow on the Formation of Defect Band in High Pressure Die Casting of Az91d Magnesium Alloy

Investigation on Surface Defects Produced in Pretreatment of Die-casting AM60B Magnesium Alloy

Computer-Aided Designs Of Die And Thermal Control For Fabrication Of A356 Wheels

Mechanical Properties and Microstructure of A356-T6 Aluminum Alloy Wheel Hub Based on Casting-Spinning Process

Defects Analysis and Improvement for Electricmotorcar Aluminum Alloy Wheel by Gravity Casting

The Evolution of Dilatant Shear Bands in High-Pressure Die Casting for Al-Si Alloys

Formation Mechanism and Main Control Methods of Bright‐Band Defects in Strip Casting Based on Numerical Simulation

Correlation of 3D Defect-Band Morphologies and Mechanical Properties in High Pressure Die Casting Magnesium Alloy

Failure Behavior of High Pressure Die Casting AZ91D Magnesium Alloy

A Banding Structure in A Ni-Cu-Si Cast Alloy

Numerical Simulation and Experimental Investigation of Microstructure Evolution and Flow Behavior in the Rheological Squeeze Casting Process of A356 Alloy

Effect of shot speeds on the microstructural framework and abnormal eutectic bands in a high pressure die casting hypoeutectic AlSi10MnMg alloy

Casting Defects Induced Fatigue Damage in Aircraft Frames of ZL205A Aluminum Alloy – A Failure Analysis

Numerical Simulation on Solidification during Vertical Centrifugal Casting Process for TC4 Alloy Wheel Hub with Enhanced Mechanical Properties

Fracture Failure Analysis of Twin Rolling Casting Magnesium by Hot Compression

Melt flow, solidification structures, and defects in 316 L steel strips produced by vertical centrifugal casting

Formation Mechanism of Surface Crack in Low Pressure Casting of A360 Alloy