ChemInform Abstract: α-MnO2Nanotubes: High Surface Area and Enhanced Lithium Battery Properties.

Lihong Li,Caiyun Nan,Jun Lu,Qing Peng,Yadong Li

DOI: https://doi.org/10.1002/chin.201241011

2012-01-01

ChemInform

Abstract:The title nanotubes are hydrothermally prepared from a mixture of KMnO4, NH4H2PO4, Bu4NOH, and H2O (autoclave, 180 °C, 48 h).

What problem does this paper attempt to address?

ChemInform Abstract: Α‐mno2 Nanotubes: High Surface Area and Enhanced Lithium Battery Properties.

Lihong Li,Caiyun Nan,Jun Lu,Qing Peng,Yadong Li

DOI: https://doi.org/10.1002/chin.201241011

2012-01-01

ChemInform

Abstract:AbstractThe title nanotubes are hydrothermally prepared from a mixture of KMnO4, NH4H2PO4, Bu4NOH, and H2O (autoclave, 180 °C, 48 h).
α-MnO 2 nanotubes: High surface area and enhanced lithium battery properties

Lihong Li,Caiyun Nan,Jun Lu,Qing Peng,Yadong Li

DOI: https://doi.org/10.1039/c2cc32306k

IF: 4.9

2012-01-01

Chemical Communications

Abstract:A simple one-step route for preparing alpha-MnO2 nanotubes is reported. The alpha-MnO2 nanotubes exhibit a high surface area of 226 m(2) g(-1) and reversible capacity of 512 mA h g(-1) at a high current density of 800 mA g(-1) after 300 cycles, as well as cycling stability when measured as an anode in lithium batteries.
Facile synthesis of mesoporous Mn3O4 nanotubes and their excellent performance for lithium-ion batteries

Zhongchao Bai,Na Fan,Zhicheng Ju,Chunli Guo,Yitai Qian,Bin Tang,Shenglin Xiong

DOI: https://doi.org/10.1039/c3ta11910f

IF: 11.9

2013-01-01

Journal of Materials Chemistry A

Abstract:Because of the low cost and operating potential, Mn3O4 is highly noticeable among transition metal oxides as an anode material for Li-ion batteries. Here, mesoporous Mn3O4 nanotubes with a high surface area of 42.18 m(2) g(-1) and an average pore size of 3.72 nm were synthesized for the first time through the hydrogen reduction of beta-MnO2 nanotubes under a H-2/Ar atmosphere at 280 degrees C for 3 h. Electrochemical results demonstrate that the reversible capacity of mesoporous Mn3O4 nanotubes is 641 mA h g(-1) (much higher than the theoretical capacity of graphite, similar to 372 mA h g(-1)) after 100 cycles at a high current density of 500 mA g(-1). The superior electrochemical performance can be attributed to the unique 1D mesoporous nano-tubular structure, which offers fast and flexible transport pathways for electrolyte ions, and also provides sufficient free space to buffer the large volume change of anodes based on the conversion reaction during the repeated lithium-ion insertion/extraction. The improved electrochemical performance makes such a mesoporous Mn3O4 tubular structure promising as an anode material for next-generation lithium-ion batteries.
Hydrothermal Synthesis of Monodispersed LiMnPO4 (010) Nanobelts and [001] Nanorods and Their Applications in Lithium-Ion Batteries

Liang Bao,Yifan Chen,Gang Xu,Tao Yang,Zhenguo Ji

DOI: https://doi.org/10.1002/ejic.201701270

IF: 2.551

2018-01-01

European Journal of Inorganic Chemistry

Abstract:Monodispersed single‐crystalline LiMnPO 4 nanobelts and nanorods were successfully prepared by a simple hydrothermal method. On the basis of the experimental results, a possible mechanism for the formation of the monodispersed LiMnPO 4 nanobelts and nanorods was proposed. Compared with our previously proposed flowerlike, stamenlike LiMnPO 4 /C nanostructures self‐assembled with (010) nanosheets and [001] nanorods, the corresponding monodispersed nanoparticles show enhanced electrochemical performances due to the full carbon coating along the surface. Moreover, because of the narrowed size along [100], the LiMnPO 4 @C nanorods exhibit a much higher discharge capacity compared with that of the LiMnPO 4 @C nanobelts.
Coaxial MnO/C Nanotubes As Anodes for Lithium-Ion Batteries

Y. L. Ding,C. Y. Wu,H. M. Yu,J. Xie,G. S. Cao,T. J. Zhu,X. B. Zhao,Y. W. Zeng

DOI: https://doi.org/10.1016/j.electacta.2011.04.071

IF: 6.6

2011-01-01

Electrochimica Acta

Abstract:Coaxial MnO/C nanotubes with an average diameter of about 450nm, a wall thickness of about 150nm, a length of 1–5μm and a 10nm thick carbon layer have been prepared using β-MnO2 nanotubes as self-templates in acetylene at 600°C. The microstructure of the product has been characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, high-resolution transmission electron microscopy, and Raman spectroscopy. The electrochemical performance of the product has been evaluated by galvanostatic charge/discharge cycling. It is found that the product exhibits a reversible capacity of nearly 500mAhg−1 at a current density of 188.9mAg−1, and 83.9% of capacity retention, higher than bare MnO nanotubes (58.2%) and MnO nanoparticles (25.8%). The results reveal that coaxial MnO/C nanotubes would be a promising anode material for next-generation lithium-ion batteries.
Electrochemical Properties Of 0.5li(2)Mno(3)Center Dot 0.5li(4)Mn(5)O(12) Nanotubes Prepared By A Self-Templating Method

Jingyi Cao,Jian Xie,Gaoshao Cao,Tiejun Zhu,Xinbing Zhao,Shichao Zhang

DOI: https://doi.org/10.1016/j.electacta.2013.08.039

IF: 6.6

2013-01-01

Electrochimica Acta

Abstract:Tubular 0.5Li(2)MnO(3)center dot 0.5Li(4)Mn(5)O(12) has been synthesized by a facile self-templating method starting from tubular beta-MnO2. The wall thickness and diameter of 0.5Li(2)MnO(3)center dot 0.5Li(4)Mn(5)O(12) nanotubes are around 200 and 500 nm, respectively. X-ray diffraction and transmission electron microscopy observations confirm the composite character, where the Li4Mn5O12 nano-domains are integrated with the Li2MnO3 nanodomains. The tubular composite synthesized at 600 degrees C exhibits better electrochemical properties than that synthesized at 700 degrees C due to the higher ratio of LiMn2O4 decomposed from Li4Mn3O12. The tubular composite also exhibits better electrochemical properties than the microsized aggregated particles due to the unique tubular nanostructure with large specific surface, short Li-ion diffusion pathway, and loose stacking of the tubes. (C) 2013 Elsevier Ltd. All rights reserved.
Fabrication and Electrochemical Performance of Nanofibrous Micro-Frameworks of Α-Mno2

Dalai Jin,Ruirui Liu,Xiaochu Ding,Longcheng Wang,Lina Wang,Linhai Yue

DOI: https://doi.org/10.1016/j.partic.2014.01.004

IF: 3.5

2014-01-01

Particuology

Abstract:A facile solid-phase conversion route is proposed to fabricate a micro-framework of alpha-MnO2 with a nanofibrous structure and high porosity. The fabrication is achieved by a three-step process using a preformed manganese tartrate with a rectangular framework as the precursor followed by thermal annealing and hydrothermal oxidation to form the final nanofibrous structure. Evolution of the phase and the morphology are characterized by FESEM, XRD, TG-DTA, and TEM measurements. The electrochemically active material alpha-MnO2 exhibits both attractive stability of the Coulombic efficiency after long-term cyclic charging/discharging and acceptable specific capacitance. (C) 2014 Published by Elsevier B.V.
Self-templating synthesis of single crystalline LiNi0.5Mn1.5O4 nanotubes with improved electrochemical performance

guoqing wang,jian xie,tiejun zhu,gaoshao cao,xinbing zhao,shichao zhang

DOI: https://doi.org/10.1142/S179360471450009X

IF: 1.4901

2014-01-01

Functional Materials Letters

Abstract:Single crystalline lithium nickel manganese oxide (LiNi0.5Mn1.5O4) nanotubes have been prepared by a facile self-templating method from beta-MnO2 nanotubes. The wall thickness and hollow part of the nanotubes are around 250 nm and 200 nm, respectively. The tubular LiNi0.5Mn1.5O4 exhibits good rate capability and high-rate cycling stability. At 10 C, it can yield a high discharge capacity of 99 mAh g(-1). After 550 cycles at 5 C, a discharge capacity of 85 mAhg(-1) can be kept, indicating a promising application in high-power Li-ion batteries.
Single-Crystalline Limn2o4 Nanotubes Synthesized Via Template-Engaged Reaction As Cathodes for High-Power Lithium Ion Batteries

Yuan-Li Ding,Jian Xie,Gao-Shao Cao,Tie-Jun Zhu,Hong-Ming Yu,Xin-Bing Zhao

DOI: https://doi.org/10.1002/adfm.201001448

IF: 19

2011-01-01

Advanced Functional Materials

Abstract:Single-crystalline nanotubes of spinel LiMn2O4 with a diameter of about 600 nm, a wall thickness of about 200 nm and a length of 1-4 mu m have been synthesized via a template-engaged reaction using beta-MnO2 nanotubes as a self-sacrifice template. In this fabrication, a minimal structural reorganization can be responsible for the chemical transformation from [001]-oriented beta-MnO2 template to [110]-oriented LiMn2O4. Galvanostatic charge/discharge measurements indicate that the nanotubes exhibit superior high-rate capabilities and good cycling stability. About 70% of its initial capacity can be retained after 1500 cycles at 5 C rate. Importantly, the tubular nanostructures and the single-crystalline nature of the most LiMn2O4 nanotubes are also well preserved after prolonged charge/discharge cycling at a relatively high current density, indicating good structural stability of the single-crystalline nanotubes during lithium intercalation/deintercalation process. As is confirmed from Raman spectra analyses, no evident microstructural changes occur upon long-term cycling. These results reveal that single-crystalline nanotubes of LiMn2O4 will be one of the most promising cathode materials for high-power lithium ion batteries.
Mno@1-D Carbon Composites from the Precursor C4h4mno6 and Their High-Performance in Lithium Batteries

Xiaona Li,Yongchun Zhu,Xing Zhang,Jianwen Liang,Yitai Qian

DOI: https://doi.org/10.1039/c3ra41132j

IF: 4.036

2013-01-01

RSC Advances

Abstract:MnO@1-D carbon composites were synthesized simultaneously through a single heating procedure using C4H4MnO6 as the precursor for both the MnO and 1-D carbon. MnO nanoparticles are uniformly dispersed inside or adhered to the surface of the 1-D carbon nanotubes, and these carbon nanotubes overlap each other to form carbon scaffolds. As an anode for lithium-ion batteries, the MnO@1-D carbon composites deliver a reversible capacity of 1482 mA h g(-1) at a current density of 200 mA g(-1). When the current density rises to 1460 mA g(-1), the capacity remains at 810 mA h g(-1) even after 1000 cycles. Such a unique carbon structure can act as a scaffold for MnO, which not only improves the electronic conductivity, but also provides a support for loading MnO nanoparticles. This synchronous process may pave a way to obtain such uniform and stable electrode materials with enhanced performance, which may find use in other applications such as catalysis, water treatment and supercapacitors.
Synthesis of Mn3O4nanowires and their transformation to LiMn2O4polyhedrons, application of LiMn2O4as a cathode in a lithium-ion battery

Xing Zhang,Zheng Xing,Yang Yu,Qianwen Li,Kaibin Tang,Tao Huang,Yongchun Zhu,Yitai Qian,Dong Chen

DOI: https://doi.org/10.1039/c1ce06289a

IF: 3.756

2012-01-01

CrystEngComm

Abstract:Mn3O4 nanowires with diameter of ∼15 nm and a length of up to several micrometres have been hydrothermally synthesized at 200 °C for 15 h without any surfactants. It was investigated that during the formation process of Mn3O4 nanowires the length of the nanowires increased while the diameter did not obviously change. The coercivity of the Mn3O4 nanowires is up to 5600 Oe at 5 K. As these Mn3O4 nanowires were treated with LiOH by solid state reaction at 750 °C for 6 h, interconnected LiMn2O4 polyhedrons were obtained. The achieved discharge capacity of the LiMn2O4 polyhedrons was 115 mAh g−1 and they retained 98.3% of this capacity after 60 cycles at 0.1 C.
Facile Synthesis of Porous MnO/C Nanotubes As a High Capacity Anode Material for Lithium Ion Batteries.

Gui-Liang Xu,Yue-Feng Xu,Hui Sun,Fang Fu,Xiao-Mei Zheng,Ling Huang,Jun-Tao Li,Shi-He Yang,Shi-Gang Sun

DOI: https://doi.org/10.1039/c2cc34218a

IF: 4.9

2012-01-01

Chemical Communications

Abstract:Porous MnO/C nanotubes are synthesized by a facile hydrothermal method followed by thermal annealing, and possess excellent cyclability and high rate capability as an anode for lithium ion batteries.
Tio2 Nanotube Arrays Grafted With Mno2 Nanosheets As High-Performance Anode For Lithium Ion Battery

Qiancheng Zhu,Hao Hu,Guojian Li,Chenbo Zhu,Ying Yu

DOI: https://doi.org/10.1016/j.electacta.2015.01.023

IF: 6.6

2015-01-01

Electrochimica Acta

Abstract:Unique TiO2 nanotube arrays (TNAs) grafted with MnO2 nanosheets is synthesized for the first time as an anode for Li battery. The character of the special structure is MnO2 nanosheets grown on the outer, inner surface and tip of the TNAs. The composite combines the advantages both from MnO2 with high capacity (1230 mA h g(-1)) and TNAs with excellent cycle stability and superior electrical conductivity. Besides, the MnO2 nanosheet layer with different thickness on the surface of TNAs is fabricated through controlling hydrothermal reaction time and it is found that the thickness has a significant impact on capacity, cycle performance and conductivity. Additionally, a very abnormal phenomenon that we call "late rise of capacity" is discovered in the capacity test after several hundreds of cycle times, for which a possible mechanism is proposed according to material characterization. (C) 2015 Elsevier Ltd. All rights reserved.
Electrochemical Properties of 0.5li2mno3·0.5li4mn5o12 Nanotubes Prepared by a Self-Templating Method

Jingyi Cao,Jian Xie,Gaoshao Cao,Tiejun Zhu,Xinbing Zhao,Shichao Zhang

DOI: https://doi.org/10.1016/j.electacta.2013.08.039

IF: 6.6

2013-01-01

Electrochimica Acta

Abstract:•Tubular 0.5Li2MnO3·0.5Li4Mn5O12 has been synthesized by a self-templating route.•The diameter and wall thickness of the nanotubes are 500 and 200nm, respectively.•The nanotubes exhibit a well-defined composite character.•The tubular composite shows a stable capacity of around 200mAhg−1 at 0.1C.
Reshaping carbon-coated Mn2Mo3O8 nanotubes and enhanced sodium storage performance

Lifeng Zhang,Liyue Xue,Jiaxi Bai,Kexin He,Bangmei Lu

DOI: https://doi.org/10.1039/d3cc03683a

IF: 4.9

2023-10-26

Chemical Communications

Abstract:Mn2Mo3O8/C nanotubes are successfully reshaped from micron-sized MnMoO4 blocks via a simple microwave combined calcination method using dopamine as both scissors and carbon source. The synthesized Mn2Mo3O8/C nanotube (MMOC-2) exhibits enhanced sodium storage performance as anodes for half-cell (217 mAh g-1 with ca. 99% coulombic efficiency after 500 cycles) and full-cell (capacity retention of 75% after 100 cycles), which is attributed to the uniquely reshaped nanostructures with abundant active sites, short ion diffusion path and fast charge transfer.

chemistry, multidisciplinary
ChemInform Abstract: Double‐Shelled CoMn2O4 Hollow Microcubes As High‐Capacity Anodes for Lithium‐Ion Batteries.

Liang Zhou,Dongyuan Zhao,Xiong Wen Lou

DOI: https://doi.org/10.1002/chin.201217009

2012-01-01

ChemInform

Abstract:AbstractNew double‐shelled CoMn2O4 hollow microcubes with nanometer‐sized building blocks are prepared by annealing Co0.33Mn0.67CO3 (600 °C, 5 h in air) obtained by coprecipitation from aqueous solutions of Co(NO3)2, MnSO4, EtOH, (NH4)2SO4, and NH4HCO3 (50 °C, 9 h).
One-Step Synthesis of Mno2 Flower/Carbon Nanotube with Improved Lithium Storage Properties

Zhuang Liu,Yongmin Wu,Jinghong Li

DOI: https://doi.org/10.1166/jnn.2015.9207

2015-01-01

Journal of Nanoscience and Nanotechnology

Abstract:This work reports a one-step hydrothermal synthesis of MnO2-flower/Carbon nanotube (CNTs) binary material, featuring a coated-worm like structure. The material showed a specific capacity of 800 mA h g(-1), a working plateau at 0.5 V against a Li+/Li electrode, and ideal stability under a current density of 2 A g(-1). The transition of the crystalline form of MnO2 was also observed when adjusting the ratio of CNTs in the reaction, which may be an intriguing result for the material's future application.
One-pot facile synthesis of hierarchical hollow microspheres constructed with MnO2 nanotubes and their application in lithium storage and water treatment

Jian Wang,Jun Liu,Yichun Zhou,Peter D. Hodgson,Yuncang Li

DOI: https://doi.org/10.1039/c3ra44244f

IF: 4.036

2013-01-01

RSC Advances

Abstract:Semiconductor alpha-MnO2 hierarchical hollow microspheres constructed with nanotubes have been facilely synthesized through a bubble template-based self-scrolling solution route. An energy-minimizing-driven self-assembly of alpha-MnO2 nanoparticles on the base of O-2 bubbles is responsible for the formation of hierarchical hollow microsphere structure. The as-obtained alpha-MnO2 products were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET), and UV-vis-NIR spectrophotometry. The Li ion storage and water treatment performances of these alpha-MnO2 hierarchical hollow microspheres constructed with nanotubes were tested. A discharge capacity as high as 983 mA h g(-1) during the 30th cycle has been delivered at a current density of 300 mA g(-1). These as-prepared samples were also used as adsorbents in water treatment, and showed an excellent ability to remove organic pollutants without any other additives.
ChemInform Abstract: Titania Nanosheets Hierarchically Assembled on Carbon Nanotubes As High‐Rate Anodes for Lithium‐Ion Batteries.

Hao Bin Wu,Xiong Wen Lou,Huey Hoon Hng

DOI: https://doi.org/10.1002/chin.201224007

2012-01-01

ChemInform

Abstract:AbstractHierarchically structured nanocables with TiO2 nanosheets anchored on carbon nanotubes are prepared from carbon nanotubes and Ti(O‐Bu)4 dispersed in a mixture of DMF and iPrOH (autoclave, 180 °C, 20 h) followed by calcination in N2 at 500 °C for 2 h.
High Rate LiMn2O4/carbon Nanotube Composite Prepared by a Two-Step Hydrothermal Process

Bang-Kun Zou,Xiao-Hang Ma,Zhong-Feng Tang,Chu-Xiong Ding,Zhao-Yin Wen,Chun-Hua Chen

DOI: https://doi.org/10.1016/j.jpowsour.2014.06.085

IF: 9.2

2014-01-01

Journal of Power Sources

Abstract:A two-step hydrothermal approach is employed to synthesize LiMn2O4/carbon nanotube (LMO/CNT) composite powders. X-ray diffraction, scanning electron microscopy, thermal gravimetry and N2-adsorption/desorption are used to characterize their structures and compositions. Galvanostatic cycling in coin-cells is adopted to measure their electrochemical properties as cathode materials of lithium-ion batteries. A LiMn2O4 pure phase of high crystallinity is observed with CNT homogeneously dispersed in the composite network. The electrochemical properties of them are associated with two factors, i.e. the content of CNT in the hydrothermal process and the annealing temperature at the subsequent heat treatment step. Excellent rate capability of these LMO/CNT electrodes can be achieved.

ChemInform Abstract: α-MnO2Nanotubes: High Surface Area and Enhanced Lithium Battery Properties.

ChemInform Abstract: Α‐mno2 Nanotubes: High Surface Area and Enhanced Lithium Battery Properties.

α-MnO 2 nanotubes: High surface area and enhanced lithium battery properties

Facile synthesis of mesoporous Mn3O4 nanotubes and their excellent performance for lithium-ion batteries

Hydrothermal Synthesis of Monodispersed LiMnPO4 (010) Nanobelts and [001] Nanorods and Their Applications in Lithium-Ion Batteries

Coaxial MnO/C Nanotubes As Anodes for Lithium-Ion Batteries

Electrochemical Properties Of 0.5li(2)Mno(3)Center Dot 0.5li(4)Mn(5)O(12) Nanotubes Prepared By A Self-Templating Method

Fabrication and Electrochemical Performance of Nanofibrous Micro-Frameworks of Α-Mno2

Self-templating synthesis of single crystalline LiNi0.5Mn1.5O4 nanotubes with improved electrochemical performance

Single-Crystalline Limn2o4 Nanotubes Synthesized Via Template-Engaged Reaction As Cathodes for High-Power Lithium Ion Batteries

Mno@1-D Carbon Composites from the Precursor C4h4mno6 and Their High-Performance in Lithium Batteries

Synthesis of Mn<sub>3</sub>O<sub>4</sub>nanowires and their transformation to LiMn<sub>2</sub>O<sub>4</sub>polyhedrons, application of LiMn<sub>2</sub>O<sub>4</sub>as a cathode in a lithium-ion battery

Facile Synthesis of Porous MnO/C Nanotubes As a High Capacity Anode Material for Lithium Ion Batteries.

Tio2 Nanotube Arrays Grafted With Mno2 Nanosheets As High-Performance Anode For Lithium Ion Battery

Electrochemical Properties of 0.5li2mno3·0.5li4mn5o12 Nanotubes Prepared by a Self-Templating Method

Reshaping carbon-coated Mn2Mo3O8 nanotubes and enhanced sodium storage performance

ChemInform Abstract: Double‐Shelled CoMn2O4 Hollow Microcubes As High‐Capacity Anodes for Lithium‐Ion Batteries.

One-Step Synthesis of Mno2 Flower/Carbon Nanotube with Improved Lithium Storage Properties

One-pot facile synthesis of hierarchical hollow microspheres constructed with MnO2 nanotubes and their application in lithium storage and water treatment

ChemInform Abstract: Titania Nanosheets Hierarchically Assembled on Carbon Nanotubes As High‐Rate Anodes for Lithium‐Ion Batteries.

High Rate LiMn2O4/carbon Nanotube Composite Prepared by a Two-Step Hydrothermal Process