Abstract:Through the redox reaction between Cu(NH3)(4)(2+) and H2O2, copper quantum dots (QDs) were deposited onto the surface of single-crystal rutile TiO2 nanorod arrays that were grown directly on transparent, conductive fluorine-doped tin oxide substrates by a facile hydrothermal process. Compared with pristine TiO2 nanorods, the top facets of TiO2 nanorods decorated with Cu QDs became flattened and adherent to each other, and the lateral facets were rough and covered with vast amounts of extremely small particles. The QDs were tightly attached on the surface of the nanorods, and the nanoparticle size measured from high resolution transmission electron microscopy images was around 6 nm, which is comparable with the Bohr exciton radius. X-ray photoelectron spectroscopy measurements showed that the QDs existed in the form of Cu(II)O and Cu(I)(2)O after the deposition process, and the Cu(0) QDs were unstable on the TiO2 surface. Furthermore, under the irradiation of a solar simulator, the photocurrent response of the QD sensitized TiO2 nanorods was improved dramatically with a small amount of QDs, and the optimal photocurrent density (98 mu A/cm(2)) was much greater than that of the undecorated sample (16 mu A/cm(2)). Likewise, external quantum efficiency (EQE) characterization demonstrated the superiority of the surface modification with Cu QDs, by which the highest EQE value of the photoanode was enhanced nearly ten times. In addition, a red shift of the peak in EQE measurement was found from the Cu QD sensitized samples, suggesting a quantum size effect caused by small QD particles.

Ultralong Rutile TiO 2 Nanorod Arrays with Large Surface Area for CdS/CdSe Quantum Dot-sensitized Solar Cells

CdS/ZnS Co-Sensitized Hierarchical TiO2Nanotree Array with Rutile/Anatase Junctions for Enhanced Photoelectrochemical Performance

Construction of TiO2 NP@TiO2 NT Double-Layered Structural Photoanode to Enhance Photovoltaic Performance of CdSe/CdS Quantum Dots Sensitized Solar Cells

Synthesis and Characterization of Bi2S3 Quantum Dot-Sensitized TiO2 Nanorod Arrays Coated with ZnSe Passivation Layers

TiO 2 Nanorod Arrays Sensitized with CdS Quantum Dots for Solar Cell Applications: Effects of Rod Geometry on Photoelectrochemical Performance

Hydrothermal Etching Treatment to Rutile TiO2 Nanorod Arrays for Improving the Efficiency of CdS-Sensitized TiO2 Solar Cells

CdSe/CdS quantum dots co-sensitized TiO 2 nanotube array photoelectrode for highly efficient solar cells

Improved Photoelectrical Performance of Single-Crystal Tio2 Nanorod Arrays by Surface Sensitization with Copper Quantum Dots

CdS Quantum Dot-Sensitized Solar Cells Based on Nano-Branched TiO2 Arrays

CdS/CdSe Co-Sensitized Vertically Aligned Anatase TiO2 Nanowire Arrays for Efficient Solar Cells

Rutile TiO2 nano-branched arrays on FTO for dye-sensitized solar cells.

Dual-functional Hetero-Structured TiO2 Nanotrees Composed of Rutile Trunks and Anatase Branches for Improved Performance of Quantum Dot-Sensitized Solar Cells.

Glutathione-assisted Hydrothermal Synthesis of CdS-decorated TiO2 Nanorod Arrays for Quantum Dot-Sensitized Solar Cells

Rectangular Bunched Rutile TiO<sub>2</sub> Nanorod Arrays Grown on Carbon Fiber for Dye-Sensitized Solar Cells

Microsphere Assembly of Rutile TiO2 Hierarchically Hyperbranched Nanorods: CdS Sensitization and Photovoltaic Properties

Cds/Cdse Cosensitized Oriented Single-Crystalline Tio2 Nanowire Array for Solar Cell Application

Ultralong Rutile TiO2 Nanowire Arrays for Highly Efficient Dye-Sensitized Solar Cells.

A Novel Sb2S3-Sb2 Se3 Nanostructure on Single-Crystalline TiO2 Nanorod Arrays for Solar Cell Applications

Rectangular bunched rutile TiO2 nanorod arrays grown on carbon fiber for dye-sensitized solar cells.

Quantum-Dots-Sensitized Solar Cells Based on Vertically Ranged Titanium Dioxide Nanotubes

Photosensitization of TiO2 nanorods with CdS quantum dots for photovoltaic devices