A Novel Sb2S3-Sb2 Se3 Nanostructure on Single-Crystalline TiO2 Nanorod Arrays for Solar Cell Applications

陈延学,李逸坦,张瑞梓,隋行

DOI: https://doi.org/10.3969/j.issn.1672-6030.2013.05.001

2013-01-01

Nanotechnology and Precision Engineering

Abstract:Semiconductor quantum dots have attracted significant attention in the past few years as a next generation absorber material for solar cell applications. Sb2S3and Sb2Se3quantum dots have become important building blocks in solar energy conversion due to their unique optoelectronic properties,including high optical absorptivity and tunable band gap. In this paper,a novel method for increasing the effective action area is presented via the introduction of 3D TiO2nanorod arrays. By using a hydrothermal method at low temperature,a large area of anatase TiO2nanorod arrays was successfully grown on the fluorinedoped tin oxide( FTO) conductive glass. Sb2S3-Sb2Se3nanostructures were deposited onto TiO2nanorod arrays via a successive ionic layer adsorption and reaction( SILAR) method. The phases of Sb2S3and Sb2Se3nanocrystals were characterized by X-ray diffraction( XRD) pattern. Scanning electron microscopy( SEM) studies reveal that the Sb2S3nanoparticles adhered to the single-crystalline TiO2nanorods,and the space between the nanorods was filled with Sb2Se3nanoparticles,which would increase the contact area between TiO2and nanoparticles. As the SILAR cycles of Sb2Se3nanoparticles growth increased,the band gap of the samples was narrowed,which suggests a controllable absorption edge from 1. 7 eV to long wave length. The nanostructure has such advantages as large surface area,easy and efficient synthesis process and strong controllability,which may help advance the development of sensitized solar cells in the future.