Abstract:Two-dimensional (2D) quasi-ordered nitrogen-enriched porous carbon (QNPC) nanohybrids, with the characteristics of an ultrathin graphite nanosheet framework and thick quasi-ordered nitrogen-doped carbon cladding with a porous texture, have been synthesized via an in situ polymerization assembly method. In the synthesis, the expandable graphite (EG) is enlarged by an intermittent microwave method, and then aniline monomers are intercalated into the interlayers of the expanded EG with the assistance of a vacuum. Subsequently, the intercalated aniline monomers could assemble on the interlayer surface of the expanded EG, accompanied by the in situ polymerization from aniline monomers to polyaniline. Meanwhile, the expanded EG could be exfoliated to graphite nanosheets. By subsequent pyrolysis and activation processes, the QNPC nanohybrids could be prepared. As supercapacitor electrodes, a typical QNPC12-700 sample derived from the precursor containing an EG content of 12%, with a high level of nitrogen doping of 5.22 at%, offers a high specific capacitance of 305.7 F g(-1) (1 A g(-1)), excellent rate-capability and long-term stability. Notably, an extremely high energy density of 95.7 Wh kg(-1) at a power density of 449.7 W kg(-1) in an ionic liquid electrolyte can be achieved. The unique structural features and moderate heteroatom doping of the QNPC nanohybrids combines electrochemical double layer and faradaic capacitance contributions, which make these nanohybrids ideal candidates as electrode materials for high-performance energy storage devices.

Nitrogen-doped sandwich-like porous carbon nanosheets for high volumetric performance supercapacitors

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

Nitrogen-doped porous carbons with nanofiber-like structure derived from poly (aniline-co-p-phenylenediamine) for supercapacitors

Sandwich-like nitrogen-doped porous carbon/graphene nanoflakes with high-rate capacitive performance

Synthesis of Nitrogen-Doped Polymeric Resin-Derived Porous Carbon for High Performance Supercapacitors

2D Quasi-Ordered Nitrogen-Enriched Porous Carbon Nanohybrids for High Energy Density Supercapacitors.

Facile synthesis of porous carbon materials with extra high nitrogen content for supercapacitor electrodes

Nitrogen-doped porous carbon derived from biomass waste for high-performance supercapacitor

Facile synthesis of nitrogen-enriched nanoporous carbon materials for high performance supercapacitors.

Promising Biomass-Derived Nitrogen-Doped Porous Carbon for High Performance Supercapacitor

Nitrogen-Doped Porous Carbon/Graphene Aerogel with Much Enhanced Capacitive Behaviors

Nitrogen-doped interpenetrating porous carbon/graphene networks for supercapacitor applications

Nitrogen-doped porous carbon with a hierarchical structure prepared for a high performance symmetric supercapacitor

Nitrogen-doped porous carbon materials derived from ionic liquids as electrode for supercapacitor

N/O Co-Enriched Amorphous Carbon Coated Graphene with a Sandwiched Porous Architecture As Supercapacitor Electrodes with High Volumetric Specific Capacitance

Facile Synthesis of Poly(P-Phenylenediamine)-Derived Three-Dimensional Porous Nitrogen-Doped Carbon Networks for High Performance Supercapacitors

Facile 3D Nitrogen‐Doped Hierarchical Porous Carbon for High‐Performance Supercapacitors

Synthesis of ultrahigh-surface-area nitrogen-doped porous carbon materials from carboxymethyl cellulose based protic polyanion ionic liquids for high performance supercapacitors

Resin-Derived Activated Carbons with In-Situ Nitrogen Doping and High Specific Surface Area for High-Performance Supercapacitors

High Specific Capacitance Electrode Material for Supercapacitors Based on Resin-Derived Nitrogen-Doped Porous Carbons

High Packing Density and Rich Pseudocapactive Nitrogen Doped Nanocarbon Boosts Superior Volumetric-Supercapacitor Performance