Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

Influence Of Zro2 Content On The Performances Of Bn-Zro2-Sic Composites For Application In The Steel Industry

Influence of Zrc Content on the Elevated Temperature Tensile Properties of Zrcp/W Composites

Corrosion Behavior and Microstructural Evolution of BN–ZrO2–SiC Composites in Molten Steel

Effect of ZrO2 content on microstructure, mechanical properties and thermal shock resistance of (ZrB2+3Y-ZrO2)/BN composites

Effect of SiC Content on Mechanical Properties and Thermal Shock Resistance of BN–ZrO2–SiC Composites

Corrosion kinetics and corrosion mechanisms of BN–ZrO 2 –SiC composites in molten steel

Effect of ZrO 2 contents on the mechanical and thermal shock properties of ZrO 2p(3Y)/BN-SiO 2 ceramics composite

Microstructure and Mechanical Properties of ZrB2-SiC Composites

Effect of ZrO2 on sintering behavior and properties of h-BN/ZrO2 composites by spark plasma sintering

Influence of SiCnp Content on the Microstructure and Mechanical Properties of ZrB2–SiC Nanocomposite

Enhanced Strengths and Thermal Shock Resistance of SiC-BN-10 Vol% Cf Composites Through ZrB2 Addition

Corrosion resistance of BN–ZrO2 ceramics with different additives by molten steel

Effects of ZrB2 on Mechanical Properties of Al2O3-ZrB2-SiC Composite Ceramics at Room Temperature

Preparation and Characterization of High-Performance ZrB 2 –sic–cf Composites Sintered at 1450 °C

Low-Temperature Sintering Behavior and Mechanical Properties of Bn-Zro2-Sic Composites

In Situ Synthesis, Mechanical Properties, and Oxidation Resistance of (sic+zrb2)/zr3[al(si)]4c6 Composites

In Situ Preparation and Mechanical Properties of (ZrB2+ZrC)/Zr3[Al(Si)]4C6 Composites

Zirconia Reinforced Reaction Bonded Silicon Carbide Composites: Microstructure and Mechanical Properties

Influence of sol-gel derived ZrB2 additions on microstructure and mechanical properties of SiBCN composites

THE INFLUENCE OF ZrC PARTICLE CONTENT ON THE MECHANICAL PROPERTIES OF TUNGSTEN MATRIX COMPOSITES

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions