Abstract:In this paper, we discussed recent studies done in our laboratories with a floating catalyst chemical vapor deposition (CVD) method. We can grow single- or double-walled carbon nanotubes (SWNTs/DWNTs) with different kinds of catalysts. Single-walled carbon nanotubes without amorphous carbon coating were prepared by thermally decomposing acetylene (C2H2) at the temperature range of 750–1200°C with ferrocene as catalyst. While with sulfur promoted ferrocene catalyst, double-walled carbon nanotubes were mass-produced by pyrolizing C2H2 at the temperature range of 900–1100°C. Furthermore, tunable growth of DWNTs with different diameter was achieved in our experiment. It is found that DWNTs produced at lower carbon partial pressure have much smaller inner tubes, even DWNTs with the smallest inner diameter of 0.4nm was found in here. As convenient and effective tool, radial breathing mode (RBM) of Raman scattering technique can be used to distinguish SWNTs from DWNTs. In further studies of Raman scattering with DWNTs, the possible match of the inner tubes and the outer tubes according to the RBM bands was assigned, and different chirality types were discussed according to the diameter and chirality dependence of resonant Raman vibration. We also investigated the temperature-dependent frequency shift of resonant Raman spectra of DWNTs in the range of 78–650K. We found that different RBM peaks, which are relative to different tube diameters, have different temperature coefficient of frequency shift, and the larger diameter carbon nanotubes have more RBM frequency downshift with increasing temperature. It is ascribed to the RBM frequency variation to the temperature dependence of the stretching force constant of C–C bond. Besides, Polarized Raman spectra were preformed on well-aligned SWNTs structure fabricated through post-growth method and found that the angular dependence of Raman intensity is consistent well with the predictions of the resonance Raman theory.

Diameter-controlled and nitrogen-doped vertically aligned single-walled carbon nanotubes

Reduction of single‐walled carbon nanotube diameter to sub‐nm via feedstock

Diameter Controlled CVD Synthesis of Single-Walled Carbon Nanotubes

Diameter Controlled Chemical Vapor Deposition Synthesis of Single-Walled Carbon Nanotubes.

The influence of ethanol on the growth and structure of carbon nanotubes

Diameter-controlled Growth of Aligned Single-Walled Carbon Nanotubes on Quartz Using Molecular Nanoclusters As Catalyst Precursors

Importance of diameter control on selective synthesis of semiconducting single-walled carbon nanotubes.

Controlling the Diameters in Large-Scale Synthesis of Single-Walled Carbon Nanotubes by Catalytic Decomposition of CH4

Towards the preparation of single-walled carbon nanotubes with average diameter of 1.2 nm

Synthesis of nitrogen doped single wall carbon nanotubes with caffeine

Controlled Growth of Single-Walled Carbon Nanotubes at Atmospheric Pressure by Catalytic Decomposition of Ethanol and an Efficient Purification Method

Synthesis of Carbon Nanotubes by Decomposing Alcohol

Diameter-Controlled Synthesis of Carbon Nanotubes Using [2n]collarenes As Rigid Organic Templates

Diameter‐Selective Density Enhancement of Horizontally Aligned Single‐Walled Carbon Nanotube Arrays by Temperature‐Mediated Method

Synthesis of Vertically-Aligned Cnt Arrays from Diameter-Controlled Fe3o4 Nanoparticles

Structural and Compositional Regulation of Nitrogen-Doped Carbon Nanotubes with Nitrogen-Containing Aromatic Precursors

Diameter-Controlled Synthesis of Carbon Nanotubes Using [2 n ]Collarenes as Rigid Organic Templates

Precise control of the number of walls formed during carbon nanotube growth using chemical vapor deposition

Controlled synthesis of N-type single-walled carbon nanotubes with 100% of quaternary nitrogen

Large-Scale Synthesis of Long Double-Walled Carbon Nanotubes

Controllable preparation and properties of single-/double-walled carbon nanotubes