Abstract:We present a novel floating catalyst synthesis route for individual, i.e. non-bundled, small diameter single-walled carbon nanotubes (SWCNTs) with a narrow chiral angle distribution peaking at high chiralities near the armchair species. An ex situ spark discharge generator was used to form iron particles with geometric number mean diameters of 3-4 nm and fed into a laminar flow chemical vapour deposition reactor for the continuous synthesis of long and high-quality SWCNTs from ambient pressure carbon monoxide. The intensity ratio of G/D peaks in Raman spectra up to 48 and mean tube lengths up to 4 microns were observed. The chiral distributions, as directly determined by electron diffraction in the transmission electron microscope, clustered around the (n,m) indices (7,6), (8,6), (8,7) and (9,6), with up to 70% of tubes having chiral angles over 20°. The mean diameter of SWCNTs was reduced from 1.10 to 1.04 nm by decreasing the growth temperature from 880 to 750 °C, which simultaneously increased the fraction of semiconducting tubes from 67 to 80%. Limiting the nanotube gas phase number concentration to approx. 100 000 per cubic centimetre successfully prevented nanotube bundle formation that is due to collisions induced by Brownian diffusion. Up to 80 % of 500 as-deposited tubes observed by atomic force and transmission electron microscopy were individual. Transparent conducting films deposited from these SWCNTs exhibited record low sheet resistances of 63 Ohms/sq. at 90 % transparency for 550 nm light.

Direct synthesis of high-quality single-walled carbon nanotubes by the physical nucleation of iron nanoparticles in an atmospheric pressure carbon monoxide flow

Water-Assisted Preparation of High-Purity Semiconducting (14,4) Carbon Nanotubes

Synthesis Of Large Quantity Single-Walled Carbon Nanotubes By Arc Discharge

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Catalyst Design Using Nanoporous Iron for the Chemical Vapor Deposition Synthesis of Single-Walled Carbon Nanotubes

A New Method to Fabricate Large Amount of Single-Walled Carbon Nanotubes

A Single‐Step Process to Produce Carbon Nanotube‐Zinc Compound Hybrid Materials

Thin-Film Metal Catalyst For The Production Of Multi-Wall And Single-Wall Carbon Nanotubes

Large Scale Synthesis of Single-Wall Carbon Nanotubes by Arc-Discharge Method

Synthesis of High-Quality Single-Walled Carbon Nanotubes by High-Frequency-induction Heating

Low-cost Synthesis of Single-Walled Carbon Nanotubes by Low-Pressure Air Arc Discharge

Gas phase synthesis of non-bundled, small diameter single-walled carbon nanotubes with near-armchair chiralities

Carbon Nanotubes Synthesized By Rapid Quenching Of Red-Hot Graphite Rod In Ethyl Alcohol

Aerosol synthesis of single-walled carbon nanotubes by tuning feeding flow configuration for transparent conducting films

Growth of Single-Walled Carbon Nanotubes from Solid Carbon Nanoparticle Seeds via Cap Formation Engineering with a Two-Step Growth Process and Water Vapor Supply

Direct Synthesis of High Purity Single-Walled Carbon Nanotube Fibers by Arc Discharge

Controlled Growth of Single-Walled Carbon Nanotubes at Atmospheric Pressure by Catalytic Decomposition of Ethanol and an Efficient Purification Method

A Novel Method to Produce Large Amount Single-Walled Carbon Nanotubes by Arc Discharging

Synthesis of Single-Walled Carbon Nanotubes by the Vertical Floating Catalyst Method

Direct Growth of Single-Walled Carbon Nanotubes without Metallic Residues by Using Lead as a Catalyst