Abstract:Mesoporous silica with Ia (3) over bard structure has been successfully prepared by using mixed surfactants of commercially available nonionic block copolymer P123 (EO(20)PO(70)EO(20)) and anionic sodium dodecyl sulfate (SDS) as structure-directing agents through an acid-catalyzed silica sol-gel process. XRD, TEM, and N(2) sorption measurements show that the products have highly ordered bicontinuous cubic mesostructure with high surface area (similar to 770 m(2)/g), large pore volume (similar to 1.5 cm(3)/g) and uniform pore size (similar to 10 nm). Effects of preparation parameters on the formation of the mesostructure have been extensively investigated. It is found that the molar ratios of SDS/P123 between 2.1 and 2.5 and that of silicic species to P123 in the range from 40 to 75 are favorable for the formation of highly ordered Ia (3) over bard mesostructure. Prolonging hydrothermal treatment time leads to almost unchanged cell parameters of the products, whereas there is obvious increase of the pore sizes and pore volume. The results show that resultant template-free mesoporous silica products have excellent thermal stability, and they are more stable in N2 atmosphere than in air. Morphologies of the resultant materials can be further controlled by adding inorganic salt (such as Na(2)SO(4)) into the mixed surfactants system. Coral- and petaline-like mesoporous silica with continuous skeletons can be obtained. Understanding this synthesis system might be useful for economical and large-scale production of mesoporous materials with controllable structures.

Facile Preparation of Highly Ordered Small Pore Mesoporous Silicas

An Economic Method for Synthesis of Highly Ordered Porous Silica.

Synthesis of ordered small pore mesoporous silicates with tailorable pore structures and sizes by polyoxyethylene alkyl amine surfactant

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Synthesis of Ordered Mesoporous Silica with Tunable Morphologies and Pore Sizes Via a Nonpolar Solvent-Assisted Stöber Method

Preparation of Ordered 2-D Hexagonal Mesoporous Silica with Ultra Thick Pore Walls Using a Novel Nonionic Organosilicon Surfactant

Synthesis of Ordered Mesoporous Silica with Nonionic Surfactant/Anionic Polyelectrolyte as Template under Near-Neutral pH Conditions.

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Synthesis of ordered MCM-48 by introducing economical anionic surfactant as co-template

Mixed Surfactant Templating Route for Mesoporous Silica

Sustainable synthesis of ordered mesoporous materials without additional solvents

Rapid Synthesis of Ordered Mesoporous Silica with the Aid of Heteropoly Acids

Synthesis of Highly Ordered Mesoporous Silica Using Cationic Trimeric Surfactant As Structure-Directing Agent

Preparation of High‐Quality MCM‐48 Mesoporous Silica and the Mode of Action of the Template

Silicone Surfactant Templated Mesoporous Silica

A Facile Preparation of Transparent and Monolithic Mesoporous Silica Materials

Preparation Of Ordered Mesoporous Silica From Polyhedral Oligomeric Silsesquioxane

Facile Preparation of Hierarchically Meso-Mesoporous Silicas with Ultra-Large Pores and Pore Volumes Via Partitioned Cooperative Self-Assembly Process

Formation Mechanism of Anionic Surfactant-Templated Mesoporous Silica

Acid Catalyzed Synthesis of Ordered Bifunctionalized Mesoporous Organosilicas with Large Pore

Synthesis of Mesoporous MCM-48 Molecular Sieves with Cationic and Anionic Mixed Surfactant System as Template