Abstract:Grain size engineering, particularly reducing grain size into the nanocrystalline regime, offers a promising pathway to further improve the strength-to-weight ratio of Al alloys. Unfortunately, the fabrication of nanocrystalline metals often requires non-equilibrium processing routes, which typically limit the specimen size and require large energy budgets. In this study, multiple dopant elements in ternary Al alloys are deliberately selected to enable segregation to the grain boundary region and promote the formation of amorphous complexions. Three different fully dense bulk nanocrystalline Al alloys (Al-Mg-Y, Al-Fe-Y, and Al-Ni-Y) with small grain sizes were successfully fabricated using a simple powder metallurgy approach, with full densification connected directly to the onset of amorphous complexion formation. All the compositions demonstrate densities above 99% with grain sizes <60 nm following consolidation via hot pressing at 585 °C. The very fine grain structure results in excellent mechanical properties, as evidenced by nanoindentation hardness values in the range of 2.2-2.8 GPa. Detailed microstructural characterization verifies the segregation of all dopant species to grain boundaries as well as the formation of amorphous complexions, which suggests their influential role in aiding effective consolidation and endowing thermal stability in the alloys. Moreover, nanorods with a core-shell structure are also observed at the grain boundaries, which likely contribute to the stabilization of the grain structure while also strengthening the materials. Finally, intermetallic particles with sizes of hundreds of nanometers form in all systems. As a whole, the results presented here demonstrate a general alloy design strategy of segregation and boundary evolution pathway that enables the fabrication of multiple nanocrystalline Al alloys with hierarchical microstructures and improved performance.

Processing behavior of nanocrystalline NiAl during milling, sintering and mechanical loading and interpretation of its intergranular fracture

Refining Micron-Sized Grains to Nanoscale in Ni-Co Based Superalloy by Quasistatical Compressive Deformation at High Temperature

Study on preparation and mechanical property of nanocrystalline NiAl intermetallic

Fabrication of nanocrystalline supersaturated W–Al alloys with enhanced thermal stability and high sinterability

Formation of Nanocrystalline Fcc Phase by Mechanically Driven Crystallization

Bulk nanocrystalline Al alloys with hierarchical reinforcement structures via grain boundary segregation and complexion formation

Microstructure and Mechanical Properties of Ultrafine Grained CoCrFeNi and CoCrFeNiAl0.3 High Entropy Alloys Reinforced with Cr2O3/Al2O3 Nanoparticles

Nanophase And Ultrafine-Grained Powders Prepared By Mechanical Milling: Full Density Processing And Unusual Mechanical Behavior

Comparative Study on Plastic Deformation of Nanocrystalline Al and Ni

Investigation of Grain Boundary Content on Crack Propagation Behavior of Nanocrystalline Al by Molecular Dynamics Simulation

Investigating the thermal stability of nanocrystalline aluminum-lithium alloy by combining different mechanisms: Reinforcing with graphene and alloying with Sr

Milling parameter optimization for refinement of NiO/Al mixtures and synthesis of Ni/Al2O3 nanocomposites

Microstructure evolution of nanostructured Ni3Al during annealing

Structural and thermal properties of the Fe-based alloys prepared by mechanical milling

MECHANICAL BEHAVIOR OF NANOCRYSTALLINE METALS

Research of nanocrystalline Ni-30%Fe solid solution synthesized by mechanical milling

Formation of Nanocrystalline Solid Solution in Al-Fe-V-Si Alloys by Mechanical Alloying

Effect of the Grain Size on the Microtensile Deformation and Fracture Behaviors of a Nickel-Based Superalloy Via EBSD and In-Situ Synchrotron Radiation X-ray Tomography

Superstructure in nano-crystalline Al50Cu28Fe22 alloy

Microstructural Evolution and Multi-Mechanism Strengthening Model of Nanocrystalline Al-Mg Alloys

Structure and mechanical behavior of ultrafine-grained aluminum-iron alloy stabilized by nanoscaled intermetallic particles