Abstract:In this study, a work-of-fracture method using a three-point bend beam （3PBB） specimen, which is commonly used to determine the fracture energy of concrete, was adapted to evaluate the mode-I fracture and durability of fiber-reinforced polymer （FRP） composite-concrete bonded interfaces. Interface fracture properties were evaluated with established data reduction procedures. The proposed test method is primarily for use in evaluating the effects of freeze-thaw （F-T） and wet-dry （W-D） cycles that are the accelerated aging protocols on the mode-I fracture of carbon FRP-concrete bonded interfaces. The results of the mode-I fracture tests of F-T and W-D cycle-conditioned specimens show that both the critical load and fracture energy decrease as the number of cycles increases, and their degradation pattern has a nearly linear relationship with the number of cycles. However, compared with the effect of the F-T cycles, the critical load and fracture energy degrade at a slower rate with W-D cycles, which suggests that F-T cyclic conditioning causes more deterioration of carbon fiber-reinforced polymer （CFRP）-concrete bonded interface. After 50 and 100 conditioning cycles, scaling of concrete was observed in all the specimens subjected to F-T cycles, but not in those subjected to W-D cycles. The examination of interface fracture surfaces along the bonded interfaces with varying numbers of F-T and W-D conditioning cycles shows that （1） cohesive failure of CFRP composites is not observed in all fractured surfaces; （2） for the control specimens that have not been exposed to any conditioning cycles, the majority of interface failure is a result of cohesive fracture of concrete （peeling of concrete from the concrete substrate）, which means that the cracks mostly propagate within the concrete; and （3） as the number of F-T or W-D conditioning cycles increases, adhesive failure along the interface begins to emerge and gradually increases. It is thus concluded that the fracture properties （i.e., the critical load and fracture energy） of the bonded interface are controlled primarily by the concrete cohesive fracture before conditioning and by the adhesive interface fracture after many cycles of F-T or W-D conditioning. As demonstrated in this study, a test method using 3PBB specimens combined with a fictitious crack model and experimental conditioning protocols for durability can be used as an effective qualification method to test new hybrid material interface bonds and to evaluate durability-related effects on the interfaces.

Mode-II Fatigue Fracture of Bi-material Bonded Interfaces Using Tapered ENF Specimens

Mode-Ii Fatigue Fracture of Wood-Composite Bonded Interfaces

Characterization of Mode-II Fracture of Bi-Material Bonded Interfaces Using Tapered ENF Specimen

Analysis of Tapered ENF Specimen and Characterization of Bonded Interface Fracture under Mode-II Loading

Fracture Toughness of Wood—Wood and Wood—FRP Bonded Interfaces under Mode-II Loading

Mixed-Mode Fracture Of Hybrid Material Bonded Interfaces Under Four-Point Bending

Fracture characterization of Carbon fiber-reinforced polymer-concrete bonded interfaces under four-point bending

Nonlinear Fracture Analysis of Delamination Crack Jumps in Laminated Composites

Compliance rate change of tapered double cantilever beam specimen with hybrid interface bonds

Mode I Fracture Toughness of Fiber Reinforced Composite-Wood Bonded Interface

Tapered beam on elastic foundation model for compliance rate change of TDCB specimen

Fiber-Reinforced Composite and Wood Bonded Interfaces: Part 2. Fracture

Mixed Mode Fracture Characterization of GFRP-concrete Bonded Interface Using Four-Point Asymmetric End-Notched Flexure Test

Cohesive Fracture Simulation and Failure Modes of FRP–concrete Bonded Interfaces

Influence Of Span Ratio On The Four-Point Bend End Notched Flexure Test

Experimental and numerical investigation on test methods for mode II fracture of composite‐titanium adhesively bonded structures

A Bi-Linear Cohesive Law-Based Model for Mode II Fracture Analysis: Application to ENF Test for Unidirectional Fibrous Composites

Mode-I Fracture and Durability of FRP-concrete Bonded Interfaces

Evaluation of Fracture Energy of Composite-Concrete Bonded Interfaces Using Three-Point Bend Tests

Characterization of Mode-I fracture of hybrid material interface bonds by contoured DCB specimens

Performance Characterization of Wood-FRP Bonded Interfaces