Abstract:ZrB2-SiC-Zr2Al4C5 multi-phase ceramics with uniform structure and high density were successfully prepared through the introduction of in situ synthesized Zr2Al4C5 into ZrB2-SiC ceramic via SPS at 1800 °C. A systematic analysis and discussion of the experimental results and proposed mechanisms were carried out to demonstrate the composition-dependent sintering properties, mechanical properties and oxidation behavior. The results showed that the in situ synthesized Zr2Al4C5 could be evenly distributed in the ZrB2-SiC ceramic matrix and inhibited the growth of ZrB2 grains, which played a positive role in the sintering densification of the composite ceramics. With increasing Zr2Al4C5 content, the Vickers hardness and Young's modulus of composite ceramics gradually decreased. The fracture toughness showed a trend that first increased and then decreased, and was increased by about 30% compared with ZrB2-SiC ceramics. The major phases resulting from the oxidation of samples were ZrO2, ZrSiO4, aluminosilicate and SiO2 glass. With increasing Zr2Al4C5 content, the oxidative weight showed a trend that first increased then decreased; the composite ceramic with 30 vol.% Zr2Al4C5 showed the smallest oxidative weight gain. We believe that the presence of Zr2Al4C5 results in the formation of Al2O3 during the oxidation process, subsequently resulting in a lowering of the viscosity of the glassy silica scale, which in turn intensifies the oxidation of the composite ceramics. This would also increase oxygen permeation through the scale, adversely affecting the oxidation resistance of the composites with high Zr2Al4C5 content.

Microstructure and Mechanical Properties of SiAlON Ceramics with Porous Structure

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Formation of an α-SiAlON Layer on ß-SiAlON and Its Effect on Mechanical Properties

Microstructure and Mechanical Properties of Porous Alumina Ceramics Fabricated by the Decomposition of Aluminum Hydroxide

Preparation of Self-Coating Al2O3 Bonded SiAlON Porous Ceramics Using Aluminum Dross and Silicon Solid Waste under Ambient Air Atmosphere

Microstructure and Properties of Porous Si3N4/Dense Si3N4 Joints Bonded Using RE-Si-Al-O-N (RE = Y or Yb) Glasses

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

Microstructure and Properties of Porous Si3N4/Dense Si3N4 Joints Bonded Using RE–Si–Al–O–N (RE = Y or Yb) Glasses

Study on Micro-structure and Properties of Al2O3/SiC Ceramics by Pressureless Sintering in Air

Pore Morphology Designs of Porous Si3n4-Based Ceramics Using Si3n4 and Al2o3 Poly-Hollow Microspheres As Pore-Forming Agents

Effect of Al(OH)<sub>3</sub> Addition on the Properties of SiC/Al<sub>2</sub>O<sub>3</sub> Composite Porous Ceramics

Microstructure and mechanical properties of β-SiAION with different Z values

Investigation on Mechanical Properties of AlON Ceramics Synthesized by Spark Plasma Sintering

SiC and ZrN Nano-Particulate Reinforced AlON Composites: Preparation, Mechanical Properties and Toughening Mechanisms

The relation of mechanical properties and resistance erosion-wear of structure ceramic

Preparation, microstructure and ion-irradiation damage behavior of Al4SiC4-added SiC ceramics

Al2O3 Ceramics with Well-Oriented and Hexagonally Ordered Pores: the Formation of Microstructures and the Control of Properties

Optimization of microstructure and mechanical properties of oscillatory pressure sintered ZrO<sub>2</sub>-Al<sub>2</sub>O<sub>3</sub>-SiCp ceramics

Effect of Zr2Al4C5 Content on the Mechanical Properties and Oxidation Behavior of ZrB2-SiC-Zr2Al4C5 Ceramics

Effects of aluminum on micro-sized pore structure of porous MoAlB ceramics fabricated via reactive synthesis

SiAlC ceramics from a new polyaluminocarbosilane: Synthesis, structure and oxidation behaviors