Relationship between Bearing Strength and Damage Progress Behavior of Mechanically Fastened Joints in CFRP Composites.

Yi XIAO,Takashi ISHIKAWA
DOI: https://doi.org/10.6089/jscm.28.56
2002-01-01
Journal of the Japan Society for Composite Materials
Abstract:This paper presents an experimental investigation of the relationship between the bearing strength and the damage progress behavior in mechanically fastened composite structures. CF/ PIXA and CF/Epoxy material systems were selected for the strength comparison, and a simple and highly functional measurement system using a non-contact electro-optical extensometer was adopted to evaluate the bearing strength. A static tensile test for a double lap bolted joint was performed. During tests, the fracture process under the load-deformation response was monitored using the acoustic emission measurement. Some of the specimens were unloaded at different loading levels, in order to assess the damage progress and failure mechanisms using soft X-radiograph and SEM observation of the internal damage. Based on these experimental observations, it can be concluded that the kink band, delamination and fiber-matrix shearing failure formed the major failure modes of the large-scale shear damage. The washer area and bolt clamping conditions should have an influence on the damage progress.
What problem does this paper attempt to address?