Abstract:Chemical complex borohydride is a promising hydrogen storage material due to its large gravimetric and volumetric hydrogen capacities. However, the high dehydrogenation temperature and sluggish kinetics still place strong restrictions on its practical application in the hydrogen storage field. In this work, a synergetic approach of partial cation substitution and catalysis is developed to enhance the hydrogen storage properties of LiBH4. The Li/Mg based dual-cation borohydride (LiMg2(BH4)5, LMBH) was successfully synthesized by wet chemical ball milling of LiBH4 and MgCl2. The optimal (LMBH (4.5:1) sample, LiBH4 and MgCl2 in molar ratios of 4.5:1, possesses a maximum hydrogen desorption capacity (11.27 wt%) and the outstanding initial decomposition temperature (∼250 °C). Importantly, the LMBH (4.5:1) doped with TiF3 shows a remarkable onset dehydrogenation temperature as low as 97.2 °C, which is about 190 °C lower than that of pristine LiBH4. The LMBH (4.5:1) doped with TiF3 system releases 7.98 wt% H2 within 170 min below 350 °C. And the dehydrogenation product of doped composite can reversibly absorb ∼4.72 wt% H2 at a relatively moderate temperature of 280 °C, which is substantially lower than the reversible hydrogen absorption temperature of previous modified borohydride systems. Based on the structural characteristic analyses, the TiF3 reacts with LMBH (4.5:1) to in-situ form actual catalytic components of TiB2 and TiH2 as the actual catalysts for LMBH (4.5:1), resulting in the improved hydrogen re/dehydrogenation properties. The synergetic modification of Li/Mg dual-cation substitution and TiB2/TiH2 catalysis may lead to the development of light-metal borohydrides with outstanding hydrogen storage properties.

Towards Easy Reversible Dehydrogenation of LiBH 4 by Catalyzing Hierarchic Nanostructured CoB

Remarkable irreversible and reversible dehydrogenation of LiBH4 by doping with nanosized cobalt metalloid compounds

Improved dehydrogenation/rehydrogenation performance of LiBH 4 by doping mesoporous Fe 2 O 3 or/and TiF 3

Synergetic Action of 0D/2D/3D N-doped Carbon Nanocages and NbB2 Nanocatalyst on Reversible Hydrogen Storage Performance of Lithium Borohydride

Achieving High Dehydrogenation Kinetics and Reversibility of LiBH4 by Adding Nanoporous H-Bn to Destabilize LiH

Direct Rehydrogenation of LiBH 4 from H-Deficient Li 2 B 12 H 12 − x

Composite Cooperative Enhancement on the Hydrogen Desorption Kinetics of Libh4 by Co-Doping with Nbcl5 and Hexagonal Bn

Direct Rehydrogenation of LiBH4 from H-Deficient Li2B12H12−x

LiBH 4 hydrogen storage system with low dehydrogenation temperature and favorable reversibility promoted by metallocene additives

Significantly Improved De/Rehydrogenation Properties of Lithium Borohydride Modified with Hexagonal Boron Nitride

Diffusion controlled hydrogen desorption reaction for the LiBH4/2LiNH2 system

Enhanced Hydrogen Storage Properties of LiBH4 Modified by NbF5

LiBH4 Hydrogen Storage System with Low Dehydrogenation Temperature and Favorable Reversibility Promoted by Metallocene Additives

In Situ Formation of TiB2 and TiH2 Catalyzed Li/Mg Based Dual-Cation Borohydride with a Low Onset Dehydrogenation Temperature below 100 °C

Enhanced catalytic dehydrogenation of LiBH4 by carbon-supported Pd nanoparticles

Enhanced catalytic hydrogen release of LiBH4 by carbon-supported Pt nanoparticles

Improved reversible dehydrogenation of 2LiBH4-MgH2 composite by the controlled formation of transition metal boride

Mechanistic understanding of CoO-catalyzed hydrogen desorption from a LiBH4·NH3-3LiH system.

Hydrogen Storage Properties of LiBH4–Li3AlH6 Composites

Mechanistic insights into the remarkable catalytic activity of nanosized Co@C composites for hydrogen desorption from the LiBH4–2LiNH2 system

Significant Destabilization Effects of Metal Borides on LiBH4