Enhanced catalytic dehydrogenation of LiBH4 by carbon-supported Pd nanoparticles

Juan Xu,Xuebin Yu,Jun Ni,Zhiqing Zou,Zhilin Li,Hui Yang

DOI: https://doi.org/10.1039/b911197b

IF: 4

2009-01-01

Dalton Transactions

Abstract:The investigation of thermally induced dehydrogenation of LiBH4 catalyzed by carbon-supported Pd nanoparticles (Pd/C) reveals that LiBH4 doped with the Pd/C catalysts shows superior dehydrogenation performance, compared to dehydrogenation in the absence of catalyst, even at very low catalyst content. We have found that smaller Pd nanoparticles result in greater enhanced catalytic dehydrogenation of LiBH4 than do larger Pd nanoparticles. For doping with 10 wt.% catalyst of an average Pd particle diameter of ca. 5.3 nm, thermal dehydrogenation of LiBH4 is found to start at ca. 280 degrees C with a total weight loss of 15.8 wt.% for the full temperature range. With increased loading of catalyst within a LiBH4 sample, the onset dehydrogenation temperature and the two main desorption peaks from LiBH4 are found to decrease while the hydrogen release amount is found to increase. All the hydrogen of ca. 18.5 wt.% can be released from LiBH4 below 580 degrees C at a catalyst doped level of 50 wt.%. Importantly, we observed a reversible hydrogenation/dehydrogenation with a capacity of approximately 4.3 wt.%. Pd nanoparticles are found to play an important role in the catalyzed dehydrogenation/rehydrogenation of LiBH4.