Abstract:For future pollution-free renewable energy production, platinum group metal (PGM)-free electrocatalysts are highly required for oxygen reduction reaction (ORR) to avoid all possible Fenton reactions and to make fuel cell more economical. Therefore, in this study, to overcome traditional electrocatalyst limitations, we applied facile method to synthesize robust mesoporous CrN-reduced graphene oxide (rGO) nanocomposite with MnO (thereafter, Cr/rGO composite with MnO) as an electrocatalyst by efficient one-step sol-gel method by ammonolysis at 900°C for 9 h. Synthesized porous structures of Cr/rGO nanocomposite with MnO have the highest estimated surface area of 379 m2·g−1, higher than that of the carbon black (216 m2·<math>gcat-1</math>) support, and almost uniform pore size distribution of about 4 nm. The Cr/rGO nanocomposites with MnO exhibit enhanced electrocatalytic ORR properties with estimated high half-wave potential of 0.89 V vs. the reversible hydrogen electrode (RHE) and current density of 5.90 mA·cm−2, compared with that of benchmark 20% Pt/C electrode (0.84 V, 5.50 mA·cm−2), with noticeable methanol tolerance and significantly enhanced stability in alkaline media. Hence, the Cr/rGO nanocomposites with MnO showed superior performance to 20 wt.% Pt/C; their half-wave potentials were 50 mV high, and the limiting current density was 0.40 mA·cm−2 high. In alkaline anion exchange membrane fuel cell (AAEMFC) setup, this cell delivers a power density of 309 mW·cm−2 for Cr/rGO nanocomposite with MnO, demonstrating its potential use for energy conversion applications. The nanosized Cr/rGO metallic crystalline nanocomposites with MnO gave a large active surface area owing to the presence of rGO, which also has an effect on the charge distribution and electronic states. Hence, it may be the reason that Cr/rGO nanocomposites with MnO, acting as more active and more stable catalytic materials, boosted the electrocatalytic properties. The synergistic consequence in nanosized Cr/rGO composite with MnO imparts the materials' high electron mobility and thus robust ORR activity in 0.1 M of KOH solution. This potential method is highly efficient for synthesis of large-scale, non-noble-metal-based electrocatalytic (NNME) materials (i.e., Cr/rGO nanocomposite with MnO) on the gram level and is efficient in preparing novel, low-cost, and more stable non-PGM catalysts for fuel cells.

Solvo/Hydrothermal Preparation of MnOx@rGO Nanocomposites for Electrocatalytic Oxygen Reduction

High-Loading Cobalt Oxide Coupled with Nitrogen-Doped Graphene for Oxygen Reduction in Anion-Exchange-Membrane Alkaline Fuel Cells

Hierarchical MnO2/rGO Hybrid Nanosheets As an Efficient Electrocatalyst for the Oxygen Reduction Reaction

Mn Doping of Cobalt Oxynitride Coupled with N-rGO Nanosheets Hybrid As a Highly Efficient Electrocatalyst for Oxygen Reduction and Oxygen Evolution Reaction

Galvanic replacement mediated synthesis of rGO–Mn3O4–Pt nanocomposites for the oxygen reduction reaction

Synthesis and characterizations of SrMnO3 with rGO nanosheets (SMO-rGO) in energy-related applications

Galvanic replacement mediated synthesis of rGO–Mn<sub>3</sub>O<sub>4</sub>–Pt nanocomposites for the oxygen reduction reaction

Highly dispersed MnO nanoparticles supported on N-doped rGO as an efficient oxygen reduction electrocatalyst via high-temperature pyrolysis

Co3O4 Nanoparticles-Modified Α-Mno2 Nanorods Supported on Reduced Graphene Oxide As Cathode Catalyst for Oxygen Reduction Reaction in Alkaline Media

Enhanced Electrocatalytic Activities of MoO3/rGO Nanocomposites for Oxygen Reduction Reaction

Microwave assisted synthesis of Mn3O4 nanograins intercalated into reduced graphene oxide layers as cathode material for alternative clean power generation energy device

Mn and Co Co-Substituted Fe3o4 Nanoparticles on Nitrogen-Doped Reduced Graphene Oxide for Oxygen Electrocatalysis in Alkaline Solution

Novel Two-Dimensional Carbon–Chromium Nitride-Based Composite as an Electrocatalyst for Oxygen Reduction Reaction

Ultrafine Co-doped ZnO Nanoparticles on Reduced Graphene Oxide As an Efficient Electrocatalyst for Oxygen Reduction Reaction

Mno2 Supported Pt Nanoparticels with High Electrocatalytic Activity Foroxygen Reduction Reaction

Efficient Oxygen Reduction Electrocatalysis on Mn3O4 Nanoparticles Decorated N-doped Carbon with Hierarchical Porosity and Abundant Active Sites

CoNx/NiFeOx/nitrogen-doping reduced graphene oxide nanocomposite derived from layered double hydroxide precursor as an efficient bifunctional electrocatalyst for oxygen electrocatalytic reactions

Monodisperse Ultrasmall Manganese-Doped Multimetallic Oxysulfide Nanoparticles as Highly Efficient Oxygen Reduction Electrocatalyst.

A Superior Oxygen Reduction Reaction Electrocatalyst Based on Reduced Graphene Oxide and Iron(II) Phthalocyanine-Supported Sub-2 Nm Platinum Nanoparticles

Visualization of the Electrocatalytic Activity of Three-Dimensional Mose2@Reduced Graphene Oxide Hybrid Nanostructures for Oxygen Reduction Reaction

Strongly Coupled MnO 2 Nanosheets/Silver Nanoparticles Hierarchical Spheres for Efficient Oxygen Reduction Reaction Electrocatalysis