Effect Of Peak Temperature During Friction Stir Welding On Microstructure Evolution Of Aluminum Alloy 1050

katsumi inagaki,s a mironov,yutaka sato,h fujii,hiroyuki kokawa

DOI: https://doi.org/10.1533/978-1-78242-164-1.41

2013-01-01

Abstract:In this work, effect of the peak temperature achieved during friction stir welding (FSW) on microstructure evolution of aluminum alloy 1050 was studied. To this end, FSW at the tool rotational speed between 200 and 2000 rpm was applied, peak temperature in the stir zone (SZ) was recorded, and the evolved microstructure was investigated via electron backscatter diffraction technique. The peak temperature increased from 150 degrees C to 450 degrees C with increasing rotational speed. The mean grain size in the SZ considerably increased from 1 to 10 mu m with increasing temperature. The crystallographic texture was also found to change from < 110 > fiber texture to B/-B texture components with increasing temperature. On the other hand, the microstructural examinations in thermo-mechanically affected zone demonstrated that the microstructural evolution in all cases was dominated by continuous recrystallization. In all cases, the grain structure development was found to go through the following sequence. The original grains were significantly sheared in a flow pattern around the SZ due to geometrical effect of the imposed strain. Simultaneously, low-angle boundaries extensively developed in the grain interiors. Approaching the SZ, they gradually accumulated misorientation, and the fine-grains mainly surrounded by grain boundaries with misorientation exceeding 15 degrees were formed