Abstract:Rare earth elements have excellent catalytic effects on improving hydrogen storage properties of the Mg 2 Ni-based alloys. This study used a small amount of Y to substitute Mg partially in Mg 2 Ni 0.9 Co 0.1 and characterized and discussed the effects of Y on the solidification and de-/hydrogenation behaviors. The Mg 2−x Y x Ni 0.9 Co 0.1 (x = 0, 0.2, 0.3, and 0.4) hydrogen storage alloys were prepared using a metallurgy method. The phase composition of the alloys was studied using X-ray diffraction (XRD). Additionally, their microstructure and chemical composition were studied using scanning electron microscopy and energy-dispersive X-ray spectroscopy, respectively. The hydrogen absorption and desorption properties of the alloys were studied using pressure-composition isotherms and differential scanning calorimetric (DSC) measurements. The structure of the as-cast Mg 2 Ni 0.9 Co 0.1 alloy was composed of the peritectic Mg 2 Ni, eutectic Mg–Mg 2 Ni, and a small amount of pre-precipitated Mg–Ni–Co ternary phases, and was converted into the Mg 2 NiH 4 , Mg 2 Ni 0.9 Co 0.1 H 4 , and MgH 2 phases after hydrogen absorption. Furthermore, the XRD patterns of the alloys showed the MgYNi 4 phase and a trace amount of the Y 2 O 3 phase along with the Mg and Mg 2 Ni phases after the addition of Y. After hydrogen absorption, the phase of the alloys was composed of the Mg 2 NiH 4 , MgH 2 , MgYNi 4 , YH 3 , Y 2 O 3 , and Mg 2 NiH 0.3 phases. With the increase of Y addition, the area ratios of the peritectic Mg 2 Ni matrix phase in the Mg 2−x Y x Ni 0.9 Co 0.1 (x = 0, 0.2, 0.3, and 0.4) alloys gradually decreased until they disappeared. However, the eutectic structure gradually increased, and the microstructures of the alloys were obviously refined. The addition of Y improves the activation performance of the alloys. The alloy only needed one cycle of de-/hydrogenation to complete the activation for x = 0.4. The DSC curves showed that the initial dehydrogenation temperatures of Mg 2 Ni 0.9 Co 0.1 and Mg 1.8 Y 0.2 Ni 0.9 Co 0.1 were 200 and 156 °C, respectively. The desorption activation energies of the hydrides of the Mg 2 Ni 0.9 Co 0.1 and Mg 1.8 Y 0.2 Ni 0.9 Co 0.1 alloys calculated using the Kissinger method were 94.7 and 56.5 kJ/mol, respectively. Moreover, the addition of Y reduced the initial desorption temperature of the alloys and improved their kinetic properties.

Preparation and Hydrogen Storage Kinetics of Nanocrystalline and Amorphous Mg2ni-Type Alloys

Hydriding and dehydriding kinetics of nanocrystalline and amorphous Mg 20Ni 10-xM x (M=Cu, Mn; x = 0-4) alloys prepared by melt spinning

The Electrochemical Hydrogen Storage Characteristics of As-Spun Nanocrystalline and Amorphous Mg20Ni10−xMx (m=cu, Co, Mn; X = 0–4) Alloys

Comparative study of electrochemical performances of the as-melt Mg 20Ni10-xMx (M = None, Cu, Co, Mn; X = 0, 4) alloys applied to Ni/metal hydride (MH) battery

Microstructures and hydrogen storage characteristics of nanocrystal/amorphous Mg17Al12 alloy prepared by ball-milling

An electrochemical investigation of mechanical alloying of MgNi-based hydrogen storage alloys

Microstructures and electrochemical hydrogen storage properties of novel Mg–Al–Ni amorphous composites

Phase Transition and Hydrogen Storage Properties of Melt-Spun Mg3LaNi0.1 Alloy

Microstructure and Hydrogen Storage Characteristics of Nanocrystalline Mg+xwt% LaMg2Ni (x=0–30) Composites

Nanocrystallization and hydriding properties of amorphous melt-spun Mg65Cu25Nd10 alloy

The Electrochemical Evaluation of Ball Milled MgNi-based Hydrogen Storage Alloys

In-situ Precipitation of Ultrafine Mg2Ni Particles in Mg-Ni-Ag Metal Fibers and Their Hydrogen Storage Properties

An Approach for Advancing the Hydrogen Storage Properties Via H-induced Precipitation of Even Nanocatalytsts in Rapid Solidified Mg–Ni–Y Alloy Fibers

Hydrogen-storage properties of amorphous Mg–Ni–Nd alloys

Study on Microstructure and Hydrogen Storage Properties of Mg80Ni16−xAlxY4 (x = 2, 4, 8) Alloys

Catalytic Effect of in Situ Formed Nano-Mg2ni and Mg2Cu on the Hydrogen Storage Properties of Mg-Y Hydride Composites

Microstructure and hydrogen storage properties of the Mg2−xYxNi0.9Co0.1 (x = 0, 0.2, 0.3, and 0.4) alloys

In-situ Formation of Uniform Mg2Ni Catalyst and Hydrogen Storage Properties of Mg41Ni Alloys with Varied Grain Sizes and Morphologies

Electrochemical Performances of the As-Melt La0.75−xMxMg0.25Ni3.2Co0.2Al0.1 (M = Pr, Zr; X = 0, 0.2) Alloys Applied to Ni/metal Hydride (MH) Battery

Hydriding Kinetics of Nano-Phase Composite Hydrogen Storage Alloys Prepared by Mechanical Alloying of Mg and MmNi5−x(CoAlMn)x

Comparison of the electrochemical properties of cast and melt-spun MLNi4.3-xCoxMn0.4Al0.3 (ML: La-rich Mischmetal) hydrogen-storage alloys