Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Self-Assembled Microwires of Aromatic Acids and Melamine

Self-Assembled Microwires Of Terephthalic Acid And Melamine

Triphenylene Nano/Microwires for Sensing Nitroaromatics

Self-Assembled Complex of Melamine and Alloxan

Crystalline Microwires of Rubrene for Chemical Sensing

Coaxially Conductive Organic Wires Through Self-Assembly

Self-assembly of tetra(aniline) nanowires in acidic aqueous media with ultrasonic irradiation

Construction Of Ultralong Nanowires Of A Perylene Bisimide Dye In Acetic Acid

Self-Assembly of a Functional Oligo(Aniline)-Based Amphiphile into Helical Conductive Nanowires

Melamine Driven Supramolecular Self‐assembly of Nucleobase Derivatives in Water

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Freestanding CH 3 NH 3 PbBr 3 single-crystal microwires for optoelectronic applications synthesized with a predefined lattice framework

Synthesis and Self-Assembly of Dendrimer Functionalized Molecular Wires

A Novel Method Self-Assemble Silver Nanowires at Room Temperature

Real time self-assembly and reassembly of molecular nanowires of trigeminal amphiphile porphyrins.

Generation of 2D organic microsheets from protonated melamine derivatives: suppression of the self assembly of a particular dimension by introduction of alkyl chains

Well-shaped poly(dimethylsiloxane)-based copolymer nanowires from spherical micelles via kinetic shape evolution

Complex Self-Assembly of Hyperbranched Polyamidoamine/Linear Polyacrylic Acid in Water and Their Functionalization

Controllable Self-Assemblies of Micro/nano-Tubes and Vesicles from Arylamides and Their Applications As Templates to Fabricate Pt Micro/nano-Tubes and Hollow Pt Nanospheres

Microwave-Assisted Synthesis and In-Situ Self-Assembly of Coaxial Ag/C Nanocables

Controllable Self‐Assembly of N‐type Semiconductors to Microtubes and Highly Conductive Ultralong Microwires