Adsorption and Reduction of Cr(VI) in Aqueous Solution Using Steel Slag Particles

杨慧芬,傅平丰,周枫
DOI: https://doi.org/10.3321/j.issn:1009-606x.2008.03.015
2008-01-01
Abstract:Steel slag particles, the solid waste produced from steelmaking industry, were used to directly remove toxic Cr(VI) in aqueous solution. The physical and chemical properties of steel slag particles were analyzed, and the process and mechanism of direct adsorption and reduction removal of Cr(VI) were studied in detail. The results showed that after 10 min stirring with grinded steel slag particles, the concentration of Cr(VI) was reduced from 200 to 0.5 mg/L, and reached national waste water discharge limits (GB8978-1996). The adsorption of Cr(VI) with steel slag particles followed the Langmuir isothermal adsorption with saturated adsorptive capacity of 6.878 mg/g. Chemical composition and XPS analysis showed that the adsorption of Cr(VI) using steel slag particles had two functions of adsorption and reduction. After adsorbing Cr(VI), the content of Cr(III) in steel slag particles increased from 0.0985% to 0.39%, and the content of FeO decreased from 9.20% to 8.35%. The Cr(OH)3 had covered on the steel slag particles surface adsorbed. The results revealed that the adsorbed Cr(VI) was reduced by reductive FeO to Cr3+ ion which was further deposited as Cr(OH)3 with lower toxicity. The Cr(OH)3 precipitation fixed on steel slag can be rapidly separated from water as steel slag particles deposit.
What problem does this paper attempt to address?