Adsorption-desorption Characteristics of Steel Slag for Ferrous and Sulfur Ions
Xie Xiaomei,Liao Min,Hua Jiayuan,Chen Na,Zhang Nan,Xu Peizhi,Xie Kaizhi,Xu Changxu,Liu Guangrong
DOI: https://doi.org/10.3785/j.issn.1008-9209.2014.05.131
2015-01-01
Abstract:Summary Ferrous ion (Fe2+ ) and reduced sulfur ion (S2 -) were main toxic elements in the cold waterlogged paddy soil . How to remove Fe2+ and S2 - effectively was the key to improve the quality of cold waterlogged paddy soil . Steel slag has been confirmed as a good sorption material in waste water treatments for some heavy metals and organic pollutants . These properties suggested that steel slag might have the ability to adsorb and fix Fe2+ and S2 - from cold waterlogged paddy soil , and improve the quality of cold waterlogged paddy soil by reducing Fe2+ and S2- . The characteristics of Fe2+ and S2 - adsorption‐desorption by steel slag were studied in the present study , to reveal whether steel slag was a good sorption material for Fe2+ and S2 - , and to understand whether steel slag had the potentiality in controlling Fe2+ and S2 - and improving the quality of cold waterlogged paddy soil . The sorption of Fe2+ and S2 - by steel slag was studied using batch incubation experiments , while the effects of adsorption time (0 .25 ,0 .5 ,1 ,1 .5 ,2 ,3 or 4 h ,respectively) ,Fe2+ and S2 - concentration (10 ,30 ,50 ,100 , 150 mg/L Fe2+or 10 , 30 , 50 , 80 , 100 mg/L S2 - , respectively) , pH ( the pH range of adsorption system was from 1.00to12.00),temperature(designedas15,25,35or45 ℃ ,respectively)andionicstrength(0.01mol/LNaCl, 0 .02 mol/L NaCl or 0 .005 mol/L MgCl2 , respectively) in adsorption reaction solution on the sorption were investigated . Except for adsorption time experiments , all treatments were shook 3 h and stood for one night for complete adsorption reaction . Then , the adsorption reaction solution was centrifuged at 4 000 r/min for 10 min and filtrated for further determination of Fe2+ and S2 -concentrations . The stability of Fe2+ and S2 -adsorbed by steel slag was further validated by desorption experiments under similar conditions . The results showed that the adsorption kinetics of Fe2+ and S2 - by steel slag followed the Elovich kinetics equation , and the correlation coefficients were 0 .94 and 0 .89 respectively . Freundlich isotherm model could simulate the adsorption processes better than other models , and the correlation coefficients for Freundlich isotherm model were 0 .97 and 0 .94 respectively . Their parameters were all less than 1 , which indicated that the adsorption processes were non‐preferential adsorption . Free energy variation (ΔG) for the Fe2+ sorption was greater than 0 , which indicated that this reaction was non‐spontaneous; but ΔG for the S2 - sorption was less than 0 , which indicated that this reaction was spontaneous . The adsorption process was endothermic because high temperature was beneficial to their adsorption . And the adsorption process had greater pH adaptability range from 1 .50 to 11 .50 . The adsorption of Fe2+ was major in inner sphere complexation , while the adsorption of S2 - was major in outer complexation , which were consistent with the results in thermodynamic experiments . The adsorption rates were all very high , but the desorption rates were low in all experimental conditions , which showed that the adsorption stability of steel slag was superior . On the whole , steel slag had good ability to remove Fe2+ and S2 - , might be a potential adsorbent in controlling Fe2+ and S2 - and improving the quality of cold waterlogged paddy soil .