Abstract:The study is aimed to analyze the macro- and microstructural changes of homogenized cast alloy 625 during uniaxial hot compression testing at various strain rates (<math>ε˙=</math>0.01–10s−1) in a temperature range of 1050–1200 °C. A Gleeble-3800 simulator was used for conducting the tests. The peak stress analysis shows that the average activation energy of 520 kJ is required to accelerate dynamic softening over hardening in the studied alloy, where recrystallization is the rate defining process. The flow stress behavior of the alloy is studied using a physical model, and further finite element method is used as a tool to map the strain distribution. At intermediate <math>ε˙</math>, especially at 1s−1, an unusual flow saturation is observed without revealing any peak stress. The macrographs of these samples indicate that the applied plastic strain is localized in small regions that are occupied with fine recrystallized grains, thereby leaving large undeformed zones. Detailed characterization of the simulated samples by SEM, EBSD and TEM indicate that at intermediate strain rates of 0.1 and 1s−1, the recrystallization rate is controlled by the formation of ∑3 twins at the interface of migrating high angle boundaries. The generation of recrystallization twins continuously changes the direction and velocity of a moving boundary by forming a new dynamically recrystallized grain. It is also observed that several recrystallization fronts are created due to the presence of carbide particles in the starting material through particle stimulated nucleation. The formation of the δ-phase by incipient melting/dissolution of carbide particles is observed for the sample deformed at 1200 °C with 10s−1. The results were discussed in terms of different softening mechanisms, such as dynamic recovery and recrystallization during the hot deformation of the studied alloy 625.

Correction of Flow Stress for Hot Compression of Inco718 Alloy

Hot compression deformation behavior and processing maps of ATI 718Plus superalloy

Correction of flow stress data due to non-homogeneous deformation and thermal conditions during hot compression testing of a polycrystalline nickel-base superalloy

Correction and Modeling of Flow Stress during Hot Deformation of 7055 Aluminum Alloy

Hot Deformation Behavior and Constitutive Modeling of Alloy 800h Considering Effects of Strain

Hot Deformation Behavior of Homogenized Al-7.8Zn-1.65Mg-2.0Cu (wt.%) Alloy

Friction correction of flow stress-strain curve in the upsetting process

Hot Working Property Study of 7055 Aluminum Alloy Based on Hot Shear-Compression Deformation

Flow Behavior and Microstructures of Superalloy 718 During High Temperature Deformation

Hot deformation behavior of a Fe-Cr-Ni alloy and the correction of constitutive model

Flow stress and dynamic recrystallization behavior and modeling of GH4738 superalloy during hot compression

Study of Hot Deformation Behavior of 6082 Aluminum Alloy

Hot Deformation Behavior and a Two-Stage Constitutive Model of 20mn5 Solid Steel Ingot During Hot Compression.

Microstructure Evolution and Flow Stress Model of a 20mn5 Hollow Steel Ingot During Hot Compression

Accurate Flow Characterization of A6082 for Precision Simulation of a Hot Metal Forming Process

Flow stress characteristics and microstructural evolution of cast superalloy 625 during hot deformation

Investigation on hot deformation behavior of 2050 Al-Cu-Li alloy

Investigation of hot deformation behavior and microstructure evolution of TC18 alloy and establishment of constitutive equation under friction-temperature correction

Strain Compensation of the Constitutive Equation for High Temperature Flow Stress of a Al-Cu-Li Alloy

Constitutive model for hot deformation of aluminum alloy

Modified constitutive model and workability of 7055 aluminium alloy in hot plastic compression