Synthesis of Hydrophilic Ge-ZSM-5 Zeolite Membranes onα-Al2 O3 Support Modified by γ-Al2 O3 Film

Shaohui ZHENG,Zhongxiang BAI,Xiaodong WANG,Wei HUANG

DOI: https://doi.org/10.16355/j.cnki.issn1007-9432tyut.2015.05.009

2015-01-01

Abstract:Hydrophilic Ge‐ZSM‐5 zeolite membranes were synthesized on α‐Al2 O3 support modified by γ‐Al2 O3 film by in situ hydrothermal synthesis method .The effect of template a‐mount and crystallization temperature on the microstructure of membranes was investigated .The results show that when the template amount was low (n(TPAOH)/n(SiO2 )=0.03) ,the zeolite membrane was not dense;however , when the amount of template was further increased (n(TPAOH)/n(SiO2 )=0.04 ,0.05) ,the film became dense and continuous .Moreover ,when the crystallization temperature was 160 ℃ ,zeolite membranes were discontinuous ;when the crystallization temperature reached 170 ℃ or 180 ℃ ,continuous and dense zeolite membranes were obtained .When the gel composition molar ratio was n(GeO2 )∶ n(SiO2 )∶ n(TPAOH)∶n(H2 O)=0 .195∶19 .5∶0 .780∶438 and its amount was 19 mL ,crystallization temperature and time was 180 ℃ and 24 h respectively ,continuous and dense Ge‐ZSM‐5 zeolite membrane with the thickness of 34 μm was obtained .When it was used to separate 95% ethanol aqueous solution at 70 ℃ by pervaporation ,the flux was 0.976 kg/(m2 · h) with a separation factor of 64.7 .