Abstract:In this work, single-phase Te-doped CoSb 3 polycrystalline bulk (Indium powder) and nanocomposites (α-WC nanopowder) were synthesized via a ball milling, hand-grinding and consolidated by spark plasma sintering technique. The thermoelectric and mechanical characteristics of as-synthesized composites were studied. The electrical resistivity varies between 11.82 and 12.82 μΩ-m for CoSb 2.875 Te 0.125 + x ( x = 0.33% In, 1% In, 2% In, 4% In and 1% In + 0.33% α-WC, respectively) composites. At temperature of 300 K, composite with x = 1% In exhibit the lowest resistivity of 11.82 μΩ-m. Also, negative values of Seebeck coefficients confirm that electrons are the predominant charge carriers. The maximum power factor of 2566 and 2482 μWm −1 K −2 are observed from x = 1% In and x = 1% In + 0.33% α-WC composites at 673 K, respectively. Notably, the power factor of 1% In and 1% In + 0.33% α-WC composites is slightly higher (1.05 times) than the CoSb 2.875 Te 0.125 sample. The composites with lowest weight percent of 1% In and 1% In + 0.33% α-WC have a considerably improved power factor. For the composite with x = 1% In + 0.33% α-WC, the minimum thermal conductivity of 2.32 W/m–K at 300 K was achieved through a combination of doping and dispersion in the CoSb 2.875 Te 0.125 matrix. It is possible that the multi-scale size distributions of grains will reduce the lattice thermal conductivity by scattering phonons over a large wavelength range. As a result, an increased figure of merit of 0.82 was achieved for CoSb 2.875 Te 0.125 + 1% In + 0.33% α-WC composites at 823 K. The results suggest that the doping with composite approach could boost thermoelectric efficiency in n-type CoSb 3 -based materials.

Improved thermoelectric performance of Te-doped and CNT dispersed CoSb3 skutterudite bulk materials via HTHP

Beneficial Effect of High Pressure and Double-Atom-doped Skutterudite Compounds Co4Sb11.5−xTe0.5Snx by HPHT

Enhanced Thermoelectric Performance of Skutterudites Via Orthogonal Experimental Design

HPHT synthesis and enhanced thermoelectric transport properties of double-doped Co4Sb11TexSn1-x skutterudites

Thermoelectric properties of (Cu,Te) co-doped CoSb 3 synthesized by high-pressure and high-temperature

High-Pressure Synthesis of Te-Ge Double-Substituted Skutterudite with Enhanced Thermoelectric Properties

Enhanced High-Temperature Thermoelectric Performance in Te-Doped Electronegative Element-Filled Skutterudites via Suppressing Bipolar Effects and Enhanced Phonon Scattering

The Thermoelectric Properties of Co4Sb12-xTex Synthesized at Different Pressure

Effect of HPHT processing on the structure, and thermoelectric properties of Co4Sb12 co-doped with Te and Sn

The enhanced thermoelectric properties of Ba0.25Pb0.05Co4Sb11.5Te0.5 alloys prepared by HPHT at different pressure

Impacts of Both High Pressure and Te–Se Double-Substituted Skutterudite on the Thermoelectric Properties Prepared by HTHP

Enhanced Thermoelectric Performance in GaxCo4Sb12.3-yTey Skutterudites Via Suppressing Bipolar Effects for Commercial Application

Synthesis Optimization and Thermoelectric Properties of S-Filled and Te-Se Double-Substituted Skutterudite under High Pressure

Enhanced Thermoelectric Performance in Ternary Skutterudite Co(Ge 0.5 Te 0.5 ) 3 via Band Engineering

Enhanced Thermoelectric Transport Properties of Electronegative-Element-Filled and (Ni, Te) Co-Doped Skutterudites through S Filling

Thermoelectric Properties of Ni0.15Co3.85Sb12 and Fe0.2Ni0.15Co3.65Sb12 Skutterudites Prepared by HPHT Method

Significant enhancement of electrical conductivity by incorporating carbon fiber into CoSb3 thermoelectric skutterudite fabricated by spark plasma sintering method

Thermoelelctric Properties of Nanostructured Skutterudite-Related Compounds

Effects of double filling of Pb and Ba on thermoelectric properties of Pb xBa yCo 4Sb 11.5Te 0.5 compounds by HPHT

Possible reduction of lattice thermal conductivity in n-type CoSb2.875Te0.125 skutterudite originating from collaborative adjustment between Indium micro and α-WC nano inclusions

Nanostructuring and Thermoelectric Properties of Bulk Skutterudite Compound Cosb3