Abstract:Using the Raney Fe-Al alloy as the precursor for Fe and Al, and tetrapropylammonium hydroxide (TPAOH) as both the base for the leaching of the alloy and the template for the synthesis of HZSM-5, we synthesized the skeletal Fe core-HZSM-5 shell catalysts (Raney Fe@HZSM-5) via a facile one-pot hydrothermal strategy. The thickness of the zeolite shell was adjusted by varying the hydrothermal time. The catalysts were characterized by inductively coupled plasma-atomic emission spectroscopy (ICP-AES), N-2 physisorption, X-ray powder diffraction (XRD), temperature-programmed desorption of NH3 (NH3-TPD), and scanning electron microscopy (SEM). It was identified that the Raney Fe-Al alloy was more suitable than the rapidly quenched Fe-Al alloy as the precursor to the skeletal Fe core, since the skeletal Fe catalyst alkali-leached from the former produced more long-chain hydrocarbons during the Fischer-Tropsch synthesis (FTS) reaction for successive cracking and isomerization. A complete HZSM-5 shell was obtained only after above 24 h of hydrothermal treatment. With the hydrothermal time from 2 d to 8 d, the thickness of the compact HZSM-5 shell increased from 1.3 mu m to 9.7 mu m, the relative crystallinity increased steadily, while the SiO2/Al2O3 ratio remained essentially constant, and the amount of the acid sites is parallel to the thickness of the zeolite shell. In the FTS reaction using syngas with the H-2/CO molar ratio of 2 and at 543 and 2.0 MPa, the CO conversion and the selectivity to the gasoline fraction (C-5 similar to C-11 hydrocarbons) evolved in a volcanic trend with the shell thickness, suggesting the existence of an optimal amount of the acid sites, while less or more is adverse to the activity and selectivity to the gasoline fraction. The Raney Fe@HZSM-5 catalyst hydrothermally treated for 4 d exhibited the highest CO conversion of 92% and the selectivity to the gasoline fraction of 71%, along with an iso-paraffin to n-paraffin ratio of 1.9. At the n(H-2)/n(CO) ratio of 1, the selectivity to the gasoline fraction and the iso-paraffin to n-paraffin ratio were further improved to 73% and 2.1, respectively, which shows promise for this catalyst to transform the coal- or biomass-derived syngas to high-octane number gasoline.

Carbon/H-ZSM-5 Composites As Supports for Bi-Functional Fischer–Tropsch Synthesis Catalysts

Co-Based Catalysts Supported on Silica and Carbon Materials: Effect of Support Property on Cobalt Species and Fischer–Tropsch Synthesis Performance

Gasoline-Range Hydrocarbon Synthesis over Cobalt-Based Fischer–Tropsch Catalysts Supported on SiO2/HZSM-5

Hierarchical ZSM-5 Supported CoMn Catalyst for the Production of Middle Distillate from Syngas

Enhanced Fischer-Tropsch synthesis performance on fe + ZSM5 bifunctional catalysts

A Highly Selective Raney Fe@HZSM-5 Fischer–Tropsch Synthesis Catalyst for Gasoline Production: One-Pot Synthesis and Unexpected Effect of Zeolites

The effects of promoters of K and Zr on the mesoporous carbon supported cobalt catalysts for Fischer-Tropsch synthesis.

Effect of pretreatment atmosphere on the activity and selectivity of Co/mesoHZSM-5 for Fischer–Tropsch synthesis

The influence of hierarchical zeolite composition and pore structure on behavior of cobalt-based Fischer–Tropsch synthesis catalysts

ZSM‐5‐Promoted Co‐Based Light‐Assisted Thermocatalytic Fischer–Tropsch Synthesis Catalyst for Production of Liquid Fuel

Co-Ru/γ-Al2O3 catalyst modified with ZrO 2 for Fischer-Tropsch synthesis

Effect of Shell Thickness on Skeletal Fe@HZSM-5 Core-Shell Catalysts for Fischer-Tropsch Synthesis

Boosting liquid hydrocarbons selectivity from CO2 hydrogenation by facilely tailoring surface acid properties of zeolite via a modified Fischer-Tropsch synthesis

Synthesis of mesoporous molecular sieves and their application as supports for catalysts in F-T synthesis

Highly dispersed Co-based Fischer–Tropsch synthesis catalysts from metal–organic frameworks

Bifunctional CoFe/HZSM-5 Catalysts Orient CO2 Hydrogenation to Liquid Hydrocarbons

Fischer-Tropsch Synthesis over Skeletal Co@HZSM-5 Core-Shell Catalysts

Enhancing the Stability of a Cobalt-Based Fischer–Tropsch Synthesis Catalyst Using G-C3n4-coated SBA-15 As Support

Catalyst design for maximizing C5+ yields during Fischer-Tropsch synthesis

Uniformity Dispersive, Anti-Coking Core@double-Shell-structured Co@SiO2@C: Effect of Graphitic Carbon Modified Interior Pore-Walls on C5+ Selectivity in Fischer-Tropsch Synthesis

Fabrication of AC@ZSM‐5 Core‐shell Particles and Their Performance in Fischer–Tropsch Synthesis