Corrosion performance of laser welding on dissimilar materials Hastelloy C-276/316L

Dong-jiang WU,Cong FAN,Shi-bo LIU,Guang-yi MA,Dong-ming GUO

2014-01-01

The Chinese Journal of Nonferrous Metals

Abstract:By using continuous laser to weld Hastelloy C-276 and 316L and method of electrochemical corrosion, the corrosion resistances of the weld and base material in acid, neutral and alkaline solution were studied, continuously. The corrosion morphology and the composition of the corrosion surface were analyzed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The results show that, in the acidic environment, the sequence of corrosion resistance from high to low are C-276, weld, 316L. In the neutral environment, there is little difference between corrosion resistance of the weld and base materials. In the alkaline environment, the corrosion tendency of 316L is the largest, corrosion tendency of the weld follows, the corrosion tendency of C-276 is the minimum. While the corrosion speed of weld and 316L has no obvious difference, and both of them are obviously less than C-276. In the acidic and neutral solution,the intergranular corrosion is found in the weld. The mass fraction of Mo in the intergranular is about 4%larger than that in the grain. This shows that the segregation of Mo element has a great influence on intergranular corrosion. In the alkaline solution, pitting corrosion is found in the weld and it is associated with lattice defects.