Abstract:Journal of Composite Materials, Ahead of Print. Laminates are produced by stacking prefabricated plies composed of fiber products. Within the aerospace industry, a ply thickness of 125 μm is commonly regarded as the standard. Ply thicknesses of less than 100 μm are generally considered as thin plies. Due to their ability to provide superior mechanical properties relative to conventional laminates thin-ply (TP) laminates are gaining interest in several high-tech industries. Although the research on TP laminates increased over the past few years, a comprehensive evaluation of the mechanical behavior of TP laminates accounting for the ply-thickness is an ongoing challenge due to the intricacies of ply interactions, and experimental difficulties. The mechanical response of fiber reinforced polymer laminates is governed by damage progression during loading, with the thickness of individual plies playing a crucial role in influencing the initiation and evolution of local cracks and failures. Therefore, in this study, the effective mechanical properties of carbon fiber reinforced polymer composite with varied ply thicknesses have been experimentally evaluated and the accumulation of the damage events has been monitored using acoustic emission measurements, utilizing a contactless laser vibrometer. In this experimental study, the ply thickness is increased in a systematic manner (ranging from 50 μm to 200 μm). Experimental investigation has been carried out in quasi-static tension and compression. The results show that unnotched TP laminates subjected to tensile loading demonstrate enhanced effective strength, attributed to less premature failure. Conversely, as the thickness of the lamina increases, there is a reduction in the overall strength of the laminate. However, in the case of the notched specimen lowest strength has been observed at a ply-thickness of 100 μm in this study. Under compressive loading, unnotched and notched specimen tends to show similar mechanical behavior to unnotched specimens under tensile loading. The overall strength is raised with decreasing ply thickness. The findings from this study may be valuable for incorporating ply-thickness considerations into models for predicting the mechanical performance of laminates under dynamic loading.

Non-Destructive Characterization of Laminated Composite Films by Laser Ultrasonic Technique

Investigation on the Compressive Mechanical Properties of Ultra-Thick CFRP Laminates

A Novel Laser Ultrasonic Thickness Measurement Method for Metal Plate Based on Spectral Analysis

Delamination Analysis of Carbon Fiber/Epoxy Composite Laminates under Different Loading Rates Using Acoustic Emission

Nondestructive characterization of mechanical properties on metallic and polymer plates using hybrid laser-air coupled ultrasonic techniques

The synthesis and mechanical property evaluation of Ni/Ni3Al microlaminates

Nonlinear Fracture Analysis of Delamination Crack Jumps in Laminated Composites

Uniaxial Tension Deformation Study of Copper/nickel Laminated Composites: Effects of Lamella Number and Interlamellar Spacing

Ultrasonic evaluation of ply and interleaf layer properties of interleaved composite laminates

Investigation on damage behaviors of carbon fiber‐reinforced nylon 6 thermoplastic composite laminates using acoustic emission and digital image correlation techniques

Simultaneous determination of Young's modulus and Poisson's ratio in metals from a single surface using laser-generated Rayleigh and leaky surface acoustic waves

Microstructures and Mechanical Properties of Laminated Structural Nb-Ti-Al Composites Fabricated by Laser Deposition

Quantitative Evaluation of Interlaminar-Toughened CFRP Composite by Ultrasonic Wave Propagation Characteristics

Fractography, Elastic Modulus, and Oxidation Resistance of Novel Metal-Intermetallic Ni/Ni3al Multilayer Films

Characterizations of Elastic Constants of Transparent Thin Films Deposited on Substrates by Laser Ultrasonic Method

Study on Porosity and Material Parameters of Hot Moulded Resin Matrix Composites using Nondestructive Laser Ultrasound Technique

Lamb wave dispersion and anisotropy profiling of composite plates via non-contact air-coupled and laser ultrasound

Through-the-thickness investigation of grain structure and microhardness of Ni-based and Mg-based laminated composites for structural applications

Evaluating the mechanical behavior of carbon composites with varied ply-thicknesses using acoustic emission measurements

Experimental failure analysis and mechanical performance evaluation of fiber-metal sandwich laminates interleaved with polyamide-6,6 interlayers through the combined usage of acoustic emission, thermography and microscopy techniques

A Study on the Intralaminar Damage and Interlaminar Delamination of Carbon Fiber Composite Laminates under Three-Point Bending Using Acoustic Emission