Abstract:Hydrothermally synthesized TiO2 nanotubes (TNTs) with a diameter of approximately 10 nm and a length of 250 nm are successfully employed in dye-sensitized solar cells (DSSCs) based on N719 dye and iodide/triiodide electrolyte and exhibiting an efficiency of 7.6% at 1 sun illumination. Randomly oriented TiO2 nanotubes are deposited on FTO glass by the electrophoretic deposition method, and the thickness of the TNT layer and hence the solar cell performance have been shown to depend on the deposition time and the nanotube concentration in the electrolyte solution. The highest efficiency is obtained for the solar cell fabricated with the 6-minute electrophoretically deposited TiO2 film having a film thickness of 6 μm. These pristine TNT photoelectrodes exhibit a short-circuit current density (Jsc), an open-circuit voltage (Voc), a fill factor (FF) and an efficiency (η) of 2.4 mA cm−2, 899 mV, 78% and 1.7%, respectively. TiCl4 treatment of pristine TNT photoelectrodes enhances the Jsc, Voc, FF and η to 13.2 mA cm−2, 819 mV, 70.4% and 7.6%, respectively. The TiCl4 treatment is found to be vital for the enhancement of the solar cell performance of hydrothermally synthesised TiO2 nanotube based devices. Enhancement of electron lifetime is noted after treatment of bare TiO2 nanotubes with 0.5 M TiCl4 solution. The electron transport resistance, electron lifetime and charge recombination properties of bare and TiCl4 treated TiO2 nanotubes are investigated by electrochemical impedance measurements. The increased performance of the DSSC fabricated with TiCl4 treated TNTs is due to several factors favouring the enhancement of efficiency. These include the dye loading amount, the decrease in electron transport resistance, the increase in density of states and enhancement of light scattering.

Novel Fabrication of TiO2/ZnO Nanotube Array Heterojunction for Dye-Sensitized Solar Cells

CdS/ZnS Co-Sensitized Hierarchical TiO2Nanotree Array with Rutile/Anatase Junctions for Enhanced Photoelectrochemical Performance

Functions of Self-Assembled Ultrafine TiO2 Nanocrystals for High Efficient Dye-Sensitized Solar Cells

Nanotube Film for Quantum Dots Sensitized Solar Cells

ZnO nanotube-based dye-sensitized solar cell and its application in self-powered devices.

Hybrid TiO2–SnO2 Nanotube Arrays for Dye-Sensitized Solar Cells

Large-scale, noncurling, and free-standing crystallized TiO2 nanotube arrays for dye-sensitized solar cells

Open-circuit voltage improvement by using TiO2 nanotubes as a working electrode of dye-sensitized solar cell

Hydrothermally synthesized titania nanotubes as a promising electron transport medium in dye sensitized solar cells exhibiting a record efficiency of 7.6% for 1-D based devices

Titanium Dioxide/zinc Indium Sulfide Hetero-Junction: an Efficient Photoanode for the Dye-Sensitized Solar Cell

A cylindrical core-shell-like TiO2 nanotube array anode for flexible fiber-type dye-sensitized solar cells.

Translucent TiO2 Nanotube Film for Quantum Dots Sensitized Solar Cells

Ordered TiO2 Nanotube Arrays on Transparent Conductive Oxide for Dye-Sensitized Solar Cells

High-efficiency dye-sensitized solar cells based on robust and both-end-open TiO2 nanotube membranes

Low Temperature Transfer of Well-Tailored TiO2 Nanotube Array Membrane for Efficient Plastic Dye-Sensitized Solar Cells

Fabrication of Highly-Oriented TiO2 Nanotube Arrays and Its Application in Dye-Sensitized Solar Cells

The Preparation of TiO2 Nanotube by ZnO Nanorod Template Method and Application in Dye-Sensitized Solar Cells

Photoelectric Performance Optimization of Dye-Sensitized Solar Cells Based on ZnO-TiO2 Composite Nanofibers

ZnO/TiO2 Composite Photoanodes for Efficient Dye-Sensitized Solar Cells

Highly Functional TNTs with Superb Photocatalytic, Optical, and Electronic Performance Achieving Record PV Efficiency of 10.1% for 1D-Based DSSCs

Anodic Ag/TiO2 nanotube array formation in NaOH/fluoride/ethylene glycol electrolyte as a photoanode for dye-sensitized solar cells