Enhanced Visible-Light Absorption and Photocurrent Generation of Three-Dimensional Metal–Dielectric Hybrid-Structured Films
Zhenlei Wang,Liwen Lai,Tianfu Zhang,Sanming Wu,Jie Zhao,Yuxin Zhao,Yuanhao Jin,Jiaping Wang,Shoushan Fan,Qunqing Li
DOI: https://doi.org/10.1021/acsaem.1c01485
IF: 6.4
2021-10-13
ACS Applied Energy Materials
Abstract:The two-dimensional planar metal–semiconductor–metal sandwich structure can achieve single-band or multiband absorption. This sandwich structure is mostly affected by the thickness of the middle dielectric and the size of the top metal nanoparticles (NPs), which makes the absorption of the planar sandwich structure sensitive to the angle of the incident light. Here, three-dimensional (3D) metal–dielectric hybrid-structured films based on titanium dioxide (TiO2) and gold (Au) were designed and fabricated, which consist of three parts: an uneven Au film based on a porous substrate, a 50 nm TiO2 film, and top random Au nanoparticles. The 3D Au/TiO2–Au NP film exhibited a strong absorption and weak angle dependence in the visible-light range of 400–850 nm. The photocurrent density of the 3D Au/TiO2–Au NP film photoanode increased to 15.8 μA cm–2 at a potential of 1.23 V versus the reversible hydrogen potential under the irradiation of visible light (λ > 420 nm), resulting in an enhancement factor of ∼32 compared with the bare TiO2 photoanode (0.5 μA cm–2). This 3D metal–dielectric hybrid-structured film and its preparation strategy may have potential application value in photocatalysis, photoelectric conversion, and other solar absorption systems.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c01485.Additional experimental details and methods, including photographs of experimental results, SEM image and magnified SEM image of the silicon substrate, low-magnification and high-magnification SEM images showing the top view of the 3D film structure on a silicon substrate and quartz substrate, size distribution of Au NPs of the film structure, AFM images of 2D and 3D film structures, high-resolution XPS spectra of Au 4f of the TiO2–Au NP film and 3D film structure, transmittance spectrum and reflectance spectrum, experimentally measured absorption spectra of the bare 2D/3D Au film and the 2D and 3D Au/TiO2 film structures, peak intensity of peaks a and b of the optimized 2D film and 3D film structure as a function of the incident angle, variation of absorption spectra of optimized 2D and 3D film structure with different incident angles, chopped I–V curves under irradiation of UV cut-off solar light, (Table S1) PEC performance of different types of photocatalysts under simulated sunlight, I–t stability test results at 1.23 V (vs RHE), I–t plots of 2D and 3D film photoanodes under irradiation of UV cut-off solar light (with only >420 nm), spatial distribution of electric field on x–z plane, and Raman spectra of various film structures (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels