Insight into the Formation of A Continuous Sheath Structure for the Ps Phase in Tri-Continuous Pvdf/Ps/Hdpe Blends

Rui Dou,Shuanglin Li,Yan Shao,Bo Yin,Mingbo Yang

DOI: https://doi.org/10.1039/c5ra22555h

IF: 4.036

2016-01-01

RSC Advances

Abstract:A hierarchical tri-continuous structure is formed and controlled in PVDF/PS/HDPE ternary blends. A very high level of PS continuity, about 80%, is achieved only with a PS volume composition as low as 11 vol%.

What problem does this paper attempt to address?

Co-Continuous Polymeric Nanostructures Via Simple Melt Mixing of Ps/Pmma

Gongwei Pu,Yingwu Luo,Qianchuan Lou,Bogeng Li

DOI: https://doi.org/10.1002/marc.200800579

IF: 5.006

2008-01-01

Macromolecular Rapid Communications

Abstract:Blends of polystyrene/poly(methyl methacrylate) (PS/PMMA) (30/70) prepared by simple melt mixing form a droplet (PS) in-matrix (PMMA) morphology. It is found that addition of a carefully designed copolymer PS-b-P(S-ran-MMA) (SSM) compatibilizer could convert the morphology into a co-continuous system. Indeed, the continuity of the dispersed PS phase increased with an increase in PS-b-P(S-ran-MMA) content, and a fully co-continuous morphology (continuity = 100%) was obtained at 20% SSM fraction with a characteristic size of 100 nm.
Tuning polymer blends to cocontinuous morphology by asymmetric diblock copolymers as the surfactants

Gongwei Pu,Yingwu Luo,Anni Wang,Bogeng Li

DOI: https://doi.org/10.1021/ma1026719

IF: 5.5

2011-01-01

Macromolecules

Abstract:We investigated the influence of the chain asymmetry of the styrene (S)-methyl methacrylate (MMA) copolymer (surfactant) on the morphology of the polystyrene (PS)/poly(methyl methacrylate) (PMMA) blends. It was, for the first time, demonstrated that the chain asymmetry of the block copolymer surfactant would have significant influence on the structure of the polymer blend in the melt mixing process. In the PS/PMMA = 30/70 blends, the addition of asymmetric AB diblock copolymers tuned the morphology from the droplet-in-matrix structure to the cocontinuous structure. At 20 wt % asymmetric AB block copolymer (PMMA(110)-block-PS430) dosage, the onset of the cocontinuous interval of the PS/PMMA blends was lowered to PS/PMMA = 20/80 and the cocontinuous interval was broadened to PS/PMMA = 20/80-30/70, compared with the onset at PS/PMMA = 45/55 and the interval at PS/PMMA = 45/55-50/50 of the PS/PMMA blends without the copolymers. The reason was that the packing of the asymmetric block copolymer on the interface provided the bending energy being against the interfacial energy when the longer block of the copolymer was in the minor phase side, suppressing the breakup of the minor phase fibers during melt mixing. With the addition of 20 wt % AC block copolymer (P(S-ran-MMA)(220)-block-PS320), which was more asymmetric than the AB block copolymer (PMMA(110)-block-PS430) of the same molecular weight and monomer composition, the PS/PMMA blends showed an even wider cocontinuous interval at PS/PMMA = 10/90-30/70.
Preparation of Porous PVDF Membrane Via Thermally Induced Phase Separation with Diluent Mixture of DBP and DEHP

Gen-Liang Ji,Chun-Hui Du,Bao-Ku Zhu,You-Yi Xu

DOI: https://doi.org/10.1002/app.26385

IF: 3

2007-01-01

Journal of Applied Polymer Science

Abstract:Poly(vinylidene fluoride) microporous membranes were prepared via the thermally induced phase separation process using diluent mixture of dibutyl phthalate (DBP) and di(2-ehylhexyl) phthalate (DEHP). The effects of the DBP ratio to DEHP in the diluent mixture on the phase diagrams were investigated. The phase diagrams can be controlled successfully by varying the DBP ratio in the diluent mixture. The compatibility between polymer and diluent mixture was characterized to explain the features in the phase diagram. The cross-sectional structures of membranes were investigated and related to the DBP ratio in diluent mixtures, initial polymer concentration, and cooling rate. When the DBP ratio to DEHP was 30 wt/70 wt, only spherulites structure was obtained at the polymer concentration of 30 wt % and at the cooling rate of IO'C/min, whereas the cellular structure was detected as the polymer concentration increased or the cooling rate deceased. In the case of the systems with only S-L phase separation, only spherulites structures were observed and the sizes of spherulites increased with increase in the polymer concentration and with decrease in the cooling rate. (c) 2007 Wiley Periodicals, Inc.
Porous PVDF membranes containing amphiphilic comblike polysiloxane formed via phase inversion process

Baoku Zhu,Yanling Qian,Jianhua Wang,Youyi Xu

2007-01-01

Abstract:Amphiphilic comb-like polysiloxane containing polyether side chains (ACPS) is presented for modification of PVDF membrane prepared via phase inversion process. The stability of ACPS in phase inversion process, the effects of ACPS on morphology, chemistry structure, crystallinity, mechanical property, hydrophilicity and filtration performance were discussed to extend. It was found that not only the ACPS molecules stay stable in membrane formation process and their side PEG chain enrich on membrane surface, but also these stability and enrichment can be reserved in membrane application process. Via supposing the schematic model, the mechanisms relating to structure and membrane performance are interpreted. From the observed results, it is concluded the ACPS should contribute to the potential candidate materials for high performance filtration membranes.
Cocontinuous Phase Morphology for an Asymmetric Composition of Polypropylene/polyamide 6 Blend by Melt Mixing of Polypropylene with Premelted Polyamide 6/organoclay Masterbatch

Li Wang,Zhao-Xia Guo,Jian Yu

DOI: https://doi.org/10.1002/app.34600

IF: 3

2011-01-01

Journal of Applied Polymer Science

Abstract:Cocontinuous morphology was obtained for an asymmetric composition of polypropylene/polyamide 6 (70/30 w/w) blend by controlling melt compounding sequence of PP, PA6, and organoclay. Three different compounding sequences were tested: direct melt mixing of all the components, melt mixing of PP with PA6/organoclay masterbatch, and melt mixing of PP with premelted PA6/organoclay masterbatch. Only the third method promotes cocontinuous morphology. In all three cases, organoclay locates preferentially in the PA6 phase and at the interface, although the level of organoclay dispersion is poorer in the case of direct mixing than in the two-masterbatch approaches. The morphology evolution processes of the three different compounding sequences were investigated and revealed that the main reason for the formation of cocontinuous morphology in the third method is the inhibiting effect of organoclay preincluded in the premelted PA6 phase on phase inversion. The viscosity of PA6 phase and the barrier effect of organoclay were confirmed to be two key factors in promoting cocontinuous structure. Dynamic mechanical analysis shows that the blend having cocontinuous morphology displays higher storage modulus than those having matrix-dispersed morphology at the same organoclay loading. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 123: 1218-1226, 2012
Influence of Processing Conditions on Percolation Threshold Value and Morphology of Co-continuous PA6/PS Blend

ZHAO Jian,XU Zhong-bin,FENG Lian-fang

DOI: https://doi.org/10.3969/j.issn.1001-4381.2006.08.009

2006-01-01

Abstract:In Haake torque rheometer, it was investigated that temperature, rotor speed, mixing time and the copolymer of styrene and maleic acid (SMA)-compatibilizer had effect on the percolation threshold value of co-continuous PA6/PS blend. The results showed that temperature, rotor speed and mixing time had little influence on the percolation threshold value; when compatibilizer (SMA) was added, the range of the region of phase co-continuity was largely narrowed because of the decreased possibility for recombination and coalescence. By the quiescent annealing of co-continuous PA6/PS, the blend morphology was examined at three different temperatures using SEM method. Co-continuous morphologies of 50/50(mass fraction/%)PA6/PS blend stayed co-continuous with annealing but showed an increase in phase size with time and the coarsening of the morphology was speeded at higher temperature. The interfacial area tends to decrease when the blend is kept at an elevated temperature, which results in an increase in the phase size of the co-continuous blend.
Formation of a Bicontinuous Structure Membrane of Polyvinylidene Fluoride in Diphenyl Carbonate Diluent Via Thermally Induced Phase Separation

J. Yang,D. W. Li,Y. K. Lin,X. L. Wang,F. Tian,Z. Wang

DOI: https://doi.org/10.1002/app.28606

IF: 3

2008-01-01

Journal of Applied Polymer Science

Abstract:The polyvinylidene fluoride (PVDF)-diphenyl ketone (DPK) mixture was studied as a new system to prepare PVDF membranes via thermally induced phase separation (TIPS). The phenomena of liquid-liquid phase separation was found in this mixture when the temperature of mixture was decreasing and the PVDF concentration was less than 30 wt %. Using DPK as diluent, PVDF membrane with bicontinuous structure was obtained without necessity to add a nonsolvent or a stretching process further. The phase diagram of PVDF-DPK system was also constructed to help investigate the effect of PVDF concentration and coarsening temperature on morphology of resulting membrane. The experiments showed that high coarsening temperatures and low PVDF concentrations resulted in the formation of the large pore size membrane. The strength of the wet membrane was decreasing with decreasing PVDF concentration. On condition that the PVDF concentration was larger than 30 wt %, thermally induced solid-liquid separation occurred and bicontinuous structure disappeared. (C) 2008 Wiley Periodicals, Inc.
Phase Behavior and Phase Separation in Blends of a Liquid Crystalline Polymer and an Amorphous Polymer Containing Hydrogen-Bonding Interaction

WJ Chen,J Wu,M Jiang

DOI: https://doi.org/10.1002/macp.1998.021990828

IF: 2.996

1998-01-01

Macromolecular Chemistry and Physics

Abstract:The phase behavior and thermally induced phase separation in blends of poly{styrene-co-[p-(2,2,2-trifluoro-1-hydroxy-1-trifluoromethyl)ethyl-α-methylstyrene]} (PS(OH)) and a thermotropic liquid crystalline polymer (LCP) were studied by optical microscopy (OM), infrared spectroscopy (IR) and time-resolved light scattering (TRLS). PS(OH) contains strong proton-donating groups —C(CF3)2OH, and the LCP is poly[p-(tert-butyl)phenylene fumarate] (PBPF), which is soluble in common solvents. For blends of PS(OH)/PBPF, the miscible region was found only at high PBPF compositions and low temperature due to intermolecular hydrogen bonding between —C(CF3)2OH groups of PS(OH) and the phenolic OH end-groups of PBPF according to IR. The PS(OH)/PBPF blend undergoes phase separation via spinodal decomposition (SD) during isothermal annealing in the two-phase regime of phase diagram. The SD yielded unique Vv and Hv scattering patterns, which can be attributed to regular periodic phase-separated structures composed of an anisotropic phase and an isotropic phase. Preliminary studies on the SD process by TRLS showed that the phase separation spontaneously occurs at a certain time, that might be associated with the presence of the LCP.
Formation of an interconnected lamellar structure in PVDF membranes with nanoparticles addition via solid-liquid thermally induced phase separation

Wenzhong Ma,Jun Zhang,Bart Van Der Bruggen,Xiaolin Wang

DOI: https://doi.org/10.1002/app.37574

IF: 3

2013-01-01

Journal of Applied Polymer Science

Abstract:Novel microporous membranes were prepared via thermally induced solid-liquid (S-L) phase separation of mixtures containing poly(vinylidene fluoride) (PVDF)/diphenyl ketone (DPK)/nanoparticles [ such as montmorillonite (MMT) and polytetrafluoroethylene (PTFE)] in diluted systems with a mass ratio of 29.7/70/0.3 wt %. The crystallization and melting characteristics of these diluted systems were investigated by polarizing optical microscopy (POM), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FTIR), and wide angle X-ray diffraction (WAXD). The nanoparticle structure and the interaction between PVDF chains and nanoparticle surfaces determined the crystallization behavior and morphology of the PVDF membrane. The addition of MMT and PTFE had a significant nucleation enhancement on the crystallization of PVDF accompanied by S-L phase separation during the thermally induced phase separation (TIPS) process. It was observed that an interconnected lamellar structure was formed in these two membranes, leading to a higher tensile strength compared with that of the reference membrane without nanoparticles addition. Additionally, addition of MMT facilitates the fiber-like beta phase crystal formation, resulting in the highest elongation at break. (C) 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 127: 2715-2723, 2013
Synergistic toughening effect of SBS and HDPE on the fracture of the PS/HDPE/SBS blends

Jingshen Wu,Baohua Guo,Chi-Ming Chan,Jianxiong Li,Hoi-Shuen Tang

DOI: https://doi.org/10.1016/S0032-3861(01)00443-8

IF: 4.6

2001-01-01

Polymer

Abstract:The microstructure and mechanical properties of the blends consisting of polystyrene and high-density polyethylene and/or styrene–butadiene–styrene were studied. The HDPE forms long fibers in both the PS/HDPE and PS/HDPE/SBS blends. The binary blends exhibit declined mechanical properties at all compositions. Mechanism study suggests that craze formation in PS followed by unstable crack propagation along the weak PS–HDPE interface is the major failure mechanism for the low impact strength of the binary blends. In the ternary blends, the SBS forms a thin layer covering the HDPE fibers, which improves the PS–HDPE interfacial strength and mechanical properties of the blends. The debonding-cavitation at the PS–HDPE interface releases the plastic constraint and enables shear deformation at the crack tip. Moreover, the HDPE-fiber-pullout promotes shear deformation of PS. Both mechanisms greatly improve the toughness of the ternary blends.
Hierarchical structure and properties of high‐density polyethylene (HDPE) microporous films fabricated via thermally‐induced phase separation (TIPS): Effect of presence of ultra‐high molecular weight polyethylene (UHMWPE)

Bin Yang,Shun Wang,Mengya Ding,Chengjun Wang,Cheng Lv,Yang Wang,Yuqing Yang,Nuo Zhang,Zhiqiang Shi,Jiasheng Qian,Ru Xia,Yirong Fang

DOI: https://doi.org/10.1002/pat.5765

IF: 3.348

2022-06-23

Polymers for Advanced Technologies

Abstract:In this study, HDPE/UHMWPE microporous films were prepared by blending UHMWPE and HDPE with DOP as the diluent via thermally‐induced phase separation (TIPS) method. Morphological studies showed that the phase separation mode of the mixed systems was hardly changed in the presence of UHMWPE. Both average pore size and porosity of the blend films increased firstly and then decreased with increasing UHMWPE content. When UHMWPE content reached 1.5 wt%, both porosity and average pore size of the film reached their maximum values (with a porosity of 84.8% and an average pore size of 0.79 μm). The addition of UHMWPE was found to not only enhance the thermal stability of the HDPE/UHMWPE blend films, but also greatly reduce their thermal shrinkage rate as well as the closed cell temperature, which made the diaphragms containing UHMWPE have good prospect for the application in lithium‐ion batteries (LIBs).

polymer science
Morphology, thermal behavior, rheological, and mechanical properties of polypropylene/polystyrene blends based on elongation flow

Rongyuan Chen,Xin Liu,Lin Han,Zhonghou Zhang,Yadong Li

DOI: https://doi.org/10.1002/pat.4998

IF: 3.348

2020-07-12

Polymers for Advanced Technologies

Abstract:<p>Binary blends comprised of polypropylene (PP) and polystyrene (PS) were prepared by a novel eccentric rotor extruder based on elongation flow. The morphology, thermal behavior, rheological and mechanical properties were investigated. As the enhanced mixed dispersion based on the novel extruder, the dispersed PS phase were uniformly dispersed in the PP matrix when the PS not more than 40%, and a distinct cocontinuous phase structure emerged when the PS content was 50%. The size of the dispersed PS phase related to the PS content and the processing flow filed influenced the crystallization behavior and the thermal stability of the blends. The PS droplet with small size could act as a nucleating agent for PP to improve the crystallinity, and PS droplet with large size could promote the thermal and heat transfer between the PS droplets and PP matrix which decreased the thermal stability. The rheological results showed that the compounding with PS into the PP matrix increased the storage and loss modulus as well as the complex viscosity of the materials. When the PS content not more than 20%, the blends showed good impact resistance, and PP/PS blends 30% PS showed good tensile and flexural properties. This study gives a new perspective for the structure and properties of the binary PP/PS blends prepared based on elongation flow.</p>

polymer science
High thermal conductivity and high electrical resistivity of poly(vinylidene fluoride)/polystyrene blends by controlling the localization of hybrid fillers

jianping cao,jun zhao,xiaodong zhao,feng you,haizhu yu,guohua hu,zhimin dang

DOI: https://doi.org/10.1016/j.compscitech.2013.09.024

IF: 9.1

2013-01-01

Composites Science and Technology

Abstract:Both high thermal conductivity and high electrical resistivity of immiscible poly(vinylidene fluoride) (PVDF)/polystyrene (PS) 30/70 blends are achieved by controlling the localization of hybrid fillers of multi-walled carbon nanotubes (MWCNTs) and silicon carbide (SiC) nanoparticles. The selective localization of both fillers in the minor phase of PVDF by using the masterbatch technique is confirmed by the scanning electron microscopy (SEM) observation. The domain size of the PVDF phase can be significantly reduced by further adding the fillers. The percolation threshold of MWCNTs in PVDF/PS 30/70 blend is measured to be ca. 2.9vol% with respect to the whole system. Compared with the case where only MWCNTs or SiC nanoparticles are present in the PVDF phase, the selective localization of both fillers in the PVDF phase can yield higher thermal conductivity and higher alternating current (AC) resistivity. Such materials could have potential applications in the electronic industry.
Ionic Conductivity of Microporous PVDF-HFP/PS Polymer Blends

Haitao Huang,Stephanie L. Wunder

DOI: https://doi.org/10.1149/1.1351756

IF: 3.9

2001-01-01

Journal of The Electrochemical Society

Abstract:Separators made from blends of poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) and polystyrene (PS) were microporous when cast from solvent/nonsolvent mixtures of acetone/dimethylcarbonate(DMC)/butanol(BuOH), where BuOH was the nonsolvent for both polymers. The ionic conductivities of these separators reached 2 mScm−1 and could be increased to 4 mScm−1 with addition of fumed silica. The morphology of the separators was characterized by scanning electron microscopy, nonsolvent (BuOH) and solvent (propylene carbonate, PC) uptake, and differential scanning calorimetry, and correlated with ionic conductivity measurements using 1 M LiPF6 in ethylene carbonate/DMC/diethyl carbonate, in the ratio 4:5:1 by weight. The solvent filled the microporous network and caused the pore walls to swell. The greater the former contribution, which increased with increasing PS content, the higher the ionic conductivity. Passing two identical microporous films through a double-roll laminator at a temperature above the glass transition temperature, Tg, of PS (Tg=95°C) and below the melt temperature, Tm, of PVDF-HFP (Tm=133°C) preserved the microporous structure, with a conductivity decrease of only 20% compared with unlaminated films. © 2001 The Electrochemical Society. All rights reserved.

electrochemistry,materials science, coatings & films
Crystallization behavior and hydrophilicity of poly(vinylidene fluoride)/poly(methyl methacrylate)/poly(vinyl pyrrolidone) ternary blends

Jing Cheng,Shichao Wang,Shuangjun Chen,Jun Zhang,Xiaolin Wang

DOI: https://doi.org/10.1002/pi.3185

IF: 3.213

2012-01-01

Polymer International

Abstract:Ternary blends composed of matrix polymer poly(vinylidene fluoride) (PVDF) with different proportions of poly(methyl methacrylate) (PMMA)/poly(vinyl pyrrolidone) (PVP) blends were prepared by melt mixing. The miscibility, crystallization behavior, mechanical properties and hydrophilicity of the ternary blends have been investigated. The high compatibility of PVDF/PMMA/PVP ternary blends is induced by strong interactions between the carbonyl groups of the PMMA/PVP blend and the CF2 or CH2 group of PVDF. According to the Fourier transform infrared and wide-angle X-ray difffraction analyses, the introduction of PMMA does not change the crystalline state (i.e. a phase) of PVDF. By contrast, the addition of PVP in the blends favors the transformation of the crystalline state of PVDF from non-polar a to polar beta phase. Moreover, the crystallinity of the PVDF/PMMA/PVP ternary blends also decreases compared with neat PVDF. Through mechanical analysis, the elongation at break of the blends significantly increases to more than six times that of neat PVDF. This confirms that the addition of the PMMA/PVP blend enhances the toughness of PVDF. Besides, the hydrophilicity of PVDF is remarkably improved by blending with PMMA/PVP; in particular when the content of PVP reaches 30 wt%, the water contact angle displays its lowest value which decreased from 91.4 degrees to 51.0 degrees. Copyright (C) 2011 Society of Chemical Industry
Crystallization and phase behavior of crystalline syndiotactic 1,2-polybutadiene/isotactic polypropylene blends in solution-cast thin films

Yong Chen,Ye Chen,Decai Yang

DOI: https://doi.org/10.1016/j.polymer.2006.01.008

IF: 4.6

2006-01-01

Polymer

Abstract:Crystallization and phase behavior in solution-cast thin films of crystalline syndiotactic 1,2-polybutadiene (s-1,2-PB) and isotactic polypropylene (i-PP) blends have been investigated by transmission electron microscopy (TEM), atomic force microscopy (AFM) and field-emission scanning electron microscopy (FESEM) techniques. Thin films of pure s-1,2-PB consist of parallel lamellae with the c-axis perpendicular to the film plane and the lateral scale in micrometer size, while those of i-PP are composed of cross-hatched and single-crystal-like lamellae. For the blends, TEM and AFM observations show that with addition of i-PP, the s-1,2-PB long lamellae become bended and i-PP itself tends to form dispersed convex regions on a continuous s-1,2-PB phase even when i-PP is the predominant component, which indicates a strong phase separation between the two polymers during film formation. FESEM micrographs of both lower and upper surfaces of the films reveal that the s-1,2-PB lamellae pass through i-PP convex regions from the bottom, i.e. the dispersed i-PP regions lie on the continuous s-1,2-PB phase. The structural development is attributed to an interplay of crystallization and phase separation of the blends in the film forming process. With solvent evaporation, s-1,2-PB would crystallize first forming the continuous phase, while the segregated i-PP phase accumulated on s-1,2-PB and crystallized subsequently, forming dispersed i-PP regions.
A "core-shell" structure imparting both gas barrier and UV shielding properties for a PLA/ PGA/ PBS ternary blend film

Mengke Zhu,Zhirui Ma,Yunxuan Weng,Zhigang Huang,Caili Zhang

DOI: https://doi.org/10.1016/j.ijbiomac.2024.135864

2024-09-20

Abstract:The core-shell structure enhances polymer blend systems by orderly assembly and leveraging complementary properties. This study aims to enhance the flexibility and barrier properties of polylactic acid (PLA, L) by blending it with polyglycolic acid (PGA, G) for gas barrier and polybutylene succinate (PBS, B) for flexibility. Encapsulating PGA in a core-shell structure using PBS resolves PGA's rapid hydrolysis issue. The theoretical models predicting dispersion patterns based on spreading coefficients and interfacial tensions were validated through SEM observations, confirming the formation of a core-shell structure in the 5L1G4B ternary blend. Compared to the PLA/PBS binary blend film, samples with PGA (5L1G4B and 4L1G5B) exhibit higher elongation at break and tearing strength. For instance, the elongation at break of the 5L1G4B sample increases from 272.3 % of 6L4B to 470.85 %. The 5L1G4B showed comparable oxygen and carbon dioxide barrier properties to the 6L4B sample. The 5L1G4B and 4L1G5B samples show <2 % UV transmittance in the UVA region, indicating excellent UV shielding. The 5L1G4B blend film, with its mechanical properties, oxygen barrier, UV resistance, and biodegradability, is ideal for outer layer packaging film and has the potential to replace LDPE in packaging juice and dairy product bottles.
In Situ Control Of Co-Continuous Phase Morphology For Ps/Ps-Co-Tmi/Pa6 Blend

Cailiang Zhang,Tao Zhang,Lianfang Feng

DOI: https://doi.org/10.1002/app.39972

IF: 3

2014-01-01

Journal of Applied Polymer Science

Abstract:The emulsification efficiency of PS-co-TMI, a copolymer polymerized by styrene and 3-isopropenyl-,-dimethylbenzene isocyanate (TMI), for polystyrene (PS)/polyamide 6 (PA6) blend was studied. During the mixing process, an effective emulsifier PS-g-PA6 was generated, which was demonstrated by differential scanning calorimetry (DSC) and fourier transform infrared spectroscopy. PS-g-PA6 generated by PS-co-TMI with high TMI content was found to contain some unreacted isocyanate active groups which reduced using efficiency of PS-co-TMI. Irrespective of TMI content in PS-co-TMI, the dosage of PS-co-TMI reached 20 wt %, unreacted PS-co-TMI was detected. These results indicated that reactive emulsification limits for both active groups' content and reactive precursors' dosage. After the rational addition of PS-co-TMI into PS/PA6 system, phase sizes of co-continuous structure were reduced conspicuously. However, co-continuous structure was evolved into matrix-dispersed structure while the dosage of PS-co-TMI reached 20 wt %. Emulsification efficiencies of PS-co-TMI with different TMI contents, 2.2, 4.1, and 7.5 wt %, were compared. The results revealed PS-co-TMI with 2.2 wt % TMI content had the highest reactive emulsification efficiency because of the block-copolymer-inclined emulsifier generated in the mixing process. (c) 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2014, 131, 39972.
Tunable Electrical Conductivity Of Carbon-Black-Filled Ternary Polymer Blends By Constructing A Hierarchical Structure

Qiyan Zhang,Bo-Yuan Zhang,Zhao-Xia Guo,Jian Yu

DOI: https://doi.org/10.3390/polym9090404

IF: 5

2017-01-01

Polymers

Abstract:A type of hierarchical structured composite composed of a minor thermoplastic polyurethane (TPU) phase spreading at the interface of two major phases polyoxymethylene/polyamide copolymer (POM/COPA) and carbon black (CB) particles selectively localized at the TPU/COPA interface of the tri-continuous blends was fabricated by melt compounding. The hierarchical structure was designed according to predictions and verified by a combination of electron microscopy and solvent extraction technique. The hierarchical structured composites show the dramatically decreased percolation threshold, a reduction of 60% compared to those without TPU where CB is selectively distributed in the COPA phase. The effects of CB contents and TPU on the phase morphology of POM/COPA were investigated, showing the occurrence of the POM/COPA phase inversion from a sea-island to a co-continuous structure beyond the percolation threshold of CB in the presence of TPU. The mechanism for the formation of conductive network is construction of CB network at the TPU/COPA interface of tri-continuous POM/COPA/TPU blends and double percolation effect.
Advanced Dielectric Polymer Nanocomposites By Constructing A Ternary Continuous Structure In Polymer Blends Containing Poly(Methyl Methacrylate) (Pmma) Modified Carbon Nanotubes

xiaodong zhao,jianping cao,jun zhao,guohua hu,zhimin dang

DOI: https://doi.org/10.1039/c4ta01214c

IF: 11.9

2014-01-01

Journal of Materials Chemistry A

Abstract:A nanocomposite with ultra-low percolation threshold and high dielectric performance is prepared by controlling the localization of multiwalled carbon nanotubes (MWNTs) in one phase of a ternary continuous polymer blend system through melt processing. Polystyrene (PS), poly(vinylidene fluoride) (PVDF), and poly(methyl methacrylate) (PMMA) can form a ternary continuous structure when the volume fractions of PS, PVDF and PMMA are 70 vol%, 20 vol%, and 10 vol%, respectively. The PS is a continuous matrix (sea-phase) whereas the other two phases are interconnected threads (the PVDF is situated as the core while the PMMA is the shell, and the thickness of the PMMA shell is about 1 mu m). Adding PMMA could improve the compatibility between the PS and PVDF components. Selective distribution of MWNTs in the PMMA shell is achieved through a combination of PMMA modified MWNTs and appropriate processing procedures. The composite shows an ultra-low percolation threshold of ca. 0.3 wt%. When the weight fraction of PMMA modified MWNTs is 0.4 wt%, the dielectric constant of the composite is as high as 182 (at 100 Hz), which is about 60 times higher than that of a pure PS matrix. The composite's dielectric properties have excellent temperature stability. This approach can provide a new and low-cost route to design high-performance dielectric materials with ultra-low percolation thresholds.

Insight into the Formation of A Continuous Sheath Structure for the Ps Phase in Tri-Continuous Pvdf/Ps/Hdpe Blends

Co-Continuous Polymeric Nanostructures Via Simple Melt Mixing of Ps/Pmma

Tuning polymer blends to cocontinuous morphology by asymmetric diblock copolymers as the surfactants

Preparation of Porous PVDF Membrane Via Thermally Induced Phase Separation with Diluent Mixture of DBP and DEHP

Porous PVDF membranes containing amphiphilic comblike polysiloxane formed via phase inversion process

Cocontinuous Phase Morphology for an Asymmetric Composition of Polypropylene/polyamide 6 Blend by Melt Mixing of Polypropylene with Premelted Polyamide 6/organoclay Masterbatch

Influence of Processing Conditions on Percolation Threshold Value and Morphology of Co-continuous PA6/PS Blend

Formation of a Bicontinuous Structure Membrane of Polyvinylidene Fluoride in Diphenyl Carbonate Diluent Via Thermally Induced Phase Separation

Phase Behavior and Phase Separation in Blends of a Liquid Crystalline Polymer and an Amorphous Polymer Containing Hydrogen-Bonding Interaction

Formation of an interconnected lamellar structure in PVDF membranes with nanoparticles addition via solid-liquid thermally induced phase separation

Synergistic toughening effect of SBS and HDPE on the fracture of the PS/HDPE/SBS blends

Hierarchical structure and properties of high‐density polyethylene (HDPE) microporous films fabricated via thermally‐induced phase separation (TIPS): Effect of presence of ultra‐high molecular weight polyethylene (UHMWPE)

Morphology, thermal behavior, rheological, and mechanical properties of polypropylene/polystyrene blends based on elongation flow

High thermal conductivity and high electrical resistivity of poly(vinylidene fluoride)/polystyrene blends by controlling the localization of hybrid fillers

Ionic Conductivity of Microporous PVDF-HFP/PS Polymer Blends

Crystallization behavior and hydrophilicity of poly(vinylidene fluoride)/poly(methyl methacrylate)/poly(vinyl pyrrolidone) ternary blends

Crystallization and phase behavior of crystalline syndiotactic 1,2-polybutadiene/isotactic polypropylene blends in solution-cast thin films

A "core-shell" structure imparting both gas barrier and UV shielding properties for a PLA/ PGA/ PBS ternary blend film

In Situ Control Of Co-Continuous Phase Morphology For Ps/Ps-Co-Tmi/Pa6 Blend

Tunable Electrical Conductivity Of Carbon-Black-Filled Ternary Polymer Blends By Constructing A Hierarchical Structure

Advanced Dielectric Polymer Nanocomposites By Constructing A Ternary Continuous Structure In Polymer Blends Containing Poly(Methyl Methacrylate) (Pmma) Modified Carbon Nanotubes