Abstract:Suitable compatibilizers are essential to prepare immiscible polymer blends with stable co‐continuous morphologies. From the thermodynamic point of view, such compatibilizer should not only reduce the interfacial tension, but also promote the formation of flat interface between different phases. Meanwhile, it must not hinder the coalescence of dispersed phase. Therefore, asymmetric structures are required for those block or graft copolymer compatibilizers. However, from the kinetic point of view, copolymers with asymmetric structures are prone to be dragged out from the interface and form micelles in one phase under the processing conditions, which will lose their compatibilization effects. The balance between such thermodynamic and kinetic factors remains unclear. In this paper, the relationship between the morphology of the compatibilized polystyrene/nylon 6/styrene‐maleic anhydride copolymers (PS/PA6/SMA) immiscible polymer blends and the structures of the in‐situ formed SMA‐g‐PA6 graft copolymers as well as the processing conditions are studied. Two kinds of SMA are used as compatibilizers: SMA28 (Mw = 110,000 g/mol, MAH content 28 wt.%) and SMA11 (Mw = 110,000 g/mol, MAH content 11 wt.%). After melt blending with PA6 into an internal mixer, the in‐situ formed copolymer SMA28‐g‐PA6 has an average four PA6 side chains grafted on one SMA backbone, while that of SMA11‐g‐PA6 has only one PA6 side chain. Dissipative particle dynamics (DPD) simulation results indicate that both SMA28‐g‐PA6 copolymer and PS/PA6/SMA28 blends tend to form co‐continuous structure, while SMA11‐g‐PA6 copolymer and PS/PA6/SMA11 blends form sea‐island morphologies. However, these results are confirmed experimentally only at relatively low rotor speed of the internal mixer (60 rpm). When the rotor speed of the mixer is higher (105 rpm), sea‐island morphologies are obtained in PS/PA6/SMA28 blends and co‐continuous ones are found in PS/PA6/SMA11 systems. These results indicate that higher shear stress will favor to elongate the minor phase domains and form flat interfaces, which is benefit for the formation of co‐continuous morphologies; meanwhile, high shear stress may pull the graft copolymers with asymmetric structures (SMA28‐g‐PA6) out from the interface of PS and PA6 and induce the formation of sea island morphologies. This article is protected by copyright. All rights reserved

Co-Continuous Polymeric Nanostructures Via Simple Melt Mixing of Ps/Pmma

Tuning polymer blends to cocontinuous morphology by asymmetric diblock copolymers as the surfactants

Interfacial silica nanoparticles stabilize cocontinuous polymer blends

The Influence of Nano-SiO2 on Co-continuous Phase Morphology of Poly (propylene carbonate) /Poly(butylene succinate) Blends

Relationship Between The Co‐Continuous Morphology of Immiscible Polymer Blends and the Structure of An In Situ Formed Graft Copolymer

Onset Reduction and Stabilization of Cocontinuous Morphology in Immiscible Polymer Blends by Snowman-like Janus Nanoparticles.

Cocontinuous Phase Morphology for an Asymmetric Composition of Polypropylene/polyamide 6 Blend by Melt Mixing of Polypropylene with Premelted Polyamide 6/organoclay Masterbatch

Advanced Dielectric Polymer Nanocomposites By Constructing A Ternary Continuous Structure In Polymer Blends Containing Poly(Methyl Methacrylate) (Pmma) Modified Carbon Nanotubes

In Situ Control Of Co-Continuous Phase Morphology For Ps/Ps-Co-Tmi/Pa6 Blend

Polypropylene/polystyrene/clay Blends Prepared by an Innovative Eccentric Rotor Extruder Based on Continuous Elongational Flow: Analysis of Morphology, Rheology Property, and Crystallization Behavior

Segmental Dynamics in PMMA-Grafted Nanoparticle Composites

Copolymer-tethered Nanoparticles As Compatibilizers of Immiscible PS/PMMA Blends

Tuning PVDF/PS/HDPE Polymer Blends to Tri-Continuous Morphology by Grafted Copolymers As the Compatibilizers

Controlling the Size of Nanostructures in Thin Films Via Blending of Block Copolymers and Homopolymers

Synthesis of Nanosize Poly(methyl Methacrylate) Microlatexes with High Polymer Content by a Modified Microemulsion Polymerization

Suppressing Phase Retraction and Coalescence of Co-Continuous Polymer Blends: Effect of Nanoparticles and Particle Network

Reactive Nanoparticles Compatibilized Immiscible Polymer Blends: Synthesis of Reactive SiO2 with Long Poly(methyl methacrylate) Chains and the in Situ Formation of Janus SiO2 Nanoparticles Anchored Exclusively at the Interface.

Suppressing phase coarsening in immiscible polymer blends using nano-silica particles located at the interface

Continuous Flow Synthesis Of Polystyrene Nanoparticles Via Emulsion Polymerization Stabilized By A Mixed Nonionic And Anionic Emulsifier

Fractionated Crystallization and Morphology of PP/PS Blends in the Presence of Silica Nanoparticles with Different Surface Chemistries

Nanoprecipitation of PMMA Stabilized by Core Cross‐Linked Star Polymers