STRUCTURAL RELAXATION IN Nd2Fe14B/α-Fe/ AMORPHOUS NdFe-B TRI-PHASE EXCHANGE COIPLING MAGNETS

计齐根,田宗军,顾本喜,章建荣,都有为

DOI: https://doi.org/10.3321/j.issn:0412-1961.2001.05.004

IF: 1.797

2001-01-01

ACTA METALLURGICA SINICA

Abstract:The nano-scaled Nd2Fe14B/α-Fe based exchange coupling magnets were prepared by the melt-spun technology. It was found that the structural relaxation at room temperature leads to an enhancement of both coercivity Hc and remanence rate mr of the powder samples. Such effect is stronger in tri-phase system of nanocrystalline Nd2Fe14B/α-Fe and amorphous Nd-Fe-B than in pure crystal or amorphous structures. After stored at temperature of 0-35℃ for one year, a quenched Nd10Fe83B6In sample's coercivity Hc and remanence rate mr has increased from 296 kA/m and 0.55 of the fresh powder to 384 kA/m and 0.62 of that stored respectively. The existence of the amorphous phase provides space for grains to complete their boundaries. This structural relaxation or atomic adjustment in boundary region results in enhanced crystallographic coherence and exchange coupling between adjacent grains and phases. A perfect grain boundary also results in enhanced magnetic hardening. The result of X-ray diffraction shows a distorted boundary phase which is most likely developed by the structural relaxation due to stress relief and defect elimination.